Binding material of anti-skidding layer of road surface and preparation method

A technology of bonding materials and thin layers, applied in the direction of roads, roads, adhesives, etc., can solve problems such as brittle cracks, poor bonding, and stone falling off, and achieve the effects of simple production process, improved roughness, and increased friction

Active Publication Date: 2014-04-30
道仑(重庆)新材料技术有限公司
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the common anti-skid layer bonding materials have the following problems: insufficient shear resistance and bonding performance, delamination with the original road surface; poor bonding with the stone, resulting in stone falling off; insufficient flexibility at low temperature, brittle cracks; anti-fouling Dustproof effect is poor, color retention time is short

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Binding material of anti-skidding layer of road surface and preparation method
  • Binding material of anti-skidding layer of road surface and preparation method
  • Binding material of anti-skidding layer of road surface and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The epoxy resin formulation is shown in Table 1.

[0030] Table 1 Epoxy Resin Recipe

[0031]

[0032] Preparation Process:

[0033] Add acrylic epoxy resin, polyurethane epoxy resin and rubber epoxy resin in weight percentage to the reaction pot, raise the temperature to 70°C, control the temperature to 70°C±5°C, stir and react, after the reaction is complete, cool the reaction pot materials to 50°C, high-speed dispersion for 0.5h to obtain epoxy resin.

[0034] Examples 2-6 bonding materials, the formulations are shown in Table 2.

[0035] Table 2 embodiment 2~6 the component charging percentage of bonding material

[0036]

[0037] Preparation Process:

[0038] Mix and stir the epoxy resin prepared in Example 1 with curing agent, toner and quartz sand for 3-4 minutes to prepare the anti-skid thin-layer adhesive material for road surface.

Embodiment 7

[0039] The construction steps of embodiment 7 pavement antiskid thin layer:

[0040] 1) Clean the cement pavement or steel plate surface, and grind the surface rough,

[0041] 2) Apply the anti-skid thin-layer bonding material for road surface of Examples 2 to 6 on the cement road surface, asphalt road surface or steel plate surface,

[0042] 3) Sprinkle natural special stones or ceramic granules on the surface of the bonding material in step 1) to form a 5mm±1mm colored thin-layer anti-skid road surface.

Embodiment 8

[0043] Embodiment 8 performance test

[0044] Performance index test, except for the method indicated in the table below, the rest are tested according to the method in the traffic industry standard "Pavement Anti-skid Coating" (JT / T712~2008), the test results are shown in Table 3

[0045] Table 3 performance test results

[0046]

[0047] *Chemical corrosion resistance: After making the anti-slip thin layer with the adhesive materials of Examples 2-6, soak the thin layer with gasoline, kerosene, strong acid, strong alkali, xylene, etc. for 24 hours, and observe that there is a change.

[0048] **Low temperature crack resistance: After the adhesive materials of Examples 2-6 are made into anti-skid thin layers, the thin layers are kept in an environment of -10°C for 4 hours, and then stored at room temperature for 4 hours. After one cycle and three consecutive cycles, observe whether there are cracks, etc.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a binding material of an anti-skidding layer of a road surface and a preparation method. The binding material is composed of the following components in percentage by weight: 40%-60% of epoxy resin, 15%-25% of a curing agent, 0.5%-1% of toner and 24%-35% of quartz sand. The binding material has excellent mechanical performance, deformation performance and endurance quality and has a consistent color.

Description

technical field [0001] The invention relates to a bonding material for an anti-skid layer for road surfaces and a preparation method thereof, in particular to a bonding material for a colored anti-skid layer for road surface engineering and traffic safety and a preparation method thereof. Background technique [0002] In recent years, my country's road construction, especially expressways, has developed rapidly. The improvement of road grade, the increase of traffic volume and the acceleration of vehicle speed put forward higher requirements for the anti-skid performance of highway pavement. The "Technical Standards for Highway Engineering" (JTJ01-88) promulgated and implemented by the Ministry of Communications stipulates that the road surface should have good stability and sufficient strength, and its surface should meet the requirements of smoothness, compactness and anti-skid. There is a certain gap in the skid resistance index of existing highways, especially highway p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J163/10C09J163/00C09J11/04C09J11/06C04B26/14E01C11/24
Inventor 陈丰李锋黄小峰
Owner 道仑(重庆)新材料技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com