Metal surface treating agent

A technology of metal surface treatment and quality, applied in the direction of metal material coating process, etc., can solve the problems of poor production continuity, affecting phosphating film, waste of chemicals, etc., and achieve the effect of improving adhesion

Inactive Publication Date: 2014-04-30
CHANGSHU MEIERTE METAL PROD
View PDF11 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the temperature of the phosphating solution needs to reach 45~65°C, and the energy consumption is high; a large amount of sediment is generated during the phosphating process, which not only wastes chemicals but also increases the workload of removing the waste residue. If it is not handled properly, it will also affect the quality of the phosphating film. ;The process is complex and the production continuity is poor
At the same time, a large amount of strong acid and strong alkali need to be used in the cleaning process, which increases the pollutant discharge load

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] A metal surface treatment agent consisting of the following components:

[0011] 5 parts by mass of vinyltrimethoxysilane, 0.5 parts by mass of lauryl alcohol, 2 parts by mass of lauryl alcohol, 0.3 parts by mass of hydroquinone, 13 parts by mass of ethanol, 95 parts by mass of water, 8 parts by mass of γ-glycidyl Ether group trimethoxysilane, 0.1 parts by mass benzotriazole, 0.2 parts by mass 4,4-methylene (2,6-di-tert-butylphenol), 0.8 parts by mass tallow amine, 0.1 parts by mass octane Base amine, 0.4 parts by mass of decylamine, 0.3 parts by mass of triethylamine, 0.2 parts by mass of 8-hydroxyquinoline, 0.3 parts by mass of hexylamine, 0.1 parts by mass of dipentylamine, 12 parts by mass of water-soluble chitin, 0.2 parts by mass of phenylnaphthylamine, 0.1 parts by mass of didodecanylamine, 0.2 parts by mass of dioctadecylamine, 0.4 parts by mass of triethanolamine, 0.2 parts by mass of dodecylamine, 0.1 parts by mass of hexadecylamine , 0.5 parts by mass of oct...

Embodiment 2

[0013] A metal surface treatment agent consisting of the following components:

[0014] 4 parts by mass of vinyltrimethoxysilane, 0.5 parts by mass of lauryl alcohol, 2 parts by mass of lauryl alcohol, 0.3 parts by mass of hydroquinone, 13 parts by mass of ethanol, 95 parts by mass of water, 8 parts by mass of γ-epoxypropylene Ether group trimethoxysilane, 0.1 parts by mass benzotriazole, 0.2 parts by mass 4,4-methylene (2,6-di-tert-butylphenol), 0.8 parts by mass tallow amine, 0.1 parts by mass octane Base amine, 0.4 parts by mass of decylamine, 0.3 parts by mass of triethylamine, 0.2 parts by mass of 8-hydroxyquinoline, 0.3 parts by mass of hexylamine, 0.1 parts by mass of dipentylamine, 12 parts by mass of water-soluble chitin, 0.2 parts by mass of phenylnaphthylamine, 0.1 parts by mass of didodecanylamine, 0.2 parts by mass of dioctadecylamine, 0.4 parts by mass of triethanolamine, 0.2 parts by mass of dodecylamine, 0.1 parts by mass of hexadecylamine , 0.5 parts by mass ...

Embodiment 3

[0016] A metal surface treatment agent consisting of the following components:

[0017] 4.5 parts by mass of vinyltrimethoxysilane, 0.5 parts by mass of lauryl alcohol, 2 parts by mass of lauryl alcohol, 0.3 parts by mass of hydroquinone, 13 parts by mass of ethanol, 95 parts by mass of water, 8 parts by mass of gamma-glycidyl propylene Ether group trimethoxysilane, 0.1 parts by mass benzotriazole, 0.2 parts by mass 4,4-methylene (2,6-di-tert-butylphenol), 0.8 parts by mass tallow amine, 0.1 parts by mass octane Base amine, 0.4 parts by mass of decylamine, 0.3 parts by mass of triethylamine, 0.2 parts by mass of 8-hydroxyquinoline, 0.3 parts by mass of hexylamine, 0.1 parts by mass of dipentylamine, 12 parts by mass of water-soluble chitin, 0.2 parts by mass of phenylnaphthylamine, 0.1 parts by mass of didodecanylamine, 0.2 parts by mass of dioctadecylamine, 0.4 parts by mass of triethanolamine, 0.2 parts by mass of dodecylamine, 0.1 parts by mass of hexadecylamine , 0.5 part...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a metal surface treating agent. The metal surface treating agent comprises the following components: vinyl trimethoxy silane, laurinol, 2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate, hydroquinone, ethanol, water, gamma-allyl glycidyl ether trimethoxy silane, benzotriazole, 4,4-methylene (2,6-di-tert-butylphenol), tallow amine, octyl amine, decyl alkyl amine, triethylamine, 8-hydroxyquinoline, hexyl amine, diamylamine, water-soluble chitin, nonox, didodecylamine, dioctadecylamine, triethanolamine, dodecylamine, hexadecylamine, octadecylamine, resorcinol, pyrocatechol, catechol, 2,6-di-tert-butyl-alpha-dimethylamino hydroquinone, fatty alcohol-polyoxyethylene ether, alkylphenol ethoxylates, polyoxyethylene stearates, and sodium bicarbonate. The metal surface treating agent obviously improves the adhesive force on the metal surface and realizes the corrosion resistance during coating of the whole metal.

Description

technical field [0001] The present invention relates to a metal surface treatment agent. Background technique [0002] At present, in the coating industry, the coating of metal products, especially plates, usually uses a phosphating process to improve the adhesion between the coating and the metal. However, the temperature of the phosphating solution needs to reach 45~65°C, and the energy consumption is high; a large amount of sediment is generated during the phosphating process, which not only wastes chemicals but also increases the workload of removing the waste residue. If it is not handled properly, it will also affect the quality of the phosphating film. ; The process is complex and the production continuity is poor. At the same time, a large amount of strong acid and strong alkali needs to be used in the cleaning process, which increases the pollutant discharge load. Contents of the invention [0003] The object of the present invention is to provide a metal surfac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C22/05
Inventor 钱建东
Owner CHANGSHU MEIERTE METAL PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap