A casting coating and environmental protection technology, applied in casting molding equipment, coatings, casting molds, etc., can solve the problems that zircon powder coatings are expensive and cannot meet the low-cost requirements of small and medium-sized foundries, and achieve good sintering peeling characteristics , enhanced peeling effect, and low raw material cost

Active Publication Date: 2015-03-25
TIANJIN NINGKANG TECH
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, zircon powder coatings are expensive and cannot meet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly alcohol group ceramic casting coating
  • Environment-friendly alcohol group ceramic casting coating

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0028] Example 1

[0029] An environmentally friendly alcohol-based ceramic casting coating composed of the following components by weight: 250 kg high alumina powder, 150 kg silica fume, 30 kg potassium feldspar powder, 175 kg pyrophyllite powder, 25 kg magnesium aluminum silicate, and rosin 10 kilograms, 5 kilograms of ethyl silicate, one kilogram of Tween 80, and 280 kilograms of ethanol.

[0030] Among them, the high alumina powder in AL 2 O 3 The mass percentage is greater than 80%, and the particle size is 325 mesh; SiO in the silicon powder 2 The mass percentage is greater than 98%, and the particle size is 325 mesh; the pyrophyllite powder contains AL 2 O 3 The mass percentage is greater than 20%, and the particle size is 200 mesh.

Example Embodiment

[0031] Example 2

[0032] An environmentally-friendly alcohol-based ceramic casting coating composed of the following components by weight: 270 kg high alumina powder, 120 kg silica fume, 32 kg potassium feldspar powder, 150 kg pyrophyllite powder, 22 kg magnesium aluminum silicate, and rosin 11 kg, 3 kg ethyl silicate, 2 kg Tween 80, 250 kg ethanol.

[0033] Among them, the high alumina powder in AL 2 O 3 The mass percentage is greater than 80%, and the particle size is 325 mesh; SiO in the silicon powder 2 The mass percentage is greater than 98%, and the particle size is 325 mesh; the pyrophyllite powder contains AL 2 O 3 The mass percentage is greater than 20%, and the particle size is 200 mesh.

Example Embodiment

[0034] Example 3

[0035] An environmentally-friendly alcohol-based ceramic casting coating composed of the following components by weight: 290 kg high alumina powder, 110 kg silica fume, 38 kg potassium feldspar powder, 190 kg pyrophyllite powder, 22 kg magnesium aluminum silicate, and rosin 9 kg, 5 kg ethyl silicate, 2 kg Tween 80, and 260 kg ethanol.

[0036] Among them, the high alumina powder in AL 2 O 3 The mass percentage is greater than 80%, and the particle size is 325 mesh; SiO in the silicon powder 2 The mass percentage is greater than 98%, and the particle size is 325 mesh; the pyrophyllite powder contains AL 2 O 3 The mass percentage is greater than 20%, and the particle size is 200 mesh.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Login to view more

Abstract

The invention provides an environment-friendly alcohol group ceramic casting coating. The environment-friendly alcohol group ceramic casting coating comprises, by weight, 250-350 parts of high-alumina powder, 50-150 parts of silica powder, 150-200 parts of pyrophillite powder, 30-50 parts of cosolvent, 20-30 parts of suspending agents, 8-15 parts of binding agents, 1-3 parts of surfactant and 250-350 parts of solvent. The environment-friendly alcohol group ceramic casting coating overcomes the defects in the prior art and is high in refractoriness, good in sintering stripping effect, low in price and excellent in comprehensive performance.

Description

technical field [0001] The invention relates to the field of casting, in particular to an environment-friendly alcohol-based ceramic casting coating. Background technique [0002] Foundry coatings refer to casting auxiliary materials that are coated on the surface of the cavity or sand core to change their refractoriness, chemical stability, sand resistance and other properties. Casting coatings mostly use high refractory powder to improve the refractory performance of the cavity or grinding wheel. However, because of the high refractoriness, the coating is easy to form a low-melting point phase during pouring, and the original powder is used throughout the casting process. The state exists, so that the molten iron penetrates into the shallow surface layer of the coating, resulting in powder sticking of the casting. The sticky powder is extremely difficult to clean and can only be removed by grinding, which will bring a very large workload to the later cleaning, and the inn...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22C3/00
CPCB22C3/00
Inventor 刘聪张保军
Owner TIANJIN NINGKANG TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap