A kind of nickel base alloy welding wire

A nickel-based alloy and welding wire technology, applied in the field of alloys, can solve the problems of poor processing plasticity, low yield, difficult deformation, etc., and achieve the effect of improving strength and hardness, uniform composition and dense structure

Active Publication Date: 2015-11-18
JIANGSU TOLAND ALLOY
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, Cr28Ni48W5 alloy has a high content of chromium and tungsten, and low content of aluminum, titanium and other elements. Therefore, Cr28Ni48W5 alloy has poor processing plasticity and is a kind of high-temperature welding wire material that is difficult to deform. It is generally used to manufacture thicker welding wire. When the welding wire is thinner, the finished product rate is extremely low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] For the nickel-based alloy welding wire in this example, the composition and mass percentage of the alloy are C: 0.41%, Mn: 1.02%, Si: 0.57%, P: 0.02%, S: 0.02%, Cr: 28.32%, Ni: 49.58 %, Co: 0.08%, Mo: 0.09%, Ti: 0.08%, Al: 0.07%, W: 4.81%, and the rest is iron.

[0031] The specific steps of the preparation method of the nickel-base alloy welding wire of the present embodiment are as follows:

[0032] A. Alloy smelting, batching is carried out according to the composition and mass percentage of the alloy, and the raw materials after surface derusting and oil stains are put into the vacuum induction furnace. After the charging is completed, the vacuum is started until the pressure reaches 0.67Pa, and the electric heating of the furnace material is started. , the temperature is controlled at about 1600°C, and the vacuum degree is controlled at 0.1-1Pa. After the furnace material is melted, immediately add an appropriate amount of massive graphite or other high-carbon ma...

Embodiment 2

[0040] In the nickel-based alloy welding wire of this embodiment, the composition and mass percentage of the alloy are C: 0.45%, Mn: 1.18%, Si: 0.15%, P: 0.02%, S: 0.02%, Cr: 29.51%, Ni: 50.32 %, Co: 0.08%, Mo: 0.09%, Ti: 0.08%, Al: 0.07%, W: 4.15%, and the rest is iron.

[0041] The preparation method of the nickel-based alloy welding wire of this embodiment is the same as that of Embodiment 1.

Embodiment 3

[0043] In the nickel-based alloy welding wire of this embodiment, the composition and mass percentage of the alloy are C: 0.42%, Mn: 1.12%, Si: 0.50%, P: 0.02%, S: 0.02%, Cr: 29.22%, Ni: 50.06 %, Co: 0.08%, Mo: 0.09%, Ti: 0.08%, Al: 0.07%, W: 4.53%, and the rest is iron.

[0044] The preparation method of the nickel-based alloy welding wire of this embodiment is the same as that of Embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a nickel-based alloy welding wire, which comprises the following components in percentage by mass: 0.4% to 0.45% of C, 1.0% to 1.5% of Mn, 0.15% to 1.2% of Si, less than or equal to 0.025% of P, less than or equal to 0.02% of S, 28% to 30% of Cr, 49% to 51% of Ni, less than or equal to 0.1% of Co, less than or equal to 0.1% of Mo, less than or equal to 0.1% of Ti, less than or equal to 0.1% of Al, 4.0% to 5.0% of W, and the balance of iron. The preparation method comprises the following steps of alloy melting - electro slag remelting - hot forging cogging - hot-rolled annealing- pickling and grinding - cold drawing - hydrogen annealing, and the electro slag remelting uses CaF2, Al2O3 and CaO slag systems. A thinner welding wire which meets the performance requirement can be prepared by the method for preparing the nickel-based alloy welding wire, with a high yield.

Description

technical field [0001] The invention relates to a nickel-based alloy welding wire, which belongs to the technical field of alloys. Background technique [0002] Cr28Ni48W5 nickel-based alloy has high temperature resistance and can be made into welding wire for repairing high temperature resistant metal materials. However, Cr28Ni48W5 alloy has a high content of chromium and tungsten, and low content of aluminum, titanium and other elements. Therefore, Cr28Ni48W5 alloy has poor processing plasticity and is a kind of high-temperature welding wire material that is difficult to deform. It is generally used to manufacture thicker welding wire. When the welding wire is thinner, the yield is extremely low. [0003] Chinese patent document CN101249591 discloses a nickel-based welding wire and its preparation process. The welding wire has a very high nickel content and does not contain tungsten. It is made by vacuum smelting-electroslag remelting-forging-hot rolling-drawing-annealing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/30B23K35/40
CPCB23K35/304B23K35/40
Inventor 苏成礼王林涛吴伟束文武
Owner JIANGSU TOLAND ALLOY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com