Special polymer and high-strength composite leakage board for pasture

A composite material and high-strength technology, which is applied in the field of high-molecular high-strength composite material ranch slatted panels, can solve problems such as poor slatted effect, high labor intensity, and high thermal conductivity, and achieve poor slatted effect and low labor intensity. The effect of large and large thermal conductivity

Inactive Publication Date: 2014-10-08
长兴绿地建材有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is that existing pasture slats have high weight, high labor intensity during installation, high cost, high thermal conductivity, and poor slatted effect, so as to provide special slats for ranch made of high-molecular high-strength composite materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0007] High-molecular high-strength composite material special slatted board for pasture, the mass percentage of the components is: 16% unsaturated resin, 8.5% styrene, 8.5% polystyrene, 47% calcium carbonate, 11% glass fiber, curing agent 3%, release agent 2%, dye agent 2%, calcium hydroxide 2%, can also be the mass percentage of other components, stable structure, high mechanical strength, good toughness, low cost, smooth product, high precision, durable Corrosion, leakage effect is good.

[0008] The curing agent is tert-butyl peroxyformate, the release agent is calcium-zinc composite, and the dye agent is a vegetable dye. The tert-butyl peroxyformate has good stability, strong fixing effect, and the demoulding effect of calcium-zinc composite Well, plant dyes are effective, safe and reliable.

[0009] It is made by mixing unsaturated resin, styrene, polystyrene, calcium carbonate, glass fiber, curing agent, mold release agent, dyeing agent and calcium hydroxide in a certa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a special polymer and high-strength composite leakage board for a pasture. The special polymer and high-strength composite leakage board comprises the following components in percentage by mass: 16% of unsaturated polyester resin, 8.5% of styrene, 8.5% of polystyrene, 47% of calcium carbonate, 11% of glass fiber, 3% of curing agent, 2% of mold release, 2% of dye and 2% of calcium hydroxide. The special polymer and high-strength composite leakage board is prepared by mixing the unsaturated polyester resin, styrene, polystyrene, calcium carbonate, glass fiber, curing agent, mold release, dye and calcium hydroxide according to a certain proportion; and in addition, the special polymer and high-strength composite leakage board has the advantages of light weight, low labor intensity during installation, high mechanical strength, good toughness, low cost, smoothness, high precision, corrosion resistance and good leakage effect.

Description

technical field [0001] The invention relates to a special-purpose slatted board for pastures made of high-molecular high-strength composite materials. Background technique [0002] Most of the existing ranch slats are made of cast iron, which makes the slats high in weight, labor-intensive during installation, high in cost, and high in thermal conductivity. Due to the rough surface of cast iron, it will corrode when it encounters strong alkali, and the slatted effect is poor. , Bacteria and germs are easy to adhere to the surface, which has a certain impact on the prevention of pig diseases. Contents of the invention [0003] Technical Problems to be Solved by the Invention The existing ranch slats have high weight, high labor intensity during installation, high cost, high thermal conductivity and poor slatted effect, so a special slatted board for ranch made of high-molecular high-strength composite materials is provided. [0004] In order to solve the above-mentioned te...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L51/00C08L51/06C08F291/00C08F212/08C08K13/04C08K7/14C08K3/26C08K3/22C08K5/14
Inventor 李梅芳李正芳李晖陈永如徐志云吴建峰
Owner 长兴绿地建材有限公司