A preparation method of a phase change energy storage type thermal insulation composite board

A technology for thermal insulation composite panels and phase change energy storage, which is applied in chemical instruments and methods, materials for heat exchange, layered products of hydraulic substances, etc. It has obvious problems such as low heat storage and release capacity, and achieves good chemical stability, improved mechanical properties, and low production costs.

Active Publication Date: 2016-03-30
CHINA PETROLEUM & CHEM CORP +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the porous particles used in this invention are also conventional hollow vitrified microspheres, expanded perlite or activated carbon particles. not obvious

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of a phase change energy storage type thermal insulation composite board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Paraffin wax with a melting point of 25° C. and a latent heat of phase change of 147 kJ / kg was selected as the organic phase change material. First dissolve 58 parts of paraffin in 280 parts of ethanol solution, heat the organic solution to 40°C, stir at constant temperature for 30 minutes, then slowly add 13 parts of nanometer γ-alumina and 10 parts of coupling agent γ-aminopropyltriethoxy Silane, stirred at high speed for 3 hours, filtered, washed and dried to prepare phase change energy storage aggregates. Then 100 parts of cement, 80 parts of phase change energy storage aggregate, 18 parts of water and 2 parts of reinforcing fiber are blended, stirred evenly, put into a mold and pressed to obtain a phase change energy storage surface layer. The latent heat value of the phase change energy storage surface layer measured by DSC is 52kJ / kg.

[0026] The polyurethane foam board added with flame retardant is used as the insulation board, and the phase change energy stor...

Embodiment 2

[0033] Paraffin wax with a melting point of 30° C. and a latent heat of phase change of 155 kJ / kg was selected as the organic phase change material. Dissolve 20 parts of paraffin in 100 parts of ethanol solution, heat to 50°C, stir at constant temperature for 30 minutes, then slowly add 5 parts of γ-alumina and 6 parts of coupling agent γ-mercaptopropyltrimethoxysilane, and stir at high speed for 3 hours After filtering, washing and drying, the phase change energy storage aggregate can be prepared. Then blend 100 parts of plaster of paris, 30 parts of phase change energy storage aggregate, 35 parts of water, 1 part of reinforcing fiber and 0.5 part of retarder, mix well, put it into a mold and press it to obtain phase change energy storage Surface layer. The latent heat value of the phase change energy storage surface layer measured by DSC is 29kJ / kg.

[0034] The phenolic foam board added with flame retardant is used as the insulation board, and the phase-change energy stor...

Embodiment 3

[0036] Paraffin wax with a melting point of 49°C and a latent heat of phase change of 165kJ / kg was selected as the organic phase change material. First dissolve 40 parts of paraffin in 100 parts of ethanol, heat to 50°C, stir at constant temperature for 30 minutes, then slowly add 7 parts of nanometer γ-alumina and 6 parts of coupling agent γ-aminopropyltriethoxysilane, and stir at high speed After 3 hours, the phase change energy storage aggregate can be prepared after filtering, washing and drying. Then blend 100 parts of plaster of paris, 50 parts of phase change energy storage aggregate, 40 parts of water, 1 part of reinforcing fiber and 0.5 part of retarder, mix well, put it into a mold and press it to obtain phase change energy storage Surface layer. The latent heat value of the phase change energy storage surface layer measured by DSC is 44kJ / kg.

[0037] The polyurethane foam board added with flame retardant is used as the insulation board, and the phase change energ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
phase transition temperatureaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method for a phase-change energy storage type insulating composite board. The preparation method comprises the following steps: dissolving an organic phase-change material into an organic solvent, wherein the mass ratio of the organic phase-change material to the organic solvent is 1:1 to 1:10; slowing adding a carrier gamma-aluminium oxide and a coupling agent, stirring at high speed for 2-5 h to enable the carrier to absorb the organic phase-change material fully, filtering, washing, and drying to obtain a phase-change energy storage aggregate, wherein the mass ratio of the gamma-aluminium oxide to the organic phase-change material is 1:1 to 1:6; mixing the phase-change energy storage aggregate, a basis material and water, placing the mixture into a mould, pressing to obtain a phase-change energy storage type surface layer, and adhering the phase-change energy storage type surface layer on the surface of an insulating board to obtain the phase-change energy storage type insulating composite board. The phase-change energy storage type insulating composite board provided by the invention has the advantages of capacity of phase-change energy storage and temperature adjustment, high pressure resistance, moisture protection, corrosion resistance, environmental protection, innocuity and the like.

Description

technical field [0001] The invention relates to a preparation method of a thermal insulation composite board, in particular to a preparation method of a thermal insulation composite board with phase change energy storage performance. Background technique [0002] The energy consumption per unit building area in my country is three times that of developed countries with similar climate conditions, and 95% of buildings are high-energy buildings, and building energy consumption accounts for about 30% of the total energy consumption of the whole society. my country is relatively energy-deficient, and its per capita energy consumption is only 40% of the world level, but its total energy consumption ranks second in the world. Therefore, building energy conservation is an extremely important and urgent subject for our country. [0003] At present, domestic thermal insulation composite panels are generally composed of outer panels and thermal insulation materials. The thermal insul...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B32B13/04C09K5/06C04B28/00
Inventor 马蕊英赵亮王海洋方向晨王刚
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap