Pit and fissure sealant for dental department

A pit and fissure sealing and dental technology, applied in dental preparations, dentistry, dental prostheses, etc., can solve the problems of large foreign exchange consumption, product dependence on imports, high price, etc. high connection effect

Active Publication Date: 2014-06-25
BEIJING GOOCHE HEALTH TECH
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no domestic manufacturer of dental light-cured fluoride-containing pit and fissure sealant materials. A...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pit and fissure sealant for dental department
  • Pit and fissure sealant for dental department
  • Pit and fissure sealant for dental department

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～3

[0038] The composition of the base resin (ie, the polymerizable acrylic resin containing the photoinitiating system) of Examples 1-3 of the present invention is shown in Table 1. The distribution ratio of the product components of Examples 1-3 and their physical properties are recorded in Table 2.

[0039] preparation:

[0040] (1) Preparation of filler submicron silica powder: pour 100ml of 17.15mol / L absolute ethanol solution and 27ml of 25% ammonia solution into a 1L glass reactor, and mechanically stir for 1.5 to 2.5 hours; mix 0.5 Dissolve gPEG1000 in 56ml of deionized water, add the aqueous solution of the dispersant to the reactor, stir at high speed to mix the solution evenly, slowly add 90ml, 4.48mol / L Si(OC 2 h 5 ) 4 , high-speed stirring and reacting for 40 minutes to obtain a uniform and stable sol; the sol was spray-dried, the inlet temperature of the spray dryer was 175-185°C, and the outlet temperature was 85-95°C to obtain spherical carbon dioxide with an ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a pit and fissure sealant for dental department. The pit and fissure sealant comprises the following two compositions in percentage by weight: 5%-30% of superfine structured packing with an average particle size of 0.05-0.4mu m, and 95%-70% of polymerizable acrylate monomer containing a photo-initiating system, wherein the superfine structured packing is superfine silica structured powder packing which is treated by fluoride. The pit and fissure sealant for dental department is high in hardness, good in wear resistance, high in compressive strength and bending strength, and low in manufacturing cost. The superfine silica structured powder packing which is treated by fluoride can continuously release fluorine ions.

Description

technical field [0001] The invention relates to a dental pit and fissure sealant, in particular to a dental pit and fissure sealing composition capable of continuously releasing fluoride ions. Background technique [0002] Pit and fissure sealant, referred to as pit and fissure sealant, is a new type of dental polymer material developed in the late 1960s. Usually, this material has good fluidity and can reach the pits and fissures. It is applied to the pits and fissures of the tooth surface, and after curing, it forms a protective barrier, which can effectively seal the pits and fissures and isolate the oral environment. The caries-causing factors can damage the teeth, so as to prevent the occurrence of caries. Its advent has opened up a new approach to prevent dental caries for oral preventive medicine. [0003] The application of pit and fissure sealant as an effective method to prevent pit and fissure caries of deciduous molars and young permanent teeth has been confirm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61K6/00C08F222/20C08F222/22C08F220/34C08F2/48C08K9/02C08K9/06C08K3/36C08K3/34
Inventor 茹岩岩陈亚东
Owner BEIJING GOOCHE HEALTH TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap