Environment-friendly thermoplastic elastomer foamed floor mat material and preparation method thereof

A thermoplastic elastomer and floor mat technology, applied in the field of floor mat materials, can solve the problems of large decline in physical properties, TPE heat resistance is not as good as rubber, and limited application range, etc., to achieve low addition, improve creep resistance, Good smoke suppression effect

Active Publication Date: 2015-04-08
FUJIAN SIJIA ENVIRONMENTAL PROTECTION MATERIAL TECH
View PDF8 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the heat resistance of TPE is not as good as that of rubber, and the physical properties decrease greatly as the temperature rises, so the scope of application is limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0051] A kind of preparation method of environment-friendly thermoplastic elastomer foaming mat material, it comprises the following steps:

[0052] 1) Pour the components of the TPU film layer into the calender molding machine and calender to obtain the TPU film layer;

[0053] 2) Pour the components of the TPE foam layer into a calender molding machine and calender to obtain a TPE foam layer;

[0054] 3) Preheat the reinforced fiber mesh under the heating roller to remove the impurities attached to the surface, then send it to the coating machine through the sending device, dip it in the PU adhesive layer coating solution, and send it to the scraper device to control Paste the amount, and then send it to the oven for drying and plasticization to obtain a first-class reinforced fiber mesh cloth with PU adhesive layers on the surface and bottom surface;

[0055] 4) Preheat the surface and bottom surface of the primary reinforced fiber mesh on the preheating roller, then heat th...

Embodiment 1

[0058] A kind of preparation method of environment-friendly thermoplastic elastomer foaming mat material, it comprises the following steps:

[0059] 1) Pour the components of the TPU film layer into the calender molding machine and calender to obtain the TPU film layer;

[0060] Described TPU film layer comprises the component of following weight portion:

[0061] 100 parts of TPU resin; 10 parts of sarin resin;

[0062] TPU slip agent masterbatch 2 parts; TPU color masterbatch 3 parts;

[0063] 25 parts of flame retardant masterbatch;

[0064] 2) Pour the components of the TPE foam layer into a calender molding machine and calender to obtain a TPE foam layer;

[0065] The TPE foam layer includes the following components by weight:

[0066] 100 parts of TPE resin; 20 parts of barium sulfate masterbatch;

[0067] 8 parts of high temperature foaming masterbatch; 3 parts of TPE color masterbatch;

[0068] 5 parts of anti-mildew and anti-bacterial masterbatch;

[0069] The ...

Embodiment 2

[0076] A kind of preparation method of environment-friendly thermoplastic elastomer foaming mat material, it comprises the following steps:

[0077] 1) Pour the components of the TPU film layer into the calender molding machine and calender to obtain the TPU film layer;

[0078] Described TPU film layer comprises the component of following weight part:

[0079] 100 parts of TPU resin; 13 parts of sarin resin;

[0080] 3 parts of TPU slip agent masterbatch; 4 parts of TPU color masterbatch;

[0081] 38 parts of flame retardant masterbatch;

[0082] 2) Pour the components of the TPE foam layer into a calender molding machine and calender to obtain a TPE foam layer;

[0083] The TPE foam layer includes the following components by weight:

[0084] 100 parts of TPE resin; 24 parts of barium sulfate masterbatch;

[0085] 8.5 parts of high temperature foaming masterbatch; 4 parts of TPE color masterbatch;

[0086] 6 parts of anti-mildew and anti-bacterial masterbatch;

[0087]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of floor mat materials, and particularly relates to an environment-friendly thermoplastic elastomer foamed floor mat material and a preparation method thereof. The environment-friendly thermoplastic elastomer foamed floor mat material sequentially comprises a surface treatment layer, a TPU film layer, a surface PU bonding layer, a reinforced fiber screen cloth layer, a bottom surface PU bonding layer and a TPE foaming layer. According to the invention, properties of the TPU material and the TPE material are integrated; the prepared environment-friendly thermoplastic elastomer foamed floor mat material is moderate in hardness, high in intensity and elasticity, and good in toughness, and has the characteristics of good anti-bacterial mildew resistance, slip resistance, flame retardance and the like.

Description

technical field [0001] The invention relates to the technical field of floor mat materials, in particular to an environment-friendly thermoplastic elastomer foamed floor mat material and a preparation method thereof. technical background [0002] At present, floor mats are mostly made of plastic floor mats, and most of these floor mats are made of PVC materials. PVC, that is, polyvinyl chloride, the material is yellowish translucent, shiny, and its transparency is better than polyethylene and polystyrene, and worse than polystyrene. With the amount of additives, it can be divided into soft and hard polyvinyl chloride, but Most of them do not have flame retardant properties. [0003] Thermoplastic polyurethane elastomer (TPU) is divided into polyester type and polyether type. TPU has excellent characteristics of high tension, high tensile force, toughness and aging resistance. It is a mature environmental protection material. At present, TPU has been widely used in medical ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/06B32B27/12B32B27/18B32B27/40B32B5/18B32B7/12B32B37/02B32B37/06C08L75/04C08L91/06C08L101/00C08L23/08C08K13/06C08K9/04C08K3/30C08K5/20C08K3/22C08K3/08C08J9/10
CPCB32B5/18B32B7/12B32B27/06B32B27/065B32B27/12B32B27/18B32B27/40B32B37/02B32B37/06B32B2266/0278C08K9/04C08L23/08C08L75/04
Inventor 林生雄张宏旺黄万能蒋石生邓中文
Owner FUJIAN SIJIA ENVIRONMENTAL PROTECTION MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com