Inorganic overcoat resin and preparation method thereof

A surface resin, inorganic technology, applied in the direction of coating, can solve the problem that the acrylic resin surface can not achieve stain resistance, and achieve the effect of excellent aging resistance.

Active Publication Date: 2014-04-09
SHENZHEN JIADA HIGH TECH IND DEV
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Currently, acrylic resins are commonly used in the market for finishes, but acrylic resins have major deficiencies in weather resistance and stain resistance. The service life of acrylic finishes can be guaranteed for about 5 years. With the continuous deterioration of the environment, Air pollution and man-made pollution are becoming more and more serious, and the acrylic resin overlay basically cannot achieve the function of anti-staining

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Inorganic overcoat resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] 1) Add 20 parts by weight of tetraethyl orthosilicate to 40 parts by weight of a water-alcohol mixture, the water-alcohol mixture is water and alcohol with a weight ratio of 65:35, and react in a water bath at 70°C for 60 minutes;

[0037] 2) Continue to add 8 parts by weight of methyltrimethoxysiloxane, and react in a water bath at 70°C for 60 minutes;

[0038] 3) Continue to add 40 parts by weight of a mixture of silicon dioxide, aluminum oxide, titanium dioxide and zirconium dioxide, the mixture of silicon dioxide, aluminum oxide, titanium dioxide and zirconium dioxide is 50:20 by weight: 20:10 silicon dioxide, aluminum oxide, titanium dioxide and zirconium dioxide, react in a water bath at 70°C for 60 minutes.

Embodiment 2

[0040] 1) Add 30 parts by weight of tetraethyl orthosilicate to 50 parts by weight of a water-alcohol mixture, the water-alcohol mixture is water and alcohol with a weight ratio of 65:35, and react in a water bath at 70°C for 60 minutes;

[0041] 2) Continue to add 10 parts by weight of methyltrimethoxysiloxane, and react in a water bath at 70°C for 60 minutes;

[0042] 3) Continue to add 50 parts by weight of a mixture of silicon dioxide, aluminum oxide, titanium dioxide and zirconium dioxide, the mixture of silicon dioxide, aluminum oxide, titanium dioxide and zirconium dioxide is a weight ratio of 50:20: 20:10 silicon dioxide, aluminum oxide, titanium dioxide and zirconium dioxide, react in a water bath at 70°C for 60 minutes.

[0043] Can be obtained by testing:

[0044]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an inorganic overcoat resin which comprises an inorganic nano material having a solid content of 42-46%, wherein the inorganic nano material is synthesized through a sol-gel method process from the following components in parts by weight: 1-30 parts of ethyl orthosilicate, 1-10 parts of methyltrimethoxy silane, 1-50 parts of mixture of silicon dioxide, aluminum oxide, titanium dioxide and zirconium dioxide and 1-50 parts of water-alcohol mixture; the weight ratio of the silicon dioxide, aluminum oxide, titanium dioxide and zirconium dioxide in the mixture thereof is 50:20:20:10; and the water-alcohol weight ratio of the water-alcohol mixture is 65:35. According to the invention, the inorganic overcoat resin is prepared from the pure inorganic nano material, and the service life can be kept at 15 years or above; and the composition adopts a methyl introduction manner, so that the overcoat has hydrophobic / oleophobic properties, thus ensuring that self cleaning of a decorative layer can be realized by rainfall.

Description

technical field [0001] The invention relates to the field of finish paint / resin technology, in particular to an inorganic finish resin and a preparation method thereof. Background technique [0002] Currently, acrylic resins are commonly used in the market for finishes, but acrylic resins have major deficiencies in weather resistance and stain resistance. The service life of acrylic finishes can be guaranteed for about 5 years. With the continuous deterioration of the environment, Air pollution and man-made pollution are becoming more and more serious, and the acrylic resin overlay basically cannot achieve the function of anti-staining. Contents of the invention [0003] The purpose of the present invention is to solve the above-mentioned technical problems, and to provide an inorganic overlay resin composed of inorganic nano-materials with super long durability and stain resistance and a preparation method thereof. [0004] In order to realize the above-mentioned purpose...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00
Inventor 樊晓军关有俊熊宸熊永强
Owner SHENZHEN JIADA HIGH TECH IND DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com