A relay and oxide technology, applied in circuits, electrical switches, electrical components, etc., to achieve excellent welding performance, greatly reduce the amount of precious metals, and reduce costs.

Active Publication Date: 2014-04-09
NINGBO ZETTLER ELECTRONICS
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005]The moving reed is a key part of the relay. At present, a large number of single precious metals or composite materials of base metals and precious metals are still used in China, which is very important for improving Quality, cost reduction, saving precious metals are all detrimental
At present, the research on moving reed materials at home and abroad is still in its infancy.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Relay

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A relay, the contact adopts double-layer silver-based composite oxide electrical contact material, and the moving spring adopts reed composite material; the double-layer silver-based composite oxide electrical contact material includes two layers, one of which is AgCuZn layer, another layer is the compound oxide layer of silver, is fixed by fusing between two layers, wherein the preparation method of the compound oxide layer of silver comprises the following steps:

[0027] (1) Alloy smelting. Ag, Sn, La, Zr are mixed according to the following mass percentages and then smelted to form an alloy melt, wherein Sn is 10%, La is 1%, Zr is 5%, and the balance is Ag. The melting temperature 600°C;

[0028] (2) Gas atomization powder making, the alloy melt is atomized by high-pressure atomization equipment to make alloy powder, wherein the gas atomization pressure is 10MPa;

[0029] (3) isostatic pressing ingot, the alloy powder is processed into embryo ingot by isostatic pre...

Embodiment 2

[0040] A relay, the contact adopts double-layer silver-based composite oxide electrical contact material, and the moving spring adopts reed composite material; the double-layer silver-based composite oxide electrical contact material includes two layers, one of which is AgCuZn layer, another layer is the compound oxide layer of silver, is fixed by fusing between two layers, wherein the preparation method of the compound oxide layer of silver comprises the following steps:

[0041] (1) Alloy smelting. Ag, Sn, La, Zr are mixed according to the following mass percentages and then smelted to form an alloy melt, wherein Sn is 5%, La is 2%, Zr is 5%, and the balance is Ag. The melting temperature is 800°C;

[0042] (2) Gas atomization powder making, the alloy melt is atomized by high-pressure atomization equipment to make alloy powder, wherein the gas atomization pressure is 15MPa;

[0043] (3) isostatic pressing ingot, the alloy powder is processed into embryo ingot by isostatic p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a relay. The contact of the relay adopts a double-layer silver-based composite oxide electric contact material; and a moving spring adopts a spring piece composite material. The silver-based composite oxide electric contact material comprises two layers, wherein one layer is a AgCuZn layer; the other layer is a silver composite oxide layer; and the two layers are fixed through fusion. The silver composite oxide layer is prepared by Ag, Sn, La and Zr. The spring piece composite material is prepared by the components with the following mass percent: 10-15% of Be, 3-5% of Zn, 10-20% of Mn, with the balance being Cu. The contact performance of the silver-based composite oxide electric contact material is improved, and meanwhile, the usage amount of the silver material is saved, and thus the cost is greatly reduced. The spring piece of the relay has excellence welding performance, bending capability and improved current-carrying capability; preparation process is simple; the usage amount of precious metals is greatly reduced; and the cost is reduced.

Description

technical field [0001] The invention relates to a relay, in particular to a relay using new materials. Background technique [0002] China's relay industry, for a long time, its production technology and production process have been mainly produced in cheap labor-intensive production methods, so the product quality, performance and price have shortcomings in the international market competition, and the performance of the same product with the same specification is very different. big difference. Therefore, the way out for the domestic relay industry lies in continuously improving the manufacturing precision of parts, focusing on product research and development, improvement of assembly production mode and improvement of reliability, in order to realize automation or semi-automation of assembly production process, and finally realize product production Integration, so as to improve the technical grade and technical content of products, improve quality and reduce costs. The...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01H1/0237H01H1/025
Inventor 陈岳建周波黄果林庆付
Owner NINGBO ZETTLER ELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com