A kind of anti-ultraviolet aging SBR modified asphalt and preparation method thereof

A modified asphalt, UV-resistant technology, used in building components, building insulation materials, buildings, etc., can solve the problems of incompatibility, SBS-modified asphalt has a great influence on the structure and performance, and poor road traffic capacity. Low temperature performance, avoiding precipitation and segregation, reducing the effect of collision aggregation

Active Publication Date: 2017-08-25
JIANGSU BAOLI INT INVESTMENT CO LTD +1
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The aging and damage of the asphalt pavement is serious. There are many broken roads on the national and provincial roads. The traffic capacity of the existing roads is poor. Except for the Qinghai-Tibet Highway, other trunk roads are seriously blocked due to various diseases
[0003] Ultraviolet light causes high energy density and strong destructiveness, which has a great impact on the structure and performance of SBS modified asphalt. Conventional modified asphalt cannot adapt to the current climate characteristics of strong ultraviolet rays in plateau areas such as Tibet and Qinghai. Patent CN102190957A proposes the use of magnesium-aluminum substrates Shaped dihydroxyl conforms to the excellent UV reflective properties of metal hydroxides to improve the UV aging resistance of SBS modified asphalt coating materials. Patent CN200810204209.4 proposes to compound UV absorbers in asphalt to improve the UV aging resistance of asphalt
However, this compound is prone to chemical changes such as volatilization and decomposition after the modified asphalt temperature reaches 180°C-190°C, and the desired effect cannot be achieved.
In addition, the above-mentioned technologies are all theoretical discussions. In practical applications, when the material is used as an additive in the production and processing of UV aging-resistant modified asphalt, it is difficult to miscible with the polymer compound of modified asphalt, and segregation is easy to occur. Caused transport tanker and asphalt mixing system to be paralyzed due to blockage
Therefore, the application of this material in UV aging-resistant modified asphalt has great technical difficulties.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-ultraviolet aging SBR modified asphalt and preparation method thereof
  • A kind of anti-ultraviolet aging SBR modified asphalt and preparation method thereof
  • A kind of anti-ultraviolet aging SBR modified asphalt and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0039] The raw materials were weighed according to the weight of the following components: 2 kg of magnesium-aluminum layered double hydroxide UV barrier material, 2 kg of reclaimed rubber, 1 kg of compatibilizer, and 2 kg of styrene-butadiene rubber, of which the magnesium-aluminum layered double hydroxide UV barrier material was produced by Jiangyin Produced by Ruifa Chemical Company, the magnesium-aluminum layered double hydroxide UV barrier material consists of magnesium-aluminum double hydroxide laminates and interlayer carbonates to form a multi-level layered structure, which belongs to anionic layered clay and belongs to Hexagonal crystal system, the specific composition is Mg 1-X al X (OH) 2 (CO 3 ) X / 2 mH 2 O, where the subscript X refers to the change of the content of metal elements, 0.2≤X≤0.33; m value represents the amount of crystal water, 0≤m≤2. Put the above-mentioned raw materials into a high internal mixer for internal mixing for 20 minutes; the temperat...

specific Embodiment 2

[0046] The raw materials were weighed according to the weight of the following components: 1.5 kg of magnesium-aluminum layered double hydroxide UV barrier material, 2 kg of reclaimed rubber, 1.6 kg of compatibilizer, and 1.8 kg of styrene-butadiene rubber, of which the magnesium-aluminum layered double hydroxide UV barrier The material is produced by Jiangyin Ruifa Chemical Co., Ltd. The magnesium-aluminum layered double hydroxide ultraviolet barrier material is composed of magnesium-aluminum double hydroxide laminates and interlayer carbonates to form a multi-level layered structure, which belongs to anionic layered Clay, belonging to the hexagonal crystal system, the specific composition is Mg 1-X al X (OH) 2 (CO 3 ) X / 2 mH 2 O, where the subscript X refers to the change of the content of metal elements, 0.2≤X≤0.33; m value represents the amount of crystal water, 0≤m≤2. The above-mentioned raw materials were put into a high internal mixer for internal mixing for 25 min...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a UV aging-resistant SBR modified asphalt and a preparation method thereof, characterized in that, the UV aging-resistant SBR modified asphalt is composed of 7-30% of ultraviolet blocking modifier particles mixed with a mass fraction of 70% ~93% base asphalt; the UV barrier modifier particles are made of SBR modifier, magnesium-aluminum layered double hydroxide UV barrier material, compatibilizer and reclaimed rubber through banbury mixing equipment kneading and mixing 20% to 60% of magnesium-aluminum layered double hydroxide UV blocking material; 25% to 35% of reclaimed rubber; 12% to 18% of compatibilizer; 25% of SBR modifier %~45%. The modified asphalt prepared by the present invention can not only withstand high temperature in summer and low temperature and severe cold in winter, but also play a good role in physical reflection, shielding and chemical absorption of ultraviolet rays in plateau areas, which can reduce early-stage diseases of the road surface and greatly prolong the use of asphalt pavement It can be used in the construction of high-grade highways in plateau areas.

Description

technical field [0001] The invention relates to the technical field of modified asphalt for road engineering, in particular to modified asphalt suitable for areas with strong ultraviolet rays in the Tibetan Plateau region and a preparation method thereof. Background technique [0002] With an average altitude of more than 4,000 meters, the Tibet Autonomous Region is the main part of the Qinghai-Tibet Plateau and is known as the "roof of the world". The annual average sunshine hours in Lhasa are about 3005 hours. The atmosphere here is weak, with less water vapor and dust content, and good transparency. When sunlight passes through the atmosphere, energy is lost, so it is the area with the most solar radiation in the country. Tibet is one of the areas with the strongest ultraviolet light in the world. Asphalt is an organic macromolecular material, which is highly susceptible to photo-oxidative aging due to the influence of ultraviolet radiation, which further deteriorates ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L95/00C08L9/06C08L17/00C08K3/26
Inventor 李福建周文婷韩君陶红
Owner JIANGSU BAOLI INT INVESTMENT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com