A kind of preparation method of anti-mold and formaldehyde-removing coating

A technology of formaldehyde and paint, which is applied in the field of preparation of anti-mildew and formaldehyde-removing paint, can solve the problems of short duration and poor anti-mildew ability, and achieve the effects of prolonging service life, improving bactericidal and antibacterial ability, and maintaining bactericidal and anti-mildew effect

Active Publication Date: 2015-08-05
苏州市东挺河智能科技发展有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problem of poor anti-mildew ability and short duration of decoration coatings in the prior art, one of the purposes of the present invention is to provide a method for preparing an anti-mildew and formaldehyde-removing coating. The coating prepared by this method can effectively resist Mildew, and the effect is long-lasting, at the same time, the paint also has the effect of removing formaldehyde

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A method for preparing an anti-mold and formaldehyde-removing coating, the raw materials used and their specific proportions (by weight) are as follows: 100 parts of polystyrene-acrylic acid copolymer, 26 parts of talcum powder less than 100 microns, 8 parts of wetting agent 6 parts, 6 parts of titanium dioxide, 10 parts of anti-mildew bactericide, 3 parts of bamboo charcoal, 40 parts of water, described anti-mold bactericide is nano-TiO 2 , Nano ZnO and ZrO 2 mixture of nano-TiO 2 , The particle size of nano-ZnO is 30-50 nanometers, ZrO 2 The particle size is -400 mesh, and the ratio of the three is TiO 2 :ZnO:ZrO 2 =1:1:0.5; the method includes the following steps:

[0020] (1). At the speed of the mixer at 1200r / min, add the anti-mold fungicide and wetting agent to an appropriate amount of water to mix and stir to form a uniform slurry, and put it in a container for later use;

[0021] (2). At the speed of the mixer at 1500r / min, add talcum powder, titanium diox...

Embodiment 2

[0026] A preparation method of an anti-mold and formaldehyde-removing coating, the raw materials used and their specific proportions (by weight) are as follows: 100 parts of polyacrylic acid copolymer, 30 parts of talcum powder less than 100 microns, 3 powders of dispersant, wetting 4 parts of antifungal agent, 10 parts of ultramarine blue, 8 parts of antimold bactericide, 5 parts of diatomaceous earth, 50 parts of water, and described antimold bactericide is nano-TiO 2 , Nano ZnO and ZrO 2 mixture of nano-TiO 2 , The particle size of nano-ZnO is 30-50 nanometers, ZrO 2 The particle size is -400 mesh, and the ratio of the three is TiO 2 :ZnO:ZrO 2 =2:1:0.5; the method includes the following steps:

[0027] (1). At the speed of the mixer at 1000r / min, add the antifungal and fungicide and additives to an appropriate amount of water to mix and stir to form a uniform slurry, and put it in a container for later use;

[0028] (2). At the speed of the mixer at 2000r / min, add tal...

Embodiment 3

[0033] A method for preparing an anti-mold and formaldehyde-removing coating, the raw materials used and their specific proportions (by weight) are as follows: 100 parts of polyvinyl acetate-acrylic acid copolymer, 28 parts of talcum powder less than 100 microns, and 2 parts of dispersant , 2 parts of wetting agent, 2 parts of defoamer, 2 parts of thickener, 8 parts of titanium dioxide, 9 parts of anti-mold and fungicide, 2 parts of activated carbon, 1 part of diatomaceous earth, 1 part of perlite, 45 parts of water, The anti-mildew bactericide is nano TiO 2 , Nano ZnO and ZrO 2 mixture of nano-TiO 2 , The particle size of nano-ZnO is 30-50 nanometers, ZrO 2 The particle size is -400 mesh, and the ratio of the three is TiO 2 :ZnO:ZrO 2 =1.5:1:0.5; the method includes the following steps:

[0034](1). At the speed of the mixer at 500r / min, add the anti-mold and fungicides and additives into an appropriate amount of water to mix and stir to form a uniform slurry, and put it...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
antibacterial rateaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing anti-mildew formaldehyde removal coating. The coating comprises a polystyrene-acrylic acid copolymer or a polyacrylic acid copolymer or a polyvinyl acetate-acrylic acid copolymer, talcum powder, an assistant, pigment, an anti-mildew fungicide, an adsorbent and water. The method comprises the steps of mixing the anti-mildew fungicide with the assistant; mixing the talcum powder with the pigment and the adsorbent; mixing the polystyrene-acrylic acid copolymer or the polyacrylic acid copolymer or the polyvinyl acetate-acrylic acid copolymer with the water, and mixing the foregoing mixtures. The coating prepared by the method disclosed by the invention can effectively resist mildew and has a durable effect, and meanwhile, the coating has a formaldehyde removal function.

Description

technical field [0001] The invention relates to the field of chemical industry, in particular to a preparation method of an anti-mildew and formaldehyde-removing coating. Background technique [0002] At present, in house decoration, due to the formaldehyde, benzene series, TVOC and other harmful substances brought by various decoration materials, the home decoration pollution and the harmful substances in the indoor air exceed the standard. It has seriously interfered with people's daily life. The long-term absorption of this formaldehyde-containing gas by the human body can cause various diseases, and even endanger human life in serious cases. Therefore, it is necessary to control the indoor air pollution of the renovated rooms and the newly purchased furniture, and eliminate the pollution of harmful gases brought by the new furniture. In order to ensure that the content of indoor harmful gases is within the range stipulated by the state, people can live in a healthy env...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D125/08C09D133/00C09D131/04C09D5/14C09D7/12
Inventor 陈晓龙李聚刚钱振宇
Owner 苏州市东挺河智能科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products