Plastic surface treatment technique

A plastic surface treatment and plastic technology, applied in metal material coating process, fusion spray plating, coating and other directions, can solve the problems of reduced plastic quality, unsightly plastic, poor heat resistance, etc., to improve high temperature oxidation resistance, guarantee Glossy, low-cost effect

Inactive Publication Date: 2014-09-03
CHUZHOU HONGYUAN SPRAYING
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the heat resistance of most plastics is poor, and it is easy to release the toxic substance bisphenol A when heated, and at high temperatures, oil stains are easy to adhere to the surface of the plastic, which not only reduces

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A plastic surface treatment process, the specific steps are:

[0035] (1) Plastic degreasing: Use high-temperature lye to spray on the plastic surface at high pressure, and use a cleaning roller to brush the plastic surface to degrease.

[0036] (2) Plastic swelling: Put the degreased plastic into the swelling solution and soak for 5 minutes; the components in the swelling solution and the volume percentages of each component are: bentonite solution: 60%, ethyl acetate: 10%, Ethyl acetoacetate: 5%, the rest is distilled water.

[0037] (3) Plastic surface roughening: prepare microetching solution, each component in the microetching solution and the volume percentage of each component are: ammonium sulfate: 20%, barium sulfate: 25%, ammonium permanganate: 20%, oxalic acid: 20%, glycerin: 15%; soak the plastic in the microetching solution, raise the temperature of the microetching solution to 45°C at a rate of 10°C / min, and take it out after keeping it for 15 minutes; pr...

Embodiment 2

[0044] A plastic surface treatment process, the specific steps are:

[0045] (1) Plastic degreasing: Use high-temperature lye to spray on the plastic surface at high pressure, and use a cleaning roller to brush the plastic surface to degrease.

[0046] (2) Plastic swelling: Put the degreased plastic into the swelling solution and soak for 7 minutes; the components in the swelling solution and the volume percentages of each component are: bentonite solution: 63%, ethyl acetate: 12%, Ethyl acetoacetate: 8%, the rest is distilled water.

[0047] (3) Plastic surface roughening: prepare microetching solution, each component in the microetching solution and the volume percentage of each component are: ammonium sulfate: 22%, barium sulfate: 22%, ammonium permanganate: 22%, oxalic acid: 20%, glycerin: 14%; soak the plastic in the microetching solution, raise the temperature of the microetching solution to 50°C at a rate of 7°C / min, and take it out after keeping it for 17 minutes; pre...

Embodiment 3

[0054] A plastic surface treatment process, the specific steps are:

[0055] (1) Plastic degreasing: Use high-temperature lye to spray on the plastic surface at high pressure, and use a cleaning roller to brush the plastic surface to degrease.

[0056] (2) Plastic swelling: Put the degreased plastic into the swelling solution and soak for 10 minutes; the components in the swelling solution and the volume percentages of each component are: bentonite solution: 65%, ethyl acetate: 15%, Ethyl acetoacetate: 10%, the rest is distilled water.

[0057] (3) Plastic surface roughening: prepare microetching solution, each component in the microetching solution and the volume percentage of each component are: ammonium sulfate: 25%, barium sulfate: 22%, ammonium permanganate: 20%, oxalic acid: 20%, glycerin: 13%; soak the plastic in the micro-etching solution, raise the temperature of the micro-etching solution to 60 °C at a speed of 10 °C / min, and take it out after keeping it for 20 minu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a plastic surface treatment technique which comprises the following steps: plastic degreasing, plastic swelling, plastic surface coarsening, primary grit blasting, spraying treatment, hole sealing treatment, secondary grit blasting (carrying out grit blasting on the plastic surface by using a high-pressure spray gun and a sand material), and water washing and drying. The treatment technique is simple, shortens the treatment time, and enhances the high-temperature oxidation resistance and corrosion resistance of the plastic; and the plastic has higher surface smoothness and is beautiful.

Description

technical field [0001] The invention belongs to the technical field of plastic surface treatment, and in particular relates to a treatment process capable of enhancing the high-temperature oxidation resistance and corrosion resistance of plastics. Background technique [0002] Plastics are polymer compounds that are polymerized from monomers as raw materials through addition polymerization or polycondensation reactions. Due to its light weight, good insulation, and low thermal conductivity, plastics are usually used to make daily necessities such as water cups, kettles, and milk bottles. [0003] However, the heat resistance of most plastics is poor, and it is easy to release the toxic substance bisphenol A when heated, and at high temperatures, oil stains are easy to adhere to the surface of the plastic, which not only reduces the quality of the plastic, but also makes the plastic Not beautiful. For this kind of plastic, if it is thermoplastic, it can also be recycled...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08J7/00C23C4/12C23C4/06C23C4/129
Inventor 王新志
Owner CHUZHOU HONGYUAN SPRAYING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap