High-power lithium ion battery pole piece and preparation process thereof
A lithium-ion battery and a preparation process technology are applied in the field of high-power lithium-ion battery pole pieces and the preparation process thereof, and can solve the problems that the lithium-ion battery is difficult to meet requirements, high equipment requirements, complex processes, etc., and achieves low internal resistance, The effect of high conductivity and sufficient and uniform mixing
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0020] 1. Slurry preparation
[0021] (1) Preparation of conductive paste
[0022] First, 30g of Ketjen Black and polyurethane ball milling with a volume of 1 / 3 of Ketjen Black for 30-120 minutes; Vacuum bake at ℃ for 120 minutes, the vacuum degree is: -0.09MPa; weigh 100g of organic solvent and heat it to 40~60℃; add the binder to the organic solvent, stir in vacuum for 60~80 minutes, the stirring speed is: 800 ~2000 rpm to get the glue; add 30g of baked Ketjen Black to the glue, stir at high speed for 100~240 minutes, and the stirring speed is 1800~3000 rpm; stir slowly in vacuum for 30~60 minutes Remove air bubbles and adjust viscosity, the viscosity range is 500~1000mpa·s, and sieve to obtain conductive paste.
[0023] (2) Preparation of cathode slurry
[0024] First weigh 5000g of lithium cobalt oxide, Super P222g, VGCF111g, and 222g of binder, respectively, and place them in a vacuum oven at 120°C for 60-180 minutes; then vacuum-stir the binder and organic solvent for...
Embodiment 2
[0031] It is basically the same as Example 1, the main difference is that the conductive agent is composed of 70% Ketjen black and 30% VGCF, and the components of the positive electrode slurry include lithium cobaltate 5000g, Super P191g, VGCF81g, binder 191.3g, The components of the positive electrode slurry include mesophase carbon microspheres 3000g, Super P64.9g, VGCF64.9g, and binder 113.5g.
PUM
Property | Measurement | Unit |
---|---|---|
viscosity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com