Cross-interface penetration adhesive

A cross-interface, adhesive technology, applied in the direction of adhesives, adhesive types, rosin adhesives, etc., can solve the problems of plasticization or dissolution, affecting the bonding strength, etc., to reduce the impact, prolong the opening time, strengthen the The effect of penetration

Active Publication Date: 2014-04-09
浙江固特新材料科技股份有限公司
View PDF12 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Especially when bonding substrates with heavy ink and varnish systems, ordinary hot melt adhesives only bond the ink or varnish layer on the surface, and hot melt adhesives are easily plasticized or dissolved by plasticizers and organic solvents on the surface, thus greatly Affected bond strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The cross-interface penetration viscose that present embodiment describes, it is by 1 weight part ethylene-acrylic acid copolymer wax, 2 weight parts paraffin, 10 weight parts maleic anhydride grafted EVA, the EVA of 10 weight parts high VA content, 6 weight parts Parts of metallocene catalyzed polyolefin, 10 parts by weight of dehydrated malic acid rosin resin, 10 parts by weight of rosin glyceride, 1 part by weight of liquid C5 petroleum resin, 0.5 parts by weight of leveling agent, 1 part by weight of plasticizer, 0.2 parts by weight of high Composed of molecular coupling agent and 0.2 parts by weight of antioxidant.

[0019] In the EVA with high VA content, the VA is 35 and the MI is 50.

[0020] The melting point of ethylene-acrylic acid copolymer wax is 95-105°C.

[0021] The VA in the maleic anhydride grafted EVA is 30, the MI is 150, and the grafting rate is >3%.

[0022] The melt index of the metallocene-catalyzed polyolefin is 1000 g / 10 minutes.

[0023] Th...

Embodiment 2

[0029] The cross-interface penetration viscose that present embodiment describes, it is by 10 parts by weight ethylene-acrylic acid copolymer wax, 12 parts by weight paraffin, 18 parts by weight of maleic anhydride grafted EVA, the EVA of 21 parts by weight high VA content, 15 parts by weight Parts of metallocene catalyzed polyolefin, 18 parts by weight of dehydrated malic acid rosin resin, 25 parts by weight of rosin glyceride, 8 parts by weight of liquid C5 petroleum resin, 2 parts by weight of leveling agent, 6 parts by weight of plasticizer, 1.2 parts by weight of high It consists of a molecular coupling agent and 1 part by weight of an antioxidant.

[0030] The production method of cross-interface infiltration viscose, mixing ethylene-acrylic acid copolymer wax and paraffin wax, heating to 1140°C, adding maleic anhydride grafted EVA, heating to 150°C after melting, then adding EVA with high VA content, half After melting, add metallocene catalyzed polyolefin and the remai...

Embodiment 3

[0032] The cross-interface penetration viscose that present embodiment describes, it is by 5 weight parts ethylene-acrylic acid copolymer wax, 7 weight parts paraffin, 14 weight parts maleic anhydride grafted EVA, the EVA of 15 weight parts high VA content, 10 weight parts Parts of metallocene catalyzed polyolefin, 15 parts by weight of dehydrated malic acid rosin resin, 18 parts by weight of rosin glyceride, 4 parts by weight of liquid C5 petroleum resin, 1.3 parts by weight of leveling agent, 3 parts by weight of plasticizer, 0.8 parts by weight of high Composed of molecular coupling agent and 1.1 parts by weight of antioxidant.

[0033] The production method of cross-interface infiltration viscose, mix ethylene-acrylic acid copolymer wax and paraffin wax and heat to 135°C, add maleic anhydride grafted EVA, heat to 150°C after melting, then add EVA with high VA content, half After melting, add metallocene catalyzed polyolefin and the remaining half of the antioxidant, then a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to the hot melt adhesive field, and especially discloses a cross-interface penetration adhesive which can achieve penetration adhesion to a surface film or a gold stamping layer. The penetration adhesive is composed of, by weight, 1-10 parts of ethylene-acrylic acid copolymer wax, 2-12 parts of paraffin, 10-18 parts of maleic anhydride grafting EVA, 10-21 parts of EVA with a high VA content, 6-15 parts of metallocene catalysis polyolefin, 10-18 parts of dehydrated malic acid abietin, 10-25 parts of rosin glyceride, 1-8 parts of liquid-state C5 petroleum resins, 0.5-2 parts of leveling agents, 1-6 parts of plasticizers, 0.2-1.2 parts of high-molecular coupling agents and 0.2-1 part of antioxidants. The obtained cross-interface penetration adhesive can penetrate through printing ink and the like and adheres to internal organic matters, the adhesion fastness is raised and the service life is prolonged.

Description

technical field [0001] The invention relates to the field of hot melt adhesives, in particular to a cross-interface permeable adhesive. Background technique [0002] When the existing smooth film or bronzing paper is packaged, when the existing viscose is bonded to it, it can only be bonded to its surface, resulting in poor bonding fastness, and it is easy to make the viscose and the surface film Or the bronzing layer falls off together, affecting its normal use. [0003] When bonding ordinary coated paper, pressed powder paper, etc., the hot melt adhesive has already started to solidify on the surface, and has not penetrated into the inside of the paper, so degumming is very easy to occur. Especially when bonding substrates with heavy ink and varnish systems, ordinary hot melt adhesives only bond the ink or varnish layer on the surface, and hot melt adhesives are easily plasticized or dissolved by plasticizers and organic solvents on the surface, thus greatly affect the b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J151/06C09J123/08C09J123/00C09J193/04C09J157/02C09J123/20C09J11/06
Inventor 李光鹏陈惠娟邵晓巍
Owner 浙江固特新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com