A kind of temperature-regulating spun silk blended fabric and its preparation method

A technology of blended fabrics and spun silk, which is applied in textiles, fabrics, textiles and papermaking, etc., can solve the problems of outlast fiber and spun silk blending research, and achieve the effects of easy implementation, good air and moisture permeability, and easy availability of raw materials

Inactive Publication Date: 2016-06-29
SUZHOU UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no relevant report on the research on the blending of Outlast fiber and spun silk

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Spun silk / Outlast blended fabric fabric, its preparation steps are as follows:

[0038] 1. The spinning steps of spun silk / Outlast blended yarn are as follows:

[0039] 1) Prepare spun silk fiber fine cotton sheet

[0040] The preparation process of spun silk fiber fine cotton sheet is as follows: spun silk fiber dry cotton → cotton blending → wetting → cotton opening → roller combing → sorting → combing → silk fiber fine cotton sheet;

[0041] Among them, the requirements for blending cotton: the linear density of spun silk fiber in refined dry cotton is above 1.11dtex, the length is 80mm, the residual oil rate is less than 0.5%, the residual glue rate is 2%, the cleanliness is less than 30 degrees, and the moisture regain is 8%;

[0042] Among them, wetting requirements: use dipping wetting method, 0.05% antistatic agent 824-N, 0.64% smoothing agent 289, 0.1% dispersant WA, 0.2% electrolyte sodium citrate.

[0043] Preparation of Outlast Short Fiber Refined Sheets ...

Embodiment 2

[0064] Spun silk / Outlast blended fabric fabric, its preparation steps are as follows:

[0065] 1. The spinning steps of spun silk / Outlast blended yarn are as follows:

[0066] 1) Prepare spun silk fiber fine cotton sheet

[0067] The preparation process of spun silk fiber fine cotton sheet is as follows: spun silk fiber dry cotton → cotton blending → wetting → cotton opening → roller combing → sorting → combing → silk fiber fine cotton sheet;

[0068] Among them, the requirements for blending cotton: the linear density of spun silk fiber in refined dry cotton is above 1.11dtex, the length is 80mm, the residual oil rate is less than 0.5%, the residual glue rate is 2%, the cleanliness is less than 30 degrees, and the moisture regain is 8%;

[0069] Among them, wetting requirements: use dipping wetting method, 0.05% antistatic agent 824-N, 0.64% smoothing agent 289, 0.1% dispersant WA, 0.2% electrolyte sodium citrate.

[0070] Preparation of Outlast Short Fiber Refined Sheets ...

Embodiment 3

[0091] Spun silk / Outlast blended fabric fabric, its preparation steps are as follows:

[0092] 1. The spinning steps of spun silk / Outlast blended yarn are as follows:

[0093] 1) preparing spun silk fiber essence sheet;

[0094]The preparation process of spun silk fiber fine cotton sheet is as follows: spun silk fiber dry cotton → cotton blending → wetting → cotton opening → roller combing → sorting → combing → silk fiber fine cotton sheet;

[0095] Among them, the requirements for blending cotton: the linear density of spun silk fiber in refined dry cotton is above 1.11dtex, the length is 80mm, the residual oil rate is less than 0.5%, the residual glue rate is 2%, the cleanliness is less than 30 degrees, and the moisture regain is 8%;

[0096] Among them, wetting requirements: use dipping wetting method, 0.05% antistatic agent 824-N, 0.64% smoothing agent 289, 0.1% dispersant WA, 0.2% electrolyte sodium citrate.

[0097] Prepare Outlast short-fiber essence sheet;

[0098] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
decontamination rateaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a spun silk / Outlast blended fabric with temperature regulating function and a preparation method thereof. Outlast short fibers are blended with spun silk fibers at a blending dry weight ratio of 20% to 60% to make linear densities of 83.3dtex and 166.7 dtex spun silk / Outlast blended yarn single yarn, and then two single yarns are combined and twisted to obtain 166.7dtex and 333.4dtex spun silk / Outlast blended yarn strands; the spun silk / Outlast blended yarn strands are used Threads are used as warp and weft yarns. The warp density is 300-600 / 10cm, the weft density is 120-300 / 10cm, and the fabric weave is 2-4 pieces to make fabric gray fabric, which is then scoured, washed and washed in four steps. Drying and setting to make finished fabrics. According to the method provided by the invention, the heating rate of the fabric at 20°C to 40°C and the cooling rate at 20°C to 10°C are obviously lower than those of pure spun silk fabrics, and it has a good temperature adjustment function, making it difficult for the human body to feel heat in a high temperature environment. It is not easy to feel cold in low temperature environment. At the same time, this kind of fabric also has the advantages of good hygroscopicity, good air permeability and moisture permeability, softness and comfort, and is a kind of functional silk fabric.

Description

technical field [0001] The invention relates to a temperature-regulating fabric and a preparation method thereof, in particular to a temperature-regulating fabric blended with spun silk and Outlast fiber and a preparation method thereof. Background technique [0002] Outlast heat storage and temperature regulating fiber is a new type of "smart" fiber, which was successfully developed by Outlast in 1988. It was first used for commercial use in 1994, used for outdoor clothing in 1997, and is now widely used in fashion and bedding. The temperature adjustment effect of Outlast fiber is achieved by using microcapsule technology to implant heat-sensitive phase change material (PCM) into the fiber. This material can absorb, store and release a large amount of heat in the form of "latent heat". It can be based on The change of the external environment temperature is transformed into solid and liquid, so as to achieve the effect of buffering the temperature change. [0003] Initiall...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D03D15/00D02G3/04D06M11/50D06M11/79D06M11/76D06L1/16D06M101/06D06M101/10D03D15/225D03D15/233D03D15/283D03D15/47D03D15/50
Inventor 潘志娟眭建华朱思敏汪亮汪明树
Owner SUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com