Single component low-temperature polyurethane foaming adhesive and preparation method thereof

A polyurethane foam adhesive, one-component technology, applied in the direction of polyurea/polyurethane adhesive, adhesive, adhesive type, etc., can solve the problems of short surface drying time, high curing temperature, long hard drying time, etc., to achieve The effect of long surface dry time, low curing temperature and short hard drying time

Active Publication Date: 2015-01-28
湖北和乐门业有限公司
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] One of the objectives of the present invention is to address the above-mentioned deficiencies and provide a single-component low-temperature polyurethane foam, in order to solve the problems of the existing foams that the surface drying time is too short, the curing temperature is too high, and the hard drying time is too long

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The one-component low-temperature polyurethane foam of the present invention comprises 150 to 200 parts of polyhexamethylene adipate or polybutylene adipate; 5 to 10 parts of trimethylolpropane; 10 to 200 parts of polybutylene adipate; 30 parts of polyether 330N; 0.1 to 0.3 parts of catalyst; 80 to 150 parts of black material and 200 to 340 parts of solvent, all the parts mentioned in the present invention are parts by mass. In the present invention, the molecular weight of polyhexamethylene adipate or polybutylene adipate is 2000-4000, and the single-component low-temperature polyurethane foam in this embodiment includes polyhexamethylene adipate 150 parts of ester; 5 parts of polytrimethylolpropane; 10 parts of ether 330N; 0.1 part of catalyst; 80 parts of black material; 200 parts of solvent.

[0029] The black material of the present invention is any one in toluene diisocyanate, diphenylmethane diisocyanate, polymethyl polyphenylisocyanate, what the black material i...

Embodiment 2

[0033] The implementation of this example is the same as that of Example 1, except that the single-component low-temperature polyurethane foam in this example is composed of the following components by mass: 155 parts of polyhexamethylene adipate; 12 parts of polyether 330N; 90 parts of black material, what black material adopts is diphenylmethane diisocyanate; 6 parts of trimethylolpropane; 210 parts of solvent, what solvent adopts is trichloroethane; 0.14 part of catalyst, what catalyst uses is dilauric acid di Butyl tin. The surface-drying time of the one-component low-temperature polyurethane foam prepared in this example is 16 minutes, the curing temperature is 55° C., and the hard-drying time is 18 minutes.

Embodiment 3

[0035] The implementation of this example is the same as Example 1, except that the single-component low-temperature polyurethane foam in this example is composed of the following components by mass: 160 parts of polyhexamethylene adipate; 15 parts of polyether 330N; 95 parts of black material, the black material used is polymethyl polyphenylisocyanate; 6.5 parts of trimethylolpropane; 240 parts of solvent, the solvent used is a compound of ethyl acetate and butyl acetate; 0.18 parts of catalyst , the catalyst used is bismorpholine. The surface-drying time of the one-component low-temperature polyurethane foam adhesive prepared in this example is 18 minutes, the curing temperature is 50° C., and the hard-drying time is 16 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tack-free timeaaaaaaaaaa
tack-free timeaaaaaaaaaa
tack-free timeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a single component low-temperature polyurethane foaming adhesive which is characterized by comprising the following components in parts by weight: 150-200 parts of polypropylene glycol adipate or polybutylene adipate, 5-10 parts of trimethylolpropane, 10-30 parts of polyester 330N, 0.1-0.3 part of a catalyst, 80-150 parts of a black material and 200-340 parts of a solvent. The single component low-temperature polyurethane foaming adhesive disclosed by the invention is relatively long in surface dry time, relatively low in curing temperature and relatively short in real-dry time, so that the application range of the foaming adhesive is widened, the resource is saved, and the working efficiency of an operator is improved; the single component low-temperature polyurethane foaming adhesive disclosed by the invention is simple in preparation method and convenient to operate, so that the production cost of the single component low-temperature polyurethane foaming adhesive is lowered, and the popularization and the application are facilitated.

Description

technical field [0001] The invention relates to a foaming glue, in particular to a single-component low-temperature polyurethane foaming glue and a preparation method thereof. Background technique [0002] In the production and assembly process of decoration materials, it is generally used to apply foam glue to the gaps and holes of decoration material parts, and use the foaming characteristics and bonding characteristics of foam glue to fill, seal and bond them. . Commonly used styrofoams include silicone styrofoam, polysulfide styrofoam, and polyurethane styrofoam. Among them, styrofoam uses trace moisture in the air as a crosslinking accelerator, and cures to an elastic state at room temperature. The advantages of strong adhesion, good elasticity, insulation, high temperature resistance and cold resistance, high adhesion to general building decoration materials, and low price, so polyurethane foam has been widely used. At present, the quality of polyurethane foam on the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J175/06C09J175/08C08G18/66C08G18/42C08G18/48C08G18/32C08G101/00
Inventor 程政
Owner 湖北和乐门业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com