Unbleached tissue packing paper and production method thereof
A wrapping paper and thin sheet technology, applied in wrapping paper, wrapping paper, packaging, etc., can solve the problems of not finding the preparation method of thin sheet wrapping paper, affecting the speed and productivity of the paper machine, and prolonging the beating time, so as to reduce refining Energy consumption, improved water filtration performance, and low beating degree
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0063] The wheat straw raw material is steamed and boiled by a conventional method, and then squeezed, washed and decomposed. Pump the straw pulp with a concentration of 10% obtained after thawing to the oxygen delignification reaction tower for oxygen delignification treatment. Magnesium sulfate with a pulp volume of 5% is mixed with 4% lye in terms of sodium hydroxide for the absolute dry pulp volume, and steam is fed into the pipeline to add the slurry to raise the temperature. Afterwards, the pulp enters the oxygen delignification reaction tower after being fully mixed in the mixing chamber. The temperature at the inlet of the reaction tower is 90°C and the pressure is 0.9Mpa. The temperature is 100°C and the pressure is maintained at 0.3Mpa. After the treatment is completed, the pulp is sprayed into the pulp tank and diluted to obtain the unbleached straw pulp. The degree of beating of the unbleached straw pulp is 34°SR.
[0064] The unbleached wood pulp and the unblea...
Embodiment 2
[0077] The bagasse raw material is steamed and boiled by a conventional method, and then squeezed, washed and decomposed. Pump the straw pulp with a concentration of 8% obtained after thawing to the oxygen delignification reaction tower for oxygen delignification treatment. Magnesium sulfate with a pulp volume of 3% is mixed with 3% lye in terms of sodium hydroxide for the absolute dry pulp volume, and steam is introduced into the pipeline to add the slurry to raise the temperature. Afterwards, the pulp enters the oxygen delignification reaction tower after being fully mixed in the mixing chamber. The temperature at the inlet of the reaction tower is 95°C and the pressure is 0.9Mpa. The temperature is 100°C and the pressure is maintained at 0.4Mpa. After the treatment is completed, the pulp is sprayed into the pulp tank and diluted to obtain the unbleached straw pulp. The beating degree of the unbleached straw pulp is 36°SR.
[0078] The unbleached wood pulp and the unbleac...
Embodiment 3
[0091] The Arundis raw material is steamed and boiled by a conventional method, and then squeezed, washed and decomposed. Pump the straw pulp with a concentration of 13% obtained after thawing to the oxygen delignification reaction tower for oxygen delignification treatment. Magnesium sulfate with a pulp volume of 4% is mixed with 2% lye in terms of sodium hydroxide for the absolute dry pulp volume, and steam is introduced into the pipeline to add the slurry to heat up. Afterwards, the pulp enters the oxygen delignification reaction tower after being fully mixed in the mixing chamber. The temperature at the inlet of the reaction tower is 100°C and the pressure is 1.02Mpa. The temperature is 105°C and the pressure is maintained at 0.4Mpa. After the treatment is completed, the pulp is sprayed into the pulp tank and diluted to obtain the unbleached straw pulp. The degree of beating of the unbleached straw pulp is 35°SR.
[0092] The unbleached wood pulp and the unbleached stra...
PUM
Property | Measurement | Unit |
---|---|---|
Tightness | aaaaa | aaaaa |
Tightness | aaaaa | aaaaa |
Tear | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com