Preparation method of bacteriostatic softening agent for aged hard and dry leather
A leather, dry and hard technology, applied in the field of preparation of bacteriostatic and softening agents, can solve the problems of reduced bacteriostatic effect, restoration of hand feel, color and luster performance, inability to permanently prevent mildew, etc., to increase antibacterial properties and restore good hand feeling. , strong antibacterial effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0014] Embodiment 1: a kind of preparation method of antibacterial softening agent for aging dry hard leather, comprising the following steps:
[0015] 1) The lanolin was heated in a water bath while stirring in an airtight container, the time was 1.5h, and the temperature was 60°C;
[0016] 2) During the heating and stirring process of lanolin, gradually add phosphorus pentoxide powder in an amount of 5% of the mass of lanolin. The amount is the same, and the addition time interval is 10min;
[0017] 3) After the above heating and stirring process is completed, the mixed liquid is titrated to neutrality with a sodium hydroxide solution with a mass fraction of 30%, and then the mixed liquid is vacuum-dried to obtain phosphorylated modified lanolin;
[0018] 4) compound the above-mentioned phosphorylated modified lanolin with Tween-80, 2-octyl-4-isothiazolin-3-one, tea saponin, ethanol and deionized water, in a water bath of 50° C. Carry out stirring and emulsification to obt...
Example Embodiment
[0019] Embodiment 2: a kind of preparation method of antibacterial softening agent for aging dry hard leather, comprising the following steps:
[0020] 1) The lanolin was heated in a water bath while stirring in an airtight container for 2.5h and the temperature was 70°C;
[0021] 2) During the heating and stirring process of lanolin, gradually add phosphorus pentoxide powder with an amount of 3% of the mass of lanolin. The addition method is to add it in 3 batches within the first 30 minutes of lanolin heating and stirring, adding phosphorus pentoxide each time. The amount is the same, and the addition time interval is 10min;
[0022] 3) After the above heating and stirring process is completed, the mixed liquid is titrated to neutrality with a sodium hydroxide solution with a mass fraction of 30%, and then the mixed liquid is vacuum-dried to obtain phosphorylated modified lanolin;
[0023] 4) compound the above-mentioned phosphorylated modified lanolin with Tween-80, 2-octy...
Example Embodiment
[0024] Embodiment 3: a kind of preparation method of antibacterial softening agent for aging dry hard leather, comprising the following steps:
[0025] 1) The lanolin was heated in a water bath while stirring in an airtight container, the time was 3.5h, and the temperature was 50°C;
[0026] 2) During the heating and stirring process of lanolin, gradually add phosphorus pentoxide powder in an amount of 4% of the mass of lanolin. The amount is the same, and the addition time interval is 10min;
[0027] 3) After the above heating and stirring process is completed, the mixed liquid is titrated to neutrality with a sodium hydroxide solution with a mass fraction of 30%, and then the mixed liquid is vacuum-dried to obtain phosphorylated modified lanolin;
[0028] 4) compound the above-mentioned phosphorylated modified lanolin with Tween-80, 2-octyl-4-isothiazolin-3-one, tea saponin, ethanol and deionized water, in a water bath of 50° C. Carry out stirring and emulsification to obt...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap