Antibacterial EVA (Ethylene-Vinyl Acetate) foam material

A technology of foaming material and antistatic agent, applied in the field of antibacterial EVA foaming material, can solve the problems of no antibacterial function, low resilience of EVA foaming material, threat to people's safety, etc., and achieve good antibacterial and antistatic functions , Good rebound and anti-seismic effect, and the effect of a wide range of applications

Inactive Publication Date: 2014-05-07
NANTONG HAIOU LIFE SAVING & PROTECTION EQUIP
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Now marine lifejackets generally use EVA foam material as buoyancy material, and when producing EVA foam material, static electricity is often generated, which seriously threatens people's safety; at present, AC foaming agent is generally used in EVA foam, but AC foam The decomposition temperature of the agent is high, and the resilience of the prepared EVA foam material is not high, and the softness is poor. At the same time, most of the EVA foam materials currently on the market do not have antibacterial function.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] An antibacterial EVA foam material, comprising the following components in parts by weight: 80 parts of ethylene-vinyl acetate copolymer, 5 parts of ethylene-acrylic acid copolymer, 6 parts of polyolefin elastomer, 0.5 part of crosslinking agent DCP , 0.5 parts of barium stearate, 10 parts of microcapsule foaming agent, 5 parts of glyceryl monostearate, 1 part of nano-titanium dioxide, and 2 parts of p-chloro-m-xylenol.

[0014] The preparation method of the antibacterial EVA foam material of the present invention is to add the above-mentioned raw materials into a kneading machine and knead at the same time to obtain a mixing material, and then cover the upper and lower surfaces of the kneading material with a polyester film, and mold it on a flat vulcanizing machine; The sample is foamed on a flat plate, and the polyester film can be removed after cooling.

[0015] The antibacterial EVA foam material obtained in this embodiment has a microporous structure, smooth surfa...

Embodiment 2

[0020] An antibacterial EVA foam material, comprising the following components in parts by weight: 100 parts of ethylene-vinyl acetate copolymer, 10 parts of ethylene-acrylic acid copolymer, 12 parts of polyolefin elastomer, 1 part of crosslinking agent DCP, hard 1 part of barium stearate, 15 parts of microcapsule foaming agent, 8 parts of glyceryl monostearate, 3 parts of nano-titanium dioxide, and 4 parts of p-chloro-m-xylenol.

[0021] The preparation method of the antibacterial EVA foam material of the present embodiment is identical with embodiment 1.

[0022] The antibacterial EVA foam material obtained in this embodiment has a microporous structure, smooth surface, soft texture, no smell, good resilience, and a density of 0.38g / cm 3 , the tensile strength is 3.0MPa, the rebound rate is 54%, and the hardness is 49.

[0023] The antibacterial property of present embodiment is tested simultaneously:

[0024] The antibacterial effect of conventional microorganisms was tes...

Embodiment 3

[0027] An antibacterial EVA foam material, comprising the following components in parts by weight: 90 parts of ethylene-vinyl acetate copolymer, 7 parts of ethylene-acrylic acid copolymer, 10 parts of polyolefin elastomer, 0.6 part of crosslinking agent DCP , 0.8 parts of barium stearate, 12 parts of microcapsule foaming agent, 7 parts of glyceryl monostearate, 2 parts of nano-titanium dioxide, and 3 parts of p-chloro-m-xylphenol.

[0028] The preparation method of the antibacterial EVA foam material of the present embodiment is identical with embodiment 1.

[0029] The antibacterial EVA foam material obtained in this embodiment has a microporous structure, smooth surface, soft texture, no smell, good resilience, and a density of 0.30g / cm 3 , the tensile strength is 2.5MPa, the rebound rate is 56%, and the hardness is 50.

[0030] Simultaneously the antibacterial property of present embodiment product is tested:

[0031] Using routine microbial antibacterial effect test, the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
tensile strengthaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to an antibacterial EVA (Ethylene-Vinyl Acetate) foam material belonging to the technical field of high-molecular materials. The antibacterial EVA foam material comprises the following components in parts by weight: 80-100 parts of EVA copolymers, 5-10 parts of ethylene-propylene copolymers, 6-12 parts of polyolefin elastomer, 0.5-1 part of a crosslinking agent, 0.5-1 part of barium stearate, 10-15 parts of a microcapsule foaming agent, 5-8 parts of antistatic agent, 1-3 parts of nanometer titanium dioxide and 2-4 parts of chloroxylenol. The antibacterial EVA foam material provided by the invention is soft in texture, smooth in surface, good in rebound vibration resistant effect, favorable in antibacterial and antistatic functions and relatively wide in application range, not only can be used for manufacturing life-saving devices, but also can be used in other fields such as packaging materials and the like.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to an antibacterial EVA foam material. Background technique [0002] Ethylene-vinyl acetate copolymer, abbreviated as EVA in English, has been widely used in sports equipment, life-saving equipment, household products and other fields due to its excellent coloring performance and good flexibility since its inception. [0003] A life jacket is a life-saving garment designed similar to a vest, made of nylon fabric, neoprene, buoyancy material, inflatable material or reflective material, etc. It has enough buoyancy to wear on the body, so that the head of the person who falls into the water can be exposed The water surface is one of the life-saving equipment on ships and aircrafts. Now marine lifejackets generally use EVA foam material as buoyancy material, and when producing EVA foam material, static electricity is often generated, which seriously threatens peop...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L23/00C08K13/02C08K5/103C08K5/098C08K3/22C08K5/136C08K5/14C08J9/04
CPCC08K2003/2241C08L23/0853C08K2201/011C08K2201/017C08L2205/03C08L23/0869C08L23/00C08K13/02C08K5/103C08K5/098C08K5/136C08K5/14
Inventor 曹伟葛锦妹
Owner NANTONG HAIOU LIFE SAVING & PROTECTION EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap