Molybdenum-tungsten acid scandium composite material and preparation method thereof

A composite material, scandium tungstate technology, applied in the field of composite materials, can solve problems such as easy expansion and poor strength, achieve the effects of excellent performance, improve high temperature strength, and avoid separation

Active Publication Date: 2014-07-09
HARBIN INST OF TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a molybdenum-scandium tungstate composite material and its preparation method in order to solve th

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Molybdenum-tungsten acid scandium composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0014] Specific implementation mode 1: In this embodiment, the molybdenum-scandium tungstate composite material is made of 35%-75% scandium tungstate, 1%-10% iron and 20%-60% molybdenum according to the mass percentage; the tungsten The mass purity of scandium acid is not less than 98%, and the mass purity of iron is not less than 99%.

Example Embodiment

[0015] Specific embodiment two: this embodiment is different from specific embodiment one in that the content of molybdenum-scandium tungstate composite material is 40%~70% scandium tungstate, 3%~7% iron and 25%~55% by mass percentage. Made of molybdenum. Others are the same as the first embodiment.

Example Embodiment

[0016] Specific embodiment three: This embodiment is different from one of specific embodiments one or two in that the molybdenum-scandium tungstate composite material is made of 60% scandium tungstate, 5% iron and 35% molybdenum according to the mass percentage. Others are the same as the first or second embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Temperature tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of composite material preparation, and particularly relates to a molybdenum-tungsten acid scandium composite material and a preparation method thereof. The molybdenum-tungsten acid scandium composite material is made of tungsten acid scandium, iron and molybdenum. The preparation method includes 1, weighing raw materials; 2, dispersing the raw materials in step 1 in a dispersant, drying under a vacuum condition, and ball-milling slurry after drying to break the slurry by grinding to obtain mixed powder; 3, sintering the mixed powder to obtain the molybdenum-tungsten acid scandium composite material. The molybdenum-tungsten acid scandium composite material prepared by the method is 300-400MPa in tensile strength at room temperature, 120-160MPa in tensile strength at 600 DEG C, -1x10-6K-1-0.3x10-6K-1 in thermal expansion coefficient at 25-600 DEG C, and smaller than or equal to 100GPa in modulus of elasticity.

Description

technical field [0001] The invention belongs to the technical field of composite materials, and in particular relates to a composite material and a preparation method thereof. Background technique [0002] The material "expands with heat and contracts with cold" due to the anharmonic vibration effect of the lattice thermal vibration. But some materials are contrary to this. They shrink when heated and expand when cooled, that is, they have a "Negative Thermal Expansion" (Negative Thermal Expansion, NTE for short) effect. We call such materials negative thermal expansion materials or thermally shrinkable materials. Scandium tungstate exhibits negative thermal expansion behavior below 1200°C. [0003] The technical importance of scandium tungstate mainly reflects that the high negative expansion properties make it possible to control the expansion coefficient of high expansion materials without destroying the excellent properties of high expansion materials; it provides a rar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F3/14B22F1/00
Inventor 韩文波张幸红王鹏赵广东张兆停程业红周长灵
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap