Hydrothermal synthesis method of carbon quantum dots from cotton

A technology of carbon quantum dots and raw material water, applied in the field of hydrothermal synthesis of carbon quantum dots, can solve the problems of many preparation steps and unsuitable for large-scale production, and achieve the effect of simple preparation process and wide sources

Active Publication Date: 2014-12-10
SHANGHAI JIAO TONG UNIV
View PDF3 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This invention uses eggs as the raw material for preparing carbon quantum dots, which is a convenient source, but the raw mater

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrothermal synthesis method of carbon quantum dots from cotton
  • Hydrothermal synthesis method of carbon quantum dots from cotton
  • Hydrothermal synthesis method of carbon quantum dots from cotton

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0022] Example 1

[0023] Step 1. Take 0.3g cotton and 400mg p-toluenesulfonic acid and add them to 25ml water;

[0024] Step 2: Hydrothermal reaction at 200°C for 5 hours;

[0025] Step 3, filter with 200μm cellulose filter membrane, and then dialyzed with 1000Da dialysis bag to obtain pure carbon quantum dots.

Example Embodiment

[0026] Example 2

[0027] Step 1. Take 0.3g cotton and 150mg p-toluenesulfonic acid and add them to 25ml water;

[0028] Step 2: Hydrothermal reaction at 200°C for 5h;

[0029] Step 3, filter with a 200μm cellulose filter membrane, and then dialyzed with a 1000Da dialysis bag to obtain pure carbon quantum dots.

Example Embodiment

[0030] Example 3

[0031] Step 1. Take 0.3g cotton and 60mg p-toluenesulfonic acid and add them to 25ml water;

[0032] Step 2: Hydrothermal reaction at 200°C for 5 hours;

[0033] Step 3, filter with a 200μm cellulose filter membrane, and then dialyzed with a 1000Da dialysis bag to obtain pure carbon quantum dots.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a hydrothermal synthesis method of carbon quantum dots from cotton. The method comprises the following steps: weighing certain amounts of cotton and acidic catalyst, adding into a right amount of water, carrying out hydrothermal reaction for some time, filtering the reaction product, and dialyzing to obtain the carbon quantum dots. The method has the advantages of wide carbon sources and simple preparation process, can implement mass production, and is a green method for synthesizing carbon quantum dots.

Description

technical field [0001] The invention relates to the technical field of nanomaterial preparation, in particular to a method for hydrothermally synthesizing carbon quantum dots based on cotton as a raw material. Background technique [0002] As a novel carbon family nanomaterial, carbon quantum dots have excellent water solubility, biocompatibility, photobleaching resistance, and tunable fluorescence properties, and are widely used in bioimaging, photocatalysis, solar cells and other fields. [0003] The hydrothermal synthesis method is widely used in the synthesis of carbon quantum dots due to its high reaction yield and uniform particle size. For the synthesis process of carbon quantum dots, most methods in the current research require strict experimental conditions or special energy sources, resulting in high costs and low yields of carbon quantum dots obtained. [0004] After searching, the Chinese invention patent with the publication number CN103832993A discloses a meth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01B31/02B82Y30/00
Inventor 杨志徐明瀚王羽希王英张亚非
Owner SHANGHAI JIAO TONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap