Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Flexible epoxy resin composition with hyperbranched structure and synthesis method thereof

A technology of epoxy resin and composition, which is applied in the field of polyester curing agent with hyperbranched structure and its synthesis, can solve many problems, and achieve the effects of cost reduction, low price and high functionality

Inactive Publication Date: 2015-03-11
天津凯华绝缘材料股份有限公司
View PDF2 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although there are many toughening methods, there are not many methods that can actually be applied to electronic packaging materials, copper clad laminate substrates and anti-corrosion coatings for steel bars

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flexible epoxy resin composition with hyperbranched structure and synthesis method thereof
  • Flexible epoxy resin composition with hyperbranched structure and synthesis method thereof
  • Flexible epoxy resin composition with hyperbranched structure and synthesis method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A kind of flexible type epoxy resin composition with hyperbranched structure, its preparation method is as follows:

[0035] Premix epoxy resin, polyester curing agent A with hyperbranched structure, other curing agents, curing accelerators and inorganic fillers according to the ratio of parts by mass. The premixing time is 5-20min, and the speed is 500-1000r / min ; Then melt kneading extrusion (extrusion temperature 70 ~ 150 ℃, extruder speed 1500 ~ 3000r / min, feeding speed 900 ~ 2400r / min), then pulverized and sieved to obtain the epoxy resin composition. The amounts of the above-mentioned substances are shown in Table 1.

[0036] Wherein, a kind of synthetic method of the polyester curing agent A of hyperbranched structure, the steps are as follows:

[0037] ⑴In a 1L four-neck flask equipped with a heating mantle, agitator, thermometer, distillation column and condenser tube, add 230g of neopentyl glycol and 59g of trimethylolpropane, heat to about 120°C and stir to...

Embodiment 2

[0044] A kind of flexible type epoxy resin composition with hyperbranched structure, its preparation method is as follows:

[0045] Pre-mix epoxy resin, polyester curing agent B with hyperbranched structure, other curing agents, curing accelerators and inorganic fillers according to the ratio of parts by mass. The pre-mixing time is 5-20 minutes, and the speed is 500-1000r / min ; Then melt kneading extrusion (extrusion temperature 70 ~ 150 ℃, extruder speed 1500 ~ 3000r / min, feeding speed 900 ~ 2400r / min), then pulverized and sieved to obtain the epoxy resin composition. The amounts of the above-mentioned substances are shown in Table 1.

[0046] A kind of synthetic method of the polyester curing agent B of hyperbranched structure, the steps are as follows:

[0047] (1) Add 230g of neopentyl glycol and 56g of trimethylolpropane into a 1L four-neck flask equipped with a heating mantle, agitator, thermometer, distillation column and condenser, heat to about 120°C and stir to me...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
epoxy valueaaaaaaaaaa
acid valueaaaaaaaaaa
Login to View More

Abstract

The invention relates to a flexible epoxy resin composition with a hyperbranched structure and a synthesis method thereof. The flexible epoxy resin composition comprises the following ingredients in parts by weight: 25-40 parts of epoxy resin, 15-20 parts of a hyperbranched polyester curing agent, 0-5 parts of other curing agents, 0.05-0.3 part of a curing accelerator and 30-55 parts of an inorganic filler. After the hyperbranched polyester curing agent is added, the synthesized polyester curing agent is applied to an epoxy electronic packaging material, the flexibility is excellent, the crosslinking density and the strength are large, the electronic packaging material is free of halogen, the machinability, the physical properties and the electrical property of the electronic packaging material are optimized, and the flexibility applied to the electronic packaging material is excellent, so that the cold and thermal shock resistances of the electronic packaging material is largely improved.

Description

technical field [0001] The invention belongs to the field of electronic packaging materials, in particular to a polyester curing agent with a hyperbranched structure and a synthesis method thereof. Background technique [0002] Epoxy resin is one of the most widely used matrix resins in polymer-based composite materials. It is a product obtained by polycondensation reaction of compounds with epoxy groups and polyhydric hydroxyl or polyol compounds. It has excellent adhesion, resistance Chemical corrosion, electrical insulation properties, mechanical properties, and easy processing, low shrinkage, small linear expansion coefficient, and low cost are widely used in the packaging of electronic components such as varistors, ceramic capacitors, diodes, and triodes. [0003] However, due to the lack of toughness of pure epoxy resin, the cured substance is easy to become brittle and cracks, so it cannot be used for the packaging of electronic components with high temperature cycle ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G59/42C08G63/20C08G63/85C08L63/00B29C47/92B29C48/92
Inventor 沈纪洋
Owner 天津凯华绝缘材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com