A kind of air tightness enhancer and its preparation method and application

An air-tightness enhancer and pan technology, which is applied in building components, building insulation materials, construction, etc., can solve the problems of unsatisfactory properties of rubber materials, and achieve the effects of shortening vulcanization time, good processing and dispersion performance, and low cost

Active Publication Date: 2016-08-24
SHANDONG YANGGU HUATAI CHEM
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the process of modern rubber processing, airtightness enhancers are mainly used for innerliner rubber to improve the airtightness of rubber products such as tires; currently, most tire companies use brominated butyl rubber (BIIR) and chlorobutyl Rubber (CIIR) produces innerliner rubber. In order to reduce costs, methods such as increasing the amount of styrene-butadiene rubber (SBR) in the rubber compound, adding butyl rubber (IIR) reclaimed rubber and calcium carbonate to reduce the rubber content, etc., but the rubber compound Performance is not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of air tightness enhancer and its preparation method and application
  • A kind of air tightness enhancer and its preparation method and application
  • A kind of air tightness enhancer and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] An airtightness enhancer, comprising the following components by weight:

[0052] 60 parts of component A, 20 parts of component B, 15 parts of component C, 5 parts of component D;

[0053] Described component A is petroleum asphalt;

[0054] Described component B is calcium stearate;

[0055] Described component C is pentaerythritol stearate;

[0056] The component D is fatty alcohol polyoxyethylene ether.

[0057] The preparation method is as follows:

[0058] Melt component A, add component C and component D to activate the temperature, control the temperature between 110-130°C, add component B after 30 minutes, mix evenly, cool down and make tablets or melt granulate to obtain air tightness enhancer.

Embodiment 2

[0060] An airtightness enhancer, comprising the following components by weight:

[0061] 50 parts of component A, 30 parts of component B, 15 parts of component C, 5 parts of component D;

[0062] Described component A is petroleum asphalt;

[0063] Described component B is light calcium carbonate;

[0064] Described component C is glyceryl monostearate;

[0065] The component D is Span 80.

[0066] The preparation method is the same as in Example 1.

Embodiment 3

[0068] An airtightness enhancer, comprising the following components by weight:

[0069] 70 parts of component A, 10 parts of component B, 15 parts of component C, 5 parts of component D;

[0070] Described component A is petroleum asphalt;

[0071] The component B is fly ash;

[0072] Described component C is hydrogenated oil;

[0073] The component D is Tween 80.

[0074] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an airtightness enhancer and its preparation method and application. The airtightness enhancer comprises the following ingredients in parts by weight: 40-80 parts of component A, 10-30 parts of component B, and 10-20 parts of component C , component D5‑10 parts; component A is petroleum pitch; component B is calcium stearate, fly ash, talcum powder, light calcium carbonate, vermiculite, kaolin, clay, mica powder, montmorillonite Component C is a mixture of one or more of pentaerythritol stearate, glyceryl monostearate, fatty acid alkanolamide, hydrogenated oil; component D is fatty alcohol poly One or two or more of oxyethylene ether, Span, and Tween are mixed. The airtightness enhancer of the invention can promote the mixing between rubbers, improve the uniformity of the mixed rubber, and increase the airtightness of the airtight layer.

Description

technical field [0001] The invention relates to an air tightness enhancer and its preparation method and application, belonging to the technical field of fine chemicals. Background technique [0002] In the process of modern rubber processing, airtightness enhancers are mainly used for innerliner rubber to improve the airtightness of rubber products such as tires; currently, most tire companies use brominated butyl rubber (BIIR) and chlorobutyl Rubber (CIIR) produces innerliner rubber. In order to reduce costs, methods such as increasing the amount of styrene-butadiene rubber (SBR) in the rubber compound, adding butyl rubber (IIR) reclaimed rubber and calcium carbonate to reduce the rubber content, etc., but the rubber compound The performance is not ideal. Contents of the invention [0003] Aiming at the deficiencies in the prior art, the invention provides an airtightness enhancer and its preparation method and application. [0004] Technical scheme of the present inve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L95/00C08L7/00C08L23/28C08L71/02C08K5/098C08K5/103C08K3/26C08K3/34C08K3/00C08K13/02C08K3/04C08K3/22C08K5/09C08K3/06
Inventor 郭庆飞李剑波张琳
Owner SHANDONG YANGGU HUATAI CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap