Composite cement enhanced grinding aid containing amide polyamine polycarboxylic acids and preparation method therefor

A technology containing amide polyamine polycarboxylic acid and amide polyamine polycarboxylic acid, which is applied in the field of composite cement reinforced grinding aids and its preparation, can solve the problems that the surface active groups are difficult to achieve multiple complementarity and the comprehensive performance is not ideal. Achieve the effects of improving cement reinforcement and grinding aid, increasing the output per machine hour, and improving the overall performance

Active Publication Date: 2014-03-19
史才军
View PDF3 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the limitation of the chemical structure of polycarboxylic acid unsaturated monomer raw materials, it is difficult for the surface active groups to achieve multi-complementation, so its comprehensive performance is not ideal.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The composite cement reinforced grinding aid AC1 containing amide polyamine polycarboxylic acid of this embodiment is made of the following raw materials in mass percentage: 25% of amide polyamine polycarboxylic acid with a solid content of 27.5%, 7% triethanolamine, triiso Propanolamine 5%, Diethanol Monoisopropanolamine 5%, Diethylene Glycol 2%, Sodium Lignosulfonate 2%, Sodium Lauryl Sulfate 4%, Waste Molasses 3%, Water 47%.

[0020] Its preparation method comprises the following steps:

[0021] (1) Inject amide polyamine polycarboxylic acid and water into the reaction kettle according to the predetermined mass percentage ratio, stir and heat to 40°C, then add sodium lignosulfonate according to the predetermined mass percentage ratio, and stir for 15 minutes;

[0022] (2) Add sodium lauryl sulfate according to the predetermined mass percentage ratio, stir for 8 minutes, then add waste molasses according to the predetermined mass percentage ratio and stir for 20 minut...

Embodiment 2

[0025] The composite cement reinforced grinding aid AC2 containing amide polyamine polycarboxylic acid of the present embodiment is made of the following raw materials in mass percentage: 30% of amide polyamine polycarboxylic acid with a solid content of 27.5%, 6% triethanolamine, triiso Propanolamine 4%, Diethanol Monoisopropanolamine 5%, Diethylene Glycol 2%, Sodium Lignosulfonate 2%, Sodium Lauryl Sulfate 4%, Waste Molasses 3%, Water 44%.

[0026] Its preparation method is with embodiment 1.

Embodiment 3

[0028] The composite high-efficiency cement reinforced grinding aid AC3 containing amide polyamine polycarboxylic acid of this embodiment is made of the following raw materials in mass percentage: 35% of amide polyamine polycarboxylic acid with a solid content of 27.5%, 6% triethanolamine, three Isopropanolamine 4%, Diethanol Monoisopropanolamine 4%, Diethylene Glycol 2%, Sodium Lignosulfonate 2%, Sodium Lauryl Sulfate 4%, Waste Molasses 3%, Water 40%.

[0029] Its preparation method is with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Provided are a composite cement enhanced grinding aid containing amide polyamine polycarboxylic acids and a preparation method therefor. The composite cement enhanced grinding aid is prepared from the following raw materials, by weight, 20-60% of amide polyamine polycarboxylic acids, 4-15% of triethanolamine, 2-12% of triisopropanolamine, 2-10% of diethanolisopropanolamine, 1.5-8.0% of diglycol, 1-6% of sodium lignosulfonate, 2.5-10.0% of sodium lauryl sulfate, 1-8% of waste molasses and 20-60% of water. The invention also comprises a preparation method for the composite cement enhanced grinding aid containing amide polyamine polycarboxylic acids. The obtained composite cement enhanced grinding aid has obvious effects at aspects of raising the machine-hour output, increasing fluidity of materials in grinding and increasing cement strength, and has good adaptability with concrete admixtures.

Description

technical field [0001] The invention relates to a composite cement reinforced grinding aid and a preparation method thereof, in particular to a composite cement reinforced grinding aid containing amide polyamine polycarboxylic acid and a preparation method thereof. Background technique [0002] The use of cement grinding aids can improve the grinding efficiency of the ball mill and the mill output per unit time, reduce the energy consumption and loss of the mill, so as to achieve the purpose of reducing the cost of cement production. There are two types of cement grinding aids widely used at home and abroad, liquid and powder. Most of their basic components belong to organic surface active substances, mainly including amines, alcohols, alcohol amines, lignosulfonates, fatty acids, etc. This kind of compound grinding aid has good grinding aid and strengthening effect, but its performance stability is poor and it is sensitive to the change of dosage. With the increasing scarc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B24/38C04B24/12C04B103/52
Inventor 史才军龙兰
Owner 史才军
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com