Peelable glue coating composition and peelable glue coating as well as preparation method and application of peelable glue coating

A coating composition and stripping technology, applied in the direction of coating, can solve the problems of low light transmittance, high haze and discomfort of strippable coatings, and achieve high strippability, low haze, and bubbles and warpage problem improvement effect

Active Publication Date: 2015-04-01
ZHANGJIAGANG KANGDE XIN OPTRONICS MATERIAL
View PDF8 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The main purpose of the present invention is to provide a kind of peelable glue coating composition, peelable glue coating, preparation method and application of peelable glue coating, to solve the low light transmittance of peelable glue coating in the prior art, High haze is unsuitable as a multi-functional hard coating protective layer in ITO-film production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Peelable glue coating composition and peelable glue coating as well as preparation method and application of peelable glue coating
  • Peelable glue coating composition and peelable glue coating as well as preparation method and application of peelable glue coating
  • Peelable glue coating composition and peelable glue coating as well as preparation method and application of peelable glue coating

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0039] According to another aspect of the present invention, there is also provided a method for preparing a peelable adhesive coating, which includes the following steps: S1, configuring a peelable adhesive coating composition; S2, coating the peelable adhesive coating composition Cover and cure to obtain a peelable adhesive coating.

[0040] When the peelable adhesive coating composition provided by the present invention is used to prepare the peelable adhesive coating, it can be directly coated, cured and shaped. The method has simple process and low operation cost.

[0041] According to the above teaching of the present invention, those skilled in the art can select a specific curing process. In a preferred embodiment, the above step S2 includes: S21, coating the peelable adhesive coating composition to obtain the layer to be cured; S22, keeping the layer to be cured at a temperature of 80-110°C for 80-100s , to obtain the pre-cured layer; S23, the pre-cured layer was ex...

Embodiment 1

[0046] (1) drop into 100g aliphatic urethane acrylate 6148J-75 (manufactured by Changxing Chemical Co., Ltd.), 16g ethoxylated trimethylolpropane triacrylate EM2380 (manufactured by Changxing Chemical Co., Ltd.) and 40g isopropanol in a 500ml shading bucket , Stir evenly with a high-speed disperser. Then add 0.4g leveling agent BYK378 (manufactured by BYK), 0.5g leveling agent 9137 (manufactured by Double Bond Chemical Co., Ltd.), 0.6g peeling force modifier methylcellulose (National Medicine) while stirring in order. 2g anti-blocking agent MEK-AB-402 (nanometer silica slurry, manufactured by Nissan Chemical Co., Ltd.) and 5g photoinitiator 184 (manufactured by Tianjin Tianjiao Chemical Co., Ltd.). After the addition, stir at a high speed of 1200rpm for 60 minutes, then let it stand for more than 60 minutes to defoam naturally, and obtain a peelable coating composition;

[0047] (2) Coat the prepared peelable adhesive coating composition on the functional hardened coating sur...

Embodiment 2

[0049](1) Put 70 g of aliphatic urethane acrylate 6148J-75 (manufactured by Changxing Chemical Co., Ltd.), 30 g of aliphatic urethane acrylate EBECRYL9260 (manufactured by Allnex), and 13 g of propoxylated neopentyl glycol diacrylate EM2251 into a 500 ml shading bucket (manufactured by Changxing Chemical Co., Ltd.) and 40g of isopropanol, stirred evenly with a high-speed disperser. Then add 0.4g leveling agent BYK-UV3505 (manufactured by BYK), 0.5g leveling agent 9137 (manufactured by Double Bond Chemical Co., Ltd.), 0.6g peeling force modifier methyl cellulose (manufactured by Sinopharm) while stirring in order. ), 2g anti-blocking agent MEK-AB-402 (nano silica slurry, manufactured by Nissan Chemical Co., Ltd.), 3g photoinitiator 184 (manufactured by Tianjin Tianjiao Chemical Co., Ltd.) and 2g photoinitiator TPO (Double Bond Chemical Co., Ltd. Ltd.). After the addition, stir at a high speed of 1200rpm for 60 minutes, then let it stand for more than 60 minutes to defoam natur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a peelable glue coating composition and a peelable glue coating as well as a preparation method and an application of the peelable glue coating. The peelable glue coating composition comprises the following components in parts by weight: 80-120 parts of an acrylate type oligomer, 8-20 parts of a dilutive monomer, 0.1-1.5 parts of a peeling force modifying agent, 2-12 parts of a triggering agent and 30-50 parts of an organic solvent. The peelable glue coating composition is relatively high in transparency and relatively high in light transmittance and relatively low in haze after film formation. Meanwhile, a coating formed by curing the peelable glue coating composition is relatively high in high temperature resistance and relatively high in peelability. By the high temperature resistance, the coating is good in adhesion property on the surface of a functional hardened layer, and the problems of air bubbles and warping can be effectively improved. By the peelability, the problem of glue layer residues caused during peeling of the coating can be reduced.

Description

technical field [0001] The invention relates to the field of ITO-film manufacture, in particular to a peelable adhesive coating composition, a peelable adhesive coating, a preparation method and an application of the peelable adhesive coating. Background technique [0002] At present, touch screen technology has been widely used in mobile phones, notebook computers, tablet computers and other fields, among which transmissive capacitance, OGS (One Glass Solution, single-chip touch panel), in-cell, and on-cell are the current mainstream technology. With the increasing size and thinning of touch screens, the OGS technology has more compressed the market share of the transmissive capacitive technology. The most critical core technology in touch screen technology is the use of ITO-film in its entire assembly. ITO-film products are not only used on touch screens, but also widely used in other flexible display devices, such as electronic paper books, OLED, etc. On the other hand...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/06C09D4/02C09D7/12
Inventor 夏有贵李冠毅丁清华
Owner ZHANGJIAGANG KANGDE XIN OPTRONICS MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap