A technology of power steering tube and inner rubber layer, applied in the field of rubber parts for automobiles, can solve problems such as poor heat resistance, and achieve the effect of improving heat resistance

Inactive Publication Date: 2015-01-21
南京中配橡塑制品有限公司
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem solved by the present invention is to provide a method for preparing the rubber used for the inner rubber layer of the automobile power steering pipe, which can solve the problem of poor heat resistance of the existing rubber used for the inner rubber layer of the automobile power steering pipe

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The rubber used for the inner rubber layer of the automobile power steering tube adopts the following raw materials: 10.0kg of chlorosulfonated polyethylene; 1.5kg of quick-pressed carbon black; 2.0kg of thermal carbon black; 1.0kg of magnesium oxide; Zinc formate 0.1kg; dilauryl thiodipropionate 0.2kg; zinc stearate 0.1kg; 2,2'-dithiodibenzothiazole 0.5kg; thiocyanate 0.05kg; trimellitic acid Trioctyl ester 1.5kg; Magnesium strong powder 0.5kg; Sulfur 0.02kg;

[0015] Its preparation method comprises the following steps:

[0016] A. Chlorosulfonated polyethylene, fast extruded carbon black, thermal black, magnesium oxide, zinc diethyldithiocarbamate, dilauryl thiodipropionate, stearic acid in the above raw materials Zinc, 2, 2'-dithiodibenzothiazole, trioctyl trimellitate and magnesium powder are placed in the internal mixer for internal mixing, and after the internal mixing is completed, the glue temperature is 160°C Glue removal to prepare masterbatch;

[0017] B....

Embodiment 2

[0020] The rubber used for the inner rubber layer of the automobile power steering tube adopts the following raw materials: 10.0kg of chlorosulfonated polyethylene; 1.2kg of quick-pressed carbon black; 2.2kg of thermal carbon black; 0.8kg of magnesium oxide; Zinc formate 0.15kg; dilauryl thiodipropionate 0.15kg; zinc stearate 0.2kg; 2,2'-dithiodibenzothiazole 0.4kg; thiocyanate 0.07kg; trimellitic acid Trioctyl ester 1.3kg; Magnesium strong powder 0.7kg; Sulfur 0.01kg;

[0021] Its preparation method comprises the following steps:

[0022] A. Chlorosulfonated polyethylene, fast extruded carbon black, thermal black, magnesium oxide, zinc diethyldithiocarbamate, dilauryl thiodipropionate, stearic acid in the above raw materials Zinc, 2, 2'-dithiodibenzothiazole, trioctyl trimellitate and magnesium powder are placed in the internal mixer for internal mixing, and after the internal mixing is completed, the glue temperature is 160°C Glue removal to prepare masterbatch;

[0023] ...

Embodiment 3

[0026] The rubber used for the inner rubber layer of the automobile power steering tube adopts the following raw materials: 10.0kg of chlorosulfonated polyethylene; 1.0kg of quick-pressed carbon black; 2.5kg of thermal carbon black; 0.5kg of magnesium oxide; Zinc formate 0.2kg; dilauryl thiodipropionate 0.1kg; zinc stearate 0.3kg; 2,2'-dithiodibenzothiazole 0.3kg; thiocyanate 0.08kg; trimellitic acid Trioctyl ester 1.0kg; Magnesium strong powder 1.0kg; Sulfur 0.01kg;

[0027] Its preparation method comprises the following steps:

[0028] A. Chlorosulfonated polyethylene, fast extruded carbon black, thermal black, magnesium oxide, zinc diethyldithiocarbamate, dilauryl thiodipropionate, stearic acid in the above raw materials Zinc, 2, 2'-dithiodibenzothiazole, trioctyl trimellitate and magnesium powder are placed in the internal mixer for internal mixing, and after the internal mixing is completed, the glue temperature is 160°C Glue removal to prepare masterbatch;

[0029] B....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method for rubber for the inner rubber layer of a car power steering hose, and belongs to the technical field of car rubber pieces. The preparation method comprises the following steps: adding chlorosulfonated polyethylene, fast extruding furnace black, cracking carbon black, magnesium oxide, zinc diethyl dithiocarbamate, dilauryl thiodipropionate, zinc stearate, 2,2'-dithio-dibenzo thiazole, trioctyl trimellitate and magnesium strong powder into an internal mixer for banburying; after banburying, discharging rubber at the rubber temperature of 160 DGE C to obtain a master batch; adding the prepared master batch into the internal mixer, and adding in trithiocyanuric acid and sulphur for mixing; after mixing, sequentially squeezing out within a certain temperature range to obtain rubber for the inner rubber layer of the car power steering hose. Compared with that manufactured rubber for an inner rubber layer of a car power steering hose in the prior art, the rubber adopts the synergistic effects of the raw materials and the corresponding squeezing temperatures to effectively improve the heat resistance property of the rubber.

Description

technical field [0001] The invention relates to the technical field of rubber parts for automobiles, in particular to a method for preparing rubber for an inner rubber layer of an automobile power steering tube. Background technique [0002] The power steering tube is a product with high technical content in the automotive steering system components. With the rapid development of the automobile industry, the application of power steering tubes in automotive steering systems is becoming more and more common. At the same time, the performance requirements for automotive power steering tubes are also increasing, especially their heat resistance. Automotive power steering tubes are generally made of inner and outer layers of rubber. At present, although people continue to study and improve the heat resistance of the rubber used for the inner rubber layer of the automobile power steering tube, the effect is not obvious, and the heat resistance still needs to be improved. Conte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/34C08K13/02C08K3/04C08K3/22C08K5/39C08K5/372C08K5/098C08K5/47C08K5/12C08K3/06B29C47/92B29C48/92
CPCC08K13/02B29C48/92B29C2948/92704C08K3/04C08K3/06C08K3/22C08K5/098C08K5/12C08K5/372C08K5/39C08K5/47C08K2003/222C08K2201/014C08L2201/08C08L2203/18C08L23/34
Inventor 陈永亮
Owner 南京中配橡塑制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap