Bamboo weaving softening agent and preparation technique thereof

A softener and bamboo weaving technology, which is applied in the manufacture of tools, wood processing equipment, reed/straw treatment, etc., can solve the problems of easy to bake and break bamboo, the softening method is too simple, and affects the toughness and strength of bamboo, so as to achieve good softening effect, Easier to promote and use, better results

Active Publication Date: 2015-04-08
山东阳信华龙纺织科技有限公司
View PDF5 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing bamboo weaving softening generally follows the traditional method of roasting. After the bamboo is roasted, it can be bent and woven into various products. This softening method is too simple, and it is easy to roast the bamboo, which affects the toughness and strength of the bamboo.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Embodiment 1: bamboo weaving softener, it is characterized in that: comprise 28 parts of strength improvers, 41 parts of form retaining agents, 66 parts of softening agents, 16 parts of initiators, 10 parts of reinforcing agents, 130 parts of water;

[0015] Strength improver: stearyl alcohol 60%, stearic acid 40%;

[0016] Form retaining agent: 15% stearic acid, 65% ethyl carbamate, 20% paraffin;

[0017] Softener: glycerol 20%, alcohol ether glycoside 20%, polyoxyethylene ether 30%, surfactant 30%;

[0018] Initiator: 15% glyoxal, 25% formaldehyde, 60% ammonium persulfate;

[0019] Enhancer: talcum powder 40%, limestone powder 30%, calcium carbonate 30%.

[0020] Preparation method of bamboo weaving softener: it is characterized in that: take glycerin, alcohol ether glycoside, polyoxyethylene ether and surfactant, put them into a stirring tank, stir for 30 minutes, and the stirring temperature is 80°C, then add glyoxal, Add formaldehyde, ammonium persulfate, talcum...

Embodiment 2

[0023] Embodiment 2: bamboo weaving softener, it is characterized in that: comprise 34 parts of strength improvers, 48 ​​parts of form retaining agents, 71 parts of softening agents, 19 parts of initiators, 16 parts of reinforcing agents, 140 parts of water;

[0024] Strength improver: stearyl alcohol 70%, stearic acid 30%;

[0025] Form retaining agent: 25% stearic acid, 65% ethyl carbamate, 15% paraffin;

[0026] Softener: glycerol 30%, alcohol ether glycoside 30%, polyoxyethylene ether 20%, surfactant 20%;

[0027] Initiator: 25% glyoxal, 20% formaldehyde, 55% ammonium persulfate;

[0028] Enhancer: talcum powder 40%, limestone powder 30%, calcium carbonate 30%.

[0029] Preparation method of bamboo weaving softener: it is characterized in that: take glycerin, alcohol ether glycoside, polyoxyethylene ether and surfactant, put them into a stirring tank, stir for 30 minutes, and the stirring temperature is 80°C, then add glyoxal, Add formaldehyde, ammonium persulfate, talc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a bamboo weaving softening agent and a preparation method thereof. The preparation method comprises the following steps: putting glycerol, alcohol ether glucoside, polyethenoxy ether and a surfactant into a stirring tank, stirring for 30 minutes at 80 DEG C, adding glyoxal, formaldehyde and ammonium persulfate, simultaneously adding talcum powder, limestone flour and calcium carbonate, quickly stirring at 130 DEG C for 3 minutes, finally adding stearyl alcohol, stearic acid, ethyl carbamate and paraffin, stirring for 1 hour, and cooling to normal temperature. The softening agent prepared by the method has the advantages of favorable softening effect, no corrosion and better effects, enhances the strength and toughness of the softened part, and is convenient for popularization and use.

Description

Technical field: [0001] The invention relates to the technical field of bamboo softening, in particular to a bamboo weaving softener and a preparation process thereof. Background technique: [0002] Existing bamboo weaving softening generally follows the traditional method of roasting. After the bamboo is roasted, it can be bent and woven into various products. This softening method is too simple, and it is easy to roast the bamboo, which affects the toughness and strength of the bamboo. Invention content: [0003] The technical problem to be solved by the present invention is to overcome the defects of the prior art and provide a bamboo weaving softener and its preparation process. [0004] The technical problem to be solved by the present invention is realized by the following technical solutions. [0005] The softening agent for bamboo weaving is characterized in that: it includes 28-34 parts of strength improving agent, 41-48 parts of shape maintaining agent, 66-71 pa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27K3/52B27K5/06
CPCB27K5/06B27K9/002
Inventor 王银
Owner 山东阳信华龙纺织科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com