Chlorinated Paraffin Rosin Lead Resin Flame Retardant Adhesive

A technology of rosin lead resin and flame-retardant adhesives, which is applied in adhesives, non-polymer organic compound adhesives, non-polymer adhesive additives, etc., can solve problems such as not found, and achieve easy manufacturing, easy-to-obtain raw materials, The effect of process simplification

Active Publication Date: 2015-09-30
SHANGHAI STAR RUBBER PROD CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] After searching for Chinese published patents, no solution identical to this patent application was found

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] The preparation method of chlorinated paraffin rosin lead resin flame retardant adhesive of the present invention is characterized in that: its formula is by weight, by 90-120 parts of methyl acrylate, 13-30 parts of rosin lead resin, 350-400 parts of isobutyl acrylate , 150-200 parts of ethyl acrylate, 15-20 parts of acrylic acid, 1-5 parts of aluminum sulfate, 1-5 parts of chlorinated paraffin, 1-5 parts of decabromodiphenyl ether; mix all the materials, 80-90 ℃ The reaction is carried out for 60-90 minutes to obtain the product.

Embodiment 2

[0014] The preparation method of chlorinated paraffin rosin lead resin flame-retardant adhesive of the present invention is characterized in that: its formula is by weight, by 90 parts of methyl acrylate, 13 parts of rosin lead resin, 350 parts of isobutyl acrylate, 150 parts of ethyl acrylate , 15 parts of acrylic acid, 1-5 parts of aluminum sulfate, 1-5 parts of chlorinated paraffin, and 1-5 parts of decabromodiphenyl ether; mix all the materials and react at 80-90 ° C for 60-90 minutes to obtain the product .

Embodiment 3

[0016] The preparation method of chlorinated paraffin rosin lead resin flame-retardant adhesive of the present invention is characterized in that: its formula is by weight, by 120 parts of methyl acrylate, 30 parts of rosin lead resin, 400 parts of isobutyl acrylate, 200 parts of ethyl acrylate , 20 parts of acrylic acid, 1-5 parts of aluminum sulfate, 1-5 parts of chlorinated paraffin, and 1-5 parts of decabromodiphenyl ether; mix all the materials and react at 80-90 ° C for 60-90 minutes to obtain the product .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a chlorinated paraffin / rosin lead resin flame-retardant adhesive which is characterized by comprising the following components in parts by weight: 90-120 parts of methyl acrylate, 13-30 parts of rosin lead resin, 350-400 parts of isobutyl acrylate, 150-200 parts of ethyl acrylate, 15-20 parts of acrylic acid, 1-5 parts of aluminum sulfate, 1-5 parts of chlorinated paraffin and 1-5 parts of decabromodiphenyl oxide. The adhesive has the advantages of accessible raw materials, low cost, environmental protection and favorable effect, and is convenient to use.

Description

technical field [0001] The invention belongs to an adhesive. Background technique [0002] Adhesive bonding (bonding, bonding, cementation, gluing) refers to the technology of connecting the surfaces of homogeneous or heterogeneous objects with adhesives, which has the characteristics of continuous stress distribution, light weight, or sealing, and low temperature in most processes. Gluing is especially suitable for the connection of different materials, different thicknesses, ultra-thin specifications and complex components. Glue is the fastest growing in modern times, with a wide range of applications, and has a major impact on the progress of high-tech science and technology and the improvement of people's daily life. Therefore, it is very important to research, develop and produce various adhesives. Adhesive (Bonding agent) is one of the most important auxiliary materials and is widely used in packaging operations. Adhesives are sticky substances that join two separat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J4/02C09J4/06C09J11/04C09J11/06
Inventor 杨毅李安平
Owner SHANGHAI STAR RUBBER PROD CO LTD