Preparation method of earthen ink-stone tea tray

A technology for drinking inkstone and tea tray, which is applied in the field of preparation of clay drinking inkstone and tea tray, can solve the problem of not firing large-scale clear mud inkstone, etc., and achieve the effects of good market response, reduced internal stress, and beautiful composition.

Inactive Publication Date: 2014-09-03
闫吉平
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional Chengni inkstone production process can only produce smaller Chengni inkstones, currently there is no technique for firing large Chengni inkstones

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] A preparation method of a clay drinking inkstone tea tray, comprising the following steps

[0026] (1) Prepare mud balls

[0027] Select cement 10-15kg, kaolin, 40-50kg, clay 40-50kg and stir in 500-600kg water to form mud, filter the mud, and knead and beat the filtered mud to make mud balls;

[0028] (2) Put the mud ball into the tea tray mold of drinking inkstone to make a blank. The length of the blank is greater than 100cm. Fruits and vegetables can be placed in the mold, and the blank is placed in the mold in a cool place to evaporate and dry;

[0029] (3) Rough engraving, rough engraving on the blank;

[0030] (4) firing, including the following steps,

[0031] A. Entering the kiln: place the roughly carved parts in the kiln, and evaporate at a low temperature of 30°C-40°C for no less than 36 hours.

[0032] B. Heating: From 40°C to 900°C at a constant speed, the heating time is not less than 24h,

[0033] C. Firing: the control temperature shall not be highe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of an earthen ink-stone tea tray. The method comprises the following steps: stirring glue mud, kaolin and clay in water according to a certain mass part ratio to form slurry, filtering the slurry, and kneading and flapping the filtered slurry to prepare mud pie; putting the mud pie into an ink-stone tea tray mould to prepare a blank, and evaporating and airing the blank in the mould in the shade; and coarsely engraving, sintering by adopting a special process, and discharging from a kiln to obtain the earthen ink-stone tea tray. The preparation method has the beneficial effects that the prepared earthen ink-stone tea tray is not deformed, the cracking rate is low after the sintering process, the yield is more than 95%, and the purpose of making mud ink-stone into the tea tray is achieved; and the prepared earthen ink-stone tea tray has various advantages of clear mud ink-stone materials.

Description

technical field [0001] The invention belongs to the technical field of tea tray preparation, and in particular relates to a preparation method of a mud inkstone tea tray. Background technique [0002] Tea trays, also known as tea boats, are shallow vessels for holding teapots, teacups, tea ceremony sets, tea pets and even tea food. They are mainly made of metal, wood, bamboo, stone, tempered glass and other materials. So far, there are no public reports of clay drinking inkstone tea trays. [0003] Chengni inkstone, fired from sediment, has many advantages that other materials do not have. First of all, because the color of the Chengni inkstone is determined by many factors such as the temperature and time of firing, the variety is more abundant, and it can adapt to people's different hobbies and needs. Secondly, Chengni inkstones are fired after they have been shaped, so they have strong plasticity, so there are more styles, finer carvings, and more beautiful shapes and co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/22C04B33/32
Inventor 闫吉平
Owner 闫吉平
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products