A body manufacturing method of an oil-immersed amorphous alloy transformer

An amorphous alloy and a production method technology, applied in the field of transformers, can solve the problems of increased noise and loss of transformers, increased noise of loose iron cores, multi-point grounding of transformers, etc., to reduce sound energy, prevent buffer vibration, and reduce core loss per unit. Effect

Active Publication Date: 2017-01-11
NINGBO AUX HIGH TECH
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In order to save costs, the oil-immersed amorphous alloy transformer must reduce the volume of the transformer body, and then reduce the amount of various raw materials. It is necessary to control the annealing of the transformer core and bind the transformer body to ensure the loss level of the transformer. Safe insulation distance and withstand voltage level, but because the amorphous core is very sensitive to stress, if the binding is too tight, the noise and loss of the transformer will increase. Loose noise will increase sharply, which is likely to damage the outsourcing insulation, and even cause multi-point grounding of the transformer, burning the transformer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The present invention will be further described below.

[0017] A body manufacturing method of an oil-immersed amorphous alloy transformer of the present invention comprises the following steps:

[0018] (1) Anneal the iron core: put the iron core into the annealing furnace, turn on the heating switch, when the maximum temperature of the monitored iron core rises to 120°C, turn on the field power supply and record the time when the field power supply is turned on; the field power supply is provided for annealing of the amorphous core For the power supply of the electromagnetic field, when the minimum temperature of the monitored iron core rises to 200°C, use a thermocouple thermometer to monitor the temperature of the iron core, turn off the heating switch, and start to pull the temperature difference. The temperature difference is to use thermal inertia and ambient temperature to reduce the temperature of the iron core in the annealing furnace Difference, record the st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a manufacturing method of a transformer body of an oil immersion type amorphous alloy transformer. The manufacturing method includes the following steps: (1) annealing treatment is carried out on iron cores; (2) the iron cores are pushed to the testing position for testing according to the furnace exiting sequence; (3) coils for forming the transformer body of the transformer draw close; (4) iron core jackets are drawn off after the iron cores are pushed into the testing position; (5) packing is carried out; (6) binding is carried out, wherein the binding belt tension ranges from 1500 N to 2500 N according to different weights of the transformer body; (7) after an amorphous sheet layer on the outmost face is closed, a shock pad is placed on the outer face of the amorphous sheet layer, a silicon steel sheet hasp on the outer layer is tightened, the hasp part is firmly glued through adhesive tape, and the adhesive tape is used for firm gluing if the hasp is damaged; (8) the coils are cleaned; (9) the lap joint position is coated with glass cement; (10) upper clamp insulation is arranged, and an upper clamp is installed in place. By means of the manufacturing method, stable-performance annealing parameters can be guaranteed, the fixing effect is improved through an elastic insulation binding belt, and the sound insulation effect and the sound absorption effect can be improved.

Description

technical field [0001] The invention relates to the technical field of transformers, in particular to a method for manufacturing an oil-immersed amorphous alloy transformer body. Background technique [0002] In order to save costs, the oil-immersed amorphous alloy transformer must reduce the volume of the transformer body, and then reduce the amount of various raw materials. It is necessary to control the annealing of the transformer core and bind the transformer body to ensure the loss level of the transformer. Safe insulation distance and withstand voltage level, but because the amorphous core is very sensitive to stress, if the binding is too tight, the noise and loss of the transformer will increase. Loose noise will increase sharply, which is likely to damage the outsourcing insulation, and even cause multi-point grounding of the transformer, which will burn the transformer. Contents of the invention [0003] The technical problem to be solved by the present inventi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01F41/00H01F27/30H01F27/26
Inventor 郑坚江杨百国任东波张明
Owner NINGBO AUX HIGH TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products