Hydrophobic mineral wool

A technology of ore rock wool and iron ore, which is applied in the production field of water-repellent ore rock wool, can solve the problems of expensive and rising costs, and achieve the effects of simple and easy operation, good water-repellent effect, and good heat insulation performance

Active Publication Date: 2015-03-11
凯华新型建材沧州有限公司
View PDF5 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the imported product is relatively expens

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrophobic mineral wool

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0016] Example 1:

[0017] Production method of hydrophobic rock wool:

[0018] (1) Raw material preparation: mix basalt, fly ash, gabbro, iron ore, bauxite, wollastonite, and melt them into a liquid mixture;

[0019] (2) Hydrophobic liquid preparation, according to weight percentage: SILRES BS 1042 0.3-0.5%, methyl cellulose 5-8%, polyacrylamide solution 1-2%, the rest is phenolic resin phase and mix well;

[0020] (3) Fiber preparation: The liquid mixture is continuously flowed into the centrifugal roller rotating at high speed, the liquid mixture is condensed into filamentous filaments under the action of centrifugal throwing and air cooling, and the filaments are collected and formed under the action of the blower. , Spray the hydrophobic liquid evenly on the rock wool fiber;

[0021] The (1) raw material components are calculated by weight percentage: basalt 10%, fly ash 25%, gabbro 1.3%, iron ore 2.7%, bauxite 25%, wollastonite 36%.

Example Embodiment

[0022] Example 2:

[0023] Production method of hydrophobic rock wool:

[0024] (1) Raw material preparation: mix basalt, fly ash, gabbro, iron ore, bauxite, wollastonite, and melt them into a liquid mixture;

[0025] (2) Hydrophobic liquid preparation, according to weight percentage: SILRES BS 1042 0.3-0.5%, methyl cellulose 5-8%, polyacrylamide solution 1-2%, the rest is phenolic resin phase and mix well;

[0026] (3) Fiber preparation: The liquid mixture is continuously flowed into the centrifugal roller rotating at high speed, the liquid mixture is condensed into filamentous filaments under the action of centrifugal throwing and air cooling, and the filaments are collected and formed under the action of the blower. , Spray the hydrophobic liquid evenly on the rock wool fiber;

[0027] The (1) raw material components are calculated according to weight percentage: 15% basalt, 20% fly ash, 5.8% gabbro, 1.2% iron ore, 20% bauxite, and 38% wollastonite.

Example Embodiment

[0028] Example 3:

[0029] Production method of hydrophobic rock wool:

[0030] (1) Raw material preparation: mix basalt, fly ash, gabbro, iron ore, bauxite, wollastonite, and melt them into a liquid mixture;

[0031] (2) Hydrophobic liquid preparation, according to weight percentage: SILRES BS 1042 0.3-0.5%, methyl cellulose 5-8%, polyacrylamide solution 1-2%, the rest is phenolic resin phase and mix well;

[0032] (3) Fiber preparation: The liquid mixture is continuously flowed into the centrifugal roller rotating at high speed, the liquid mixture is condensed into filamentous filaments under the action of centrifugal throwing and air cooling, and the filaments are collected and formed under the action of the blower. , Spray the hydrophobic liquid evenly on the rock wool fiber;

[0033] The (1) raw material components are calculated according to weight percentage: basalt 12%, fly ash 14%, gabbro 2.8%, iron ore 1.2%, bauxite 30%, wollastonite 40%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a production method of hydrophobic mineral wool. The production method is characterized by comprising the following steps of 1, raw material blending: mixing graystone, fly ash, gabbro, iron ore, bauxite and wollastonite and melting the mixture to obtain a liquid mixture, 2, hydrophobic liquid preparation: mixing 0.3-0.5wt% of SILRES BS 1042, 5-8wt% of methyl cellulose, 1-2wt% of a polyacrylamide solution and the balance phenolic resin to obtain a uniform mixture, and 3, fiber preparation: continuously feeding the liquid mixture into a centrifugal roll in a high-speed rotation state so that the liquid mixture is coagulated to form fibers under the action of centrifugal throwing and air cooling and then the fibers are collected and molded under the action of blower air-blasting, and spraying the hydrophobic liquid to mineral wool fibers. The hydrophobic mineral wool comprises, by weight, 10-20% of graystone, 14-30% of fly ash, 2.8-6.8% of gabbro, 1.2-6.2% of iron ore, 20-35% of bauxite and 25-45% of wollastonite.

Description

technical field [0001] The invention relates to a production method of mineral rock wool, in particular to a novel production method of water-repellent mineral rock wool. Background technique [0002] Rock wool, also known as rock wool, is a kind of mineral wool. Fluffy short fibers made from natural rocks and minerals. It is an inorganic fiber made of natural rocks such as basalt, gabbro, dolomite, iron ore, bauxite, etc., which are melted and fibrillated at high temperature. The natural rock, ore and other raw materials are melted in a cupola or other pool kiln (temperature below 2000 ℃), blown and quenched into a fibrous shape with a pressure of 50 atmospheres. Or use the spinning method to drop the molten liquid flow on the multi-stage rotary rotor, and spin it into fibers by centrifugal force. According to the use temperature, it can be divided into ordinary rock wool (less than 900°C); high temperature rock wool (less than 900°C). High-quality rock wool can withsta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03B37/005C03C13/06C03C25/14C03C25/34
Inventor 潘高峰
Owner 凯华新型建材沧州有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap