A Composite Reinforced Plastic Inspection Well
A plastic inspection well and composite reinforcement technology, applied in the field of plastic inspection well materials, can solve the problems of poor hardness and tensile strength, weak static load capacity, short service life, etc., to improve surface hardness and tensile strength, improve static Load capacity, good adaptation effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0012] Example 1, a composite reinforced plastic inspection well, the parts by weight of the raw materials for the plastic inspection well are: 30 parts of polyvinyl chloride resin, 20 parts of PP resin, 9 parts of reactive polyamide resin, acrylate type anti-impact 2 parts of modifier ACR, 2 parts of polyethylene wax, 2 parts of polytetrafluoroethylene, 2 parts of composite stabilizer, 3 parts of filler, 6 parts of carbon fiber, 2 parts of modified polycarbonate; the composite stabilizer is powder Bulk calcium zinc composite heat stabilizer, dioctyl adipate, flame retardant, foaming agent, processing modifier mixture; the filler is calcium carbonate and barium sulfate.
Embodiment 2
[0013] Example 2, a composite reinforced plastic inspection well, the parts by weight of the raw materials for the plastic inspection well are: 35 parts of polyvinyl chloride resin, 40 parts of PP resin, 11 parts of reactive polyamide resin, acrylate-based impact-resistant 3 parts of modifier ACR, 6 parts of polyethylene wax, 6 parts of polytetrafluoroethylene, 8 parts of composite stabilizer, 5 parts of filler, 8 parts of carbon fiber, 2 parts of modified polycarbonate; the composite stabilizer is powder Bulk calcium zinc composite heat stabilizer, dioctyl adipate, flame retardant, foaming agent, processing modifier mixture; the filler is calcium carbonate and barium sulfate.
Embodiment 3
[0014] Example 3, a composite reinforced plastic inspection well, the parts by weight of the raw materials for the plastic inspection well are: 33 parts of polyvinyl chloride resin, 30 parts of PP resin, 10 parts of reactive polyamide resin, acrylate type anti-impact 3 parts of modifier ACR, 5 parts of polyethylene wax, 4 parts of polytetrafluoroethylene, 5 parts of composite stabilizer, 4 parts of filler, 7 parts of carbon fiber, 2 parts of modified polycarbonate; the composite stabilizer is powder Bulk calcium zinc composite heat stabilizer, dioctyl adipate, flame retardant, foaming agent, processing modifier mixture; the filler is calcium carbonate and barium sulfate.
[0015] The preparation method comprises the following steps:
[0016] (1) take each raw material by the weight part that forms raw material in the embodiment;
[0017] (2) Add some raw materials into the extruder and stir at 185°C for 8 minutes, then add the rest of the raw materials, heat at 180°C for 20 m...