Photocuring epoxy resin-base film for flexible or thin-film solar cells and preparation method thereof

A technology for curing epoxy resin and solar cells, applied in circuits, photovoltaic power generation, electrical components, etc., can solve the problem of low shrinkage, achieve large absorption, improve performance, and prevent light escape

Inactive Publication Date: 2014-07-02
ZHONGYUAN ENGINEERING COLLEGE
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

4. low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] (1) Glycidyl ether epoxy resin (Zhejiang Kaihua Chengxin Resin Co., Ltd.) 100 Kg; nano-aluminum powder 0.0001Kg; Oxygen) hexane) 0.8Kg; UV absorber (2-hydroxy-4 methoxybenzophenone) 0.1 Kg; antioxidant (tetra[B-(3,5-di-tert-butyl-4-hydroxy phenyl)propionate]pentaerythritol ester) 0.1 Kg; amine light stabilizer (bis(1-octyloxy-2,2,6,6-tetramethyl-4-piperidinyl)decanediester) 0.2 Kg , Stir and blend evenly with a stirrer at a temperature of -10-5°C;

[0022] (2) Import the above blend into a screw mixing extruder for blending and extrusion, the temperature is controlled at 120-290 °C, the extrudate is filtered through a 180-mesh filter, and metered and extruded (the pressure difference between the inlet and outlet of the metering pump is 2MPa) , cast film thickness 50UM, 10 ℃ air cooling, 4 times drafting ratio drafting, release paper coating, coiling and other processes to obtain a polycarbonate film for flexible or thin film solar cells. The performance of the thin-fi...

Embodiment 2

[0024](1) Glycidyl ester epoxy resin (Foshan Longxiang Resin Raw Materials Co., Ltd.) 100 Kg; nano-aluminum powder 0.1 Kg; cross-linking curing agent (2,5-dimethyl-2,5 bis(tert-butyl Peroxy) hexane) 0.5 Kg; UV absorber (2-hydroxy-4 methoxybenzophenone) 0.12 Kg; antioxidant (tris(nonylphenyl) phosphite) 0.2 Kg; amine light Stabilizer (bis(1-octyloxy-2,2,6,6-tetramethyl-4-piperidinyl)decanediester) 0.1 Kg, stir with a stirrer at -10-40℃ mix well;

[0025] (2) Import the above blend into a screw mixing extruder for blending and extrusion, the temperature is controlled at 120-290 °C, the extrudate is filtered through a 180-mesh filter, and metered and extruded (the pressure difference between the inlet and outlet of the metering pump is 2MPa) , cast film thickness 50UM, 10 ℃ air cooling, 4 times drafting ratio drafting, release paper coating, coiling and other processes to obtain a polycarbonate film for flexible or thin film solar cells. The performance of the thin-film solar c...

Embodiment 3

[0027] (1) Glycidyl amine epoxy resin (Foshan Longxiang Resin Raw Materials Co., Ltd.) 100 Kg; nano-aluminum powder, 0.05Kg; 3,5-trimethylcyclohexane) 1.25Kg; UV absorber (2-hydroxy-4 n-octyloxybenzophenone) 0.16 Kg; antioxidant (phosphorous acid tris(mononylbenzene and di nonylbenzene) mixed ester) 0.15 Kg; amine light stabilizer ((2,2,6,6-tetramethyl-4-piperidinyl) sebacate) 0.15 Kg, with a stirrer at 0-10 Stir and blend evenly under the temperature environment of ℃;

[0028] (2) Import the above blend into a screw mixing extruder for blending and extrusion, the temperature is controlled at 120-290 °C, the extrudate is filtered through a 180-mesh filter, and metered and extruded (the pressure difference between the inlet and outlet of the metering pump is 2MPa) , cast film thickness 50UM, 10 ℃ air cooling, 4 times drafting ratio drafting, release paper coating, coiling and other processes to obtain a polycarbonate film for flexible or thin film solar cells.

[0029] The pe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a photocuring epoxy resin-base film for flexible or thin-film solar cells and a preparation method thereof. The film is prepared from the following components in parts by weight: 100 parts of epoxy resin, 0.0001-0.1 part of nano aluminum powder, 0.5-1.25 parts of photocuring agent, 0.1-0.2 part of antioxidant, 0.1-0.2 part of ultraviolet absorbent and 0.1-0.2 part of amine photostabilizer. The product is attached to the photic surface of the thin-film solar cell or used as an upper packaging film of the solar cell to directly enhance the generating efficiency of the flexible or thin-film solar cell.

Description

technical field [0001] The invention relates to a photocurable epoxy resin base film for flexible or thin film solar cells and a preparation method thereof. By using the film to encapsulate the light-incident surface of the flexible or thin film solar cell, the efficiency of the flexible or thin film solar cell can be directly improved. Background technique [0002] Among the effective utilization of solar energy projects: photovoltaic utilization is the fastest growing and most dynamic research field in recent years. The production of general solar cells is mainly based on semiconductor materials, which use photoelectric materials to absorb light energy and generate photoelectric conversion reactions to generate electricity. According to the different materials used, solar cells can be divided into: 1. Silicon solar cells; 2. Solar cells made of inorganic salts such as gallium arsenide III-V compounds, cadmium sulfide, copper indium selenide and other multi-component compou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L63/00C08K13/02C08K3/08C08K5/3435H01L31/048
CPCY02E10/50
Inventor 张迎晨吴红艳
Owner ZHONGYUAN ENGINEERING COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap