Anion easy-cleaning functional ceramic additive and preparation method thereof, ceramic prepared by using additive and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of functional ceramics and additives, applied in the field of ceramics, can solve problems such as groundwater pollution and harm to health, and achieve the effect of easy cleaning and strong affinity
Active Publication Date: 2014-11-05
ZIBO BAIKANG ECONOMIC & TRADE
View PDF4 Cites 34 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
At the same time, the use of various detergents will also cause groundwater pollution and endanger human health. Relevant data show that the annual consumption of detergents in my country is between 300,000 and 400,000 tons. Theoretically
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0044] The negative ion and easy-to-clean functional ceramic additive of the present invention is made of the following raw materials in mass percentage:
[0045] Sogo stone 16% of 5-20 microns, 19% of tourmaline of 5-15 microns, 12% of seastone of 5-20 microns, 8% of nano-titanium dioxide, 6% of nano-zinc oxide, 6% of lead-free frit, nitric acid 8% cerium, 9% ultrafine alumina, 11% ultrafine quartz powder and 5% sodium carbonate.
[0046] The preparation method is first to mix and ball-mill lead-free frit, rare earth materials, ultrafine alumina, ultrafine quartz powder and sodium carbonate for 9 hours, and then add 5-20 micron sogo stone, 5-15 micron tourmaline, 5- The 20-micron haveronite, nano-titanium dioxide and nano-zinc oxide are ball-milled for 9 hours to obtain negative ion and easy-to-clean functional ceramic additives with a particle size of 1-10 microns.
Embodiment 2
[0048] The negative ion and easy-to-clean functional ceramic additive of the present invention is made of the following raw materials in mass percentage:
[0049] Sogo stone 10% of 5-20 microns, 25% of tourmaline of 5-15 microns, 10% of seastone of 5-20 microns, 8% of nano-titanium dioxide, 6% of nano-zinc oxide, 5% of lead-free frit, oxide Neodymium 10%, superfine alumina 8%, superfine quartz powder 12% and sodium carbonate 6%.
[0050] The preparation method is the same as in Example 1.
Embodiment 3
[0052] The negative ion and easy-to-clean functional ceramic additive of the present invention is made of the following raw materials in mass percentage:
[0053] Sogo stone 12% of 5-20 microns, 23% of tourmaline of 5-15 microns, 5% of seastone of 5-20 microns, 10% of nano-titanium dioxide, 7% of nano-zinc oxide, 5% of lead-free frit, nitric acid 4% cerium, 5% neodymium oxide, 9% ultra-fine alumina, 13% ultra-fine quartz powder and 7% sodium carbonate.
[0054] The preparation method is the same as in Example 1.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention belongs to the technical field of ceramics, and particularly relates to an anion easy-cleaning functional ceramic additive and a preparation method thereof, a ceramic prepared by using the additive and a preparation method thereof. The additive is prepared from the following raw materials in percentage by mass: 10-16% of Chongguang stones with a particle size of 5-20 microns, 16-25% of tourmaline with a particle size of 5-15 microns, 5-15% of copper pectolite with a particle size of 5-20 microns, 8-12% of nano titanium dioxide, 6-8% of nano zinc oxide, 5-10% of lead-free frits, 7-20% of rare earth materials, 8-10% of superfine alumina, 8-15% of superfine quartz powder and 5-10% of sodium carbonate. The preparation method of the additive comprises the following steps of carrying out mixed ball-milling on the lead-free frits, the rare earth materials, the superfine alumina, the superfine quartz powder and the sodium carbonate firstly; and then, adding the Chongguang stones, the tourmaline, the copper pectolite, the nano titanium dioxide and the nano zinc oxide into the obtained product, and ball-milling the obtained mixture, so that the additive with a particle size of 1-10 microns is obtained. The additive disclosed by the invention has a self-polarizing performance, and has strong adsorption and decomposition functions, so that negative ions are produced; and after the additive is added into a ceramic, the ceramic is extremely easy to clean and not stained, and has no hidden dirt, therefore, the ceramic has a strong affinity to water.
Description
technical field [0001] The invention belongs to the technical field of ceramics, and in particular relates to a negative ion easy-to-clean functional ceramic additive, a preparation method thereof, ceramics prepared therefrom, and a preparation method of the ceramics. Background technique [0002] At present, the pollution of indoor environment, products consumed by human beings, and water is gradually increasing. The main pollutants are formaldehyde, lead, cadmium, mercury, cyanide and other harmful chemicals. People live in such a polluted environment for a long time and contact with contaminated food, which is very harmful to the body and often induces various diseases. At the same time, the use of various detergents will also cause groundwater pollution and endanger human health. Relevant data show that the annual consumption of detergents in my country is between 300,000 and 400,000 tons. Theoretically, it is non-toxic, but some harmful substance monomers will be absorb...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more