Anti-corrosion PE water supply pipe and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A water supply pipe, corrosion-resistant technology, applied in the direction of pipes, rigid pipes, mechanical equipment, etc., can solve the problems of poor corrosion resistance, reduce the service life of PE pipes, limit the scope of application, etc., to achieve excellent chemical corrosion resistance, adaptability strong effect
Inactive Publication Date: 2014-10-15
ANHUI DINGYUAN ZHENYUN PLASTIC
View PDF5 Cites 5 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
In recent years, with the rapid development of science and technology and the continuous improvement of people's living standards, the performance requirements of PE water supply pipes are getting higher and higher. At present, the corrosion resistance of PE water supply pipes on the market is poor. Under corrosive media such as raw rot and electrochemical corrosion, it is easy to occur, which greatly reduces the service life of PE pipes and limits its application range.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0013] A corrosion-resistant PE water supply pipe, made of the following raw materials in weight (kg): ultra-high molecular weight polyethylene 58, polyphenylene sulfide 32, liquid crystal polymer 18, terpene resin 12, precipitated barium sulfate 18, magnesite 12. Nano-calcium titanate 10, dibasic lead phthalate 2.5, zinc ricinoleate 2, barium ricinoleate 1.5, trimethylolpropane 2.5, thiodiethylene glycol bis(β-aminobutene Acid) ester 1.5, stearyl benzoyl methane 2, behenic acid amide 3, glycerol triacetyl ricinoleate 4, solid paraffin 6, filler masterbatch 26, liquid nitrile rubber 12, 1,4- Cyclohexanedimethanol dibenzoate 1.5, N,N'-bis[β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionyl]hydrazine 1;
[0014] The preparation method of the filler masterbatch is as follows: a. Weigh the following raw materials by weight (kg): serpentine 40, diatomite 30, pyrophyllite 16, olivine 14, behenyloxypolydimethylsiloxane 2. Distearyloxy isopropyl aluminate 2.5, di-n-octyl phthalate 12,...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
yield strength
aaaaa
aaaaa
compressive strength
aaaaa
aaaaa
Vicat softening point
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses an anti-corrosion PE water supply pipe and a preparation method thereof. The pipe is prepared from the following raw materials by weight part: 46-62 of ultra-high molecular weight polyethylene, 22-36 of polyphenylene sulfide, 12-24 of a liquid crystal polymer, 10-15 of terpene resin, 16-22 of precipitated barium sulphate, 10-15 of magnesia, 8-14 of nano-calcium titanate, 2-3 of dibasic lead phthalate, 1.5-2.5 of zinc ricinate, 1-2 of barium ricinate, 2-3 of trimethylolpropane, 1-2 of thiodiethylene glycol bis(beta-aminocrotonic acid)ester, 1.5-2.5 of stearoylbenzoylmethane, 2-4 of docosanamide, 3-5 of glycerol triacetylricinoleate, 4-8 of solid paraffin, 22-28 of filling masterbatch, 10-15 of liquid nitrile rubber, 1-2 of 1, 4-cyclohexanedimethanol dibenzoate, and 1-2 of N, N'-bis[beta-(3, 5-di-tert-butyl-4-hydroxyphenyl)propionyl]hydrazine. The PE pipe provided by the invention has excellent resistance to chemical corrosion, can resist erosion of a variety of chemical mediums, especially acid, alkali, salt and oil, and is free of electrochemical corrosion, has strong adaptability to the environment, does not rot or corrode after long-term use, and is durable in use.
Description
technical field [0001] The invention relates to a PE pipe material and a preparation method thereof, in particular to a corrosion-resistant PE water supply pipe material and a preparation method thereof. Background technique [0002] PE pipes are widely used in the field of water supply manufacturing because of their high strength, high temperature resistance, corrosion resistance, non-toxicity, and wear resistance. They are replacement products for traditional steel pipes and PVC drinking water pipes. In recent years, with the rapid development of science and technology and the continuous improvement of people's living standards, the performance requirements of PE water supply pipes are getting higher and higher. At present, the corrosion resistance of PE water supply pipes on the market is poor. Under such corrosive media, raw rot and electrochemical corrosion are prone to occur, which greatly reduces the service life of PE pipes and limits its application range. Therefor...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.