Refining agent for smelting aluminum alloy

A technology of refining agent and aluminum alloy, applied in the field of refining agent for aluminum alloy smelting, can solve the problems of polluted environment, toxic and irritating odor, unfavorable health of workers, etc. The effect of processability

Active Publication Date: 2014-04-02
COSCO W M J ALUMINUM DEV CO LTD
View PDF8 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The above refining agent reacts under high temperature smelting to generate Cl 2 , AlCl 3 、C 2 Cl 4 and other gases, and the above-mentioned refining agent also contains harmful elements such as benzene, which is not only poisonous but also has a strong pungent smell, which is harmful to the health of workers and pollutes the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Weigh NaCl by mass percentage: 35 parts, KNO 3 : 35 parts, CaF 2 : 3 parts, Na 2 SiF 6 : 6 parts, Na 3 A1F 6 : 7 parts, graphite: 5 parts, rare earth scandium and yttrium: 0.5 parts, the above several materials are mixed, stirred evenly, put into an electric furnace for overheating and melting to remove crystallization water, cool after coming out of the furnace, and finally sieve and filter to obtain the present invention. Refining agent for aluminum alloy melting.

Embodiment 2

[0021] Weigh NaCl by mass percentage: 38 parts, KNO 3 : 30 parts, CaF 2 : 4 parts, Na 2 SiF 6 : 7 parts, Na 3 A1F 6 : 8 parts, graphite: 6 parts, rare earth scandium and yttrium: 0.6 parts, the above several materials are mixed, stirred evenly, put into an electric furnace for overheating and melting to remove crystallization water, cool after coming out of the furnace, and finally sieve and filter to obtain the present invention. Refining agent for aluminum alloy melting.

Embodiment 3

[0023] Weigh NaCl by mass percentage: 40 parts, KNO 3 : 28 parts, CaF 2 : 5 parts, Na 2 SiF 6 : 8 parts, Na 3 A1F 6 : 9 parts, graphite: 7 parts, rare earth scandium and yttrium: 0.8 parts, BaSO 4 : 5 parts, the above several materials are mixed, stirred evenly, put into an electric furnace for superheating and melting to remove crystal water, cool after being out of the furnace, and finally sieve and filter to obtain the refining agent for aluminum alloy smelting of the present invention.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a refining agent for smelting an aluminum alloy. The refining agent is characterized by comprising the following components by mass percent: 35% to 45% of NaCl, 25% to 35% of KNO3, 3% to 8% of CaF2, 6% to 10% of Na2SiF6, 7% to 12% of Na3AlF6, 5% to 10% of graphite and 0.5% to 1.5% of rare earth. The refining agent has the characteristics of good refining effect, strong degassing capacity and the like, and cannot generate noxious gas during a production process.

Description

technical field [0001] The invention relates to the field of smelting and processing of aluminum alloys, in particular to a refining agent for smelting aluminum alloys. Background technique [0002] Aluminum alloys inevitably absorb and carry gases and produce inclusions during the smelting process, which will reduce the purity of aluminum alloys and affect the quality. Therefore, it is necessary to refine and purify the aluminum alloy smelting process to remove these gases and inclusions and improve the quality of the aluminum alloy. Adding a refining agent to the aluminum alloy for refining and purification is a commonly used measure. [0003] At present, domestic aluminum alloy smelting mainly adopts the adsorption refining method of adding various fluxes, including the refining method of introducing nitrogen and using chlorine salt as a refining agent. Commonly used chlorides are sodium chloride, zinc chloride, manganese chloride, hexachloroethane, carbon tetrachloride,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C1/06C22C21/00
Inventor 张聪聪
Owner COSCO W M J ALUMINUM DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products