A technology for acid etching waste liquid and copper recovery, applied in the field of environmental engineering, can solve the problems of affecting purity, value discount, and poor sales, and achieve the effects of reducing etching speed, inhibiting back-dissolution, and improving current efficiency

Active Publication Date: 2016-04-20
GUANGZHOU HONWAY TECH CORP +1
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing method of direct electrolytic recovery of copper from acidic etching waste liquid is the membrane electrolysis method, because the acidic etching liquid contains a large amount of Cl - (The concentration is between 200g / L-330g / L), which has a strong depolarization effect, making the copper easily obtained in the electrolysis process of the etching waste liquid be powdery or produce serious nodular phenomenon, nodular Copper is easy to block or pierce the diaphragm, causing electrolysis equipment to be paralyzed and affecting production
However, copper powder is easy to peel off to the bottom of the cathode tank, and a special auxiliary system for copper powder removal is required, and copper powder is easily oxidized and discolored, which affects purity, poor appearance, and its value will be greatly reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The acidic etching waste solution was taken from the acidic etching production line of an electronics factory in Guangdong Province, and the solution was dark green. After analysis, its total copper content is 152.2g / L, HCl content is 73.5g / L, Cl - The content is 305.6g / L. Use this as the anolyte and catholyte, add 1.0% of 50% hydrazine hydrate to the catholyte before electrolysis to make it fully react, then add 20mg / L sodium polydithiopropanesulfonate (SPS) and 20mg / L of polyvinyl alcohol. Through direct current electrolysis, under stirring conditions (100r / min), the cathode current density is 1000A / m respectively 2 、600A / m 2 、300A / m 2 Under the conditions of continuous electrolysis for 8 hours, a relatively dense copper block can be obtained.

[0025] The cathode-deposited copper block has no knots, will not pierce the separator and is easy to peel off and form. The current efficiency of cathode-deposited copper is 91.6%, and the average copper deposition rate ...

Embodiment 2

[0027] The acidic etching waste solution was taken from the acidic etching production line of an electronics factory in Guangdong Province, and the solution was dark green. After analysis, its total copper content is 127.5g / L, HCl content is 64.6g / L, Cl - The content is 273.5g / L. Use this as the anolyte and catholyte. Before electrolysis, add 0.8% of 50% hydroxylamine to the catholyte to make it fully react, and then add 15mg / L sodium dimethylformamide sulfonate (TPS) and poly(dimethoxylate) Sodium thiopropane sulfonate (SPS) composition, 15 mg / L polyvinyl alcohol. Through direct current electrolysis, under stirring conditions (200r / min), the current density of the cathode is 800A / m 2 、500A / m 2 、300A / m 2 Under the condition of continuous electrolysis for 7 hours, a relatively dense copper block can be obtained.

[0028] The cathode-deposited copper block has no knots, will not pierce the separator and is easy to peel off and form. The current efficiency of cathode-deposit...

Embodiment 3

[0030] The acidic etching waste solution was taken from the acidic etching production line of an electronics factory in Guangdong Province, and the solution was dark green. After analysis, its total copper content is 108.2g / L, HCl content is 57.2g / L, Cl - The content is 266.8g / L. Use this as the anolyte and catholyte, add 0.5% of 50% hydrazine hydrate to the catholyte before electrolysis to make it fully react, and then add 15mg / L of 3-mercapto-1-propanesulfonate sodium (MPS ) and 10mg / L of polyvinyl alcohol. Through direct current electrolysis, under stirring conditions (150r / min), according to the cathode current density of 700A / m 2 、500A / m 2 、200A / m 2 Under the condition of continuous electrolysis for 7 hours, a relatively dense copper block can be obtained.

[0031] The cathode-deposited copper block has no knots, will not pierce the separator and is easy to peel off and form. The current efficiency of cathode-deposited copper is 92.8%, and the average copper depositi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for recovering copper from an acidic etching waste liquid, which comprises the following steps: by using the acidic etching waste liquid emitted by a PCB (printed circuit board) etching process as a catholyte and anolyte, sequentially adding an accelerator, a grain refiner and a leveling agent into the catholyte, and carrying out direct-current electrolysis at the cathode current density of 100-1000A / m<2> for 10-30 hours, thereby obtaining the metal copper in the cathode chamber, wherein the accelerator is an ammonia derivative, the grain refiner is a sulfonic organic sulfide, and the leveling agent is polyvinyl alcohol. The method can be used for directly obtaining a copper block, and the deposited copper block has the advantages of high purity, easy stripping and no branch and can not penetrate through the diaphragm.

Description

technical field [0001] The invention relates to the technical field of environmental engineering, in particular to a method for recovering copper from acidic etching waste liquid. Background technique [0002] Acid etching solution is an etching solution used in the etching process in the production process of printed circuit boards (especially the production of fine lines and the inner layer of multi-layer boards), mainly including HCl / NaCl / CuCl 2 System, HCl / NH 4 Cl / CuCl 2 System, HCl / CuCl 2 system. With the progress of the etching process, the Cu in the etching solution 2+ Concentration decreases continuously, Cu + And the total copper concentration continues to rise, and the etching rate decreases. At this time, it is necessary to discharge the etching waste liquid or perform regeneration. The copper concentration in the etching waste liquid is very high, between 100g / L-160g / L, direct discharge will seriously pollute the environment, if the high value-added copper ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C25C1/12C22B7/00C23F1/46
CPCY02P10/20
Inventor 赵国鹏徐海清钟洪胜胡耀红袁国伟陈力格罗慧梅徐金来
Owner GUANGZHOU HONWAY TECH CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap