Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Acrylic acid modified epoxy phosphate resin and aqueous dispersion thereof

A technology of epoxy phosphate ester and epoxy resin, used in epoxy resin coatings, coatings, anti-corrosion coatings, etc., can solve problems such as VOC emissions, and achieve good rust resistance and low hardness.

Inactive Publication Date: 2015-04-08
BEIJING JINHWEILI APPLIED CHEM PROD
View PDF0 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, solvent-based epoxy resin paints need to be diluted with a large amount of solvents, resulting in a large amount of VOC emissions, which cannot meet the increasingly stringent environmental protection requirements. In order to solve the above problems, and improve the adhesion of resin substrates, and provide other Anti-rust performance, specially developed the present invention

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Acrylic acid modified epoxy phosphate resin and aqueous dispersion thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] (1) Add 60940g of epoxy resin and 16g of ethylene glycol butyl ether into the reaction flask, heat to 155°C and stir to dissolve;

[0029] (2) Add 0.4g of phosphoric acid to 2g of diethylene glycol butyl ether to dissolve, drop into the material in (1) at 150-155°C, add dropwise at a constant speed for 20-30min, finish dropping, and keep warm for 2hr;

[0030] (3) Mix 1.4g of acrylic acid, 0.9g of methyl methacrylate, 4.5g of butyl acrylate, 1.2g of hydroxyethyl acrylate, and 2g of diethylene glycol butyl ether, add 0.5g of cumene hydroperoxide, and mix well Finally, drop it into the above material at 150-155°C for 2-3 hours, and finally keep it warm for 3 hours to obtain acrylic modified epoxy phosphate resin;

[0031] (4) Cool down the modified resin to 100°C, add 3.2g of N,N-dimethylethanolamine, stir evenly, drop 80g of distilled water at 70°C into the resin under strong stirring, emulsify, and make a water dispersion . Its solid content is 32.1%, VOC 15.2%, and t...

Embodiment 2

[0034] (1) Add 60942g of epoxy resin and 22g of ethylene glycol butyl ether into the reaction flask, heat to 155°C and stir to dissolve;

[0035] (2) Add 0.45 g of phosphoric acid to 2 g of diethylene glycol butyl ether to dissolve, drop into the material in (1) at 150-155 ° C, add dropwise at a constant speed for 20-30 minutes, and keep warm for 2 hours;

[0036] (3) Mix 1.5g of acrylic acid, 0.9g of methyl methacrylate, 4.5g of butyl acrylate, 1.6g of hydroxyethyl acrylate, and 2g of diethylene glycol butyl ether, add 0.7g of cumene hydroperoxide, and mix well Finally, drop it into the above material at 150-155°C for 2-3 hours, and finally keep it warm for 3 hours to obtain acrylic acid-modified epoxy phosphate;

[0037] (4) Cool down the modified resin to 100°C, add 4g of N,N-dimethylethanolamine, stir evenly, drop 85g of distilled water at 70°C into the resin under strong stirring, emulsify, and make a water dispersion . It contains 31% solids and 18% VOC. , the lotion ...

Embodiment 3

[0040] (1) Add 60745g of epoxy resin and 28g of ethylene glycol butyl ether into the reaction flask, heat to 155°C and stir to dissolve;

[0041] (2) Add 0.5 g of phosphoric acid to 2 g of diethylene glycol butyl ether to dissolve, drop it into the material in (1) at 150-155 ° C, drop it at a constant speed for 20-30 minutes, and keep it warm for 2 hours;

[0042] (3) Mix 2g of acrylic acid, 0.9g of methyl methacrylate, 6.5g of butyl acrylate, 1.8g of hydroxyethyl acrylate, and 2g of diethylene glycol butyl ether, add 0.8g of cumene hydroperoxide, and mix well Drop into the above material at 150-155°C for 2-3 hours, and finally keep warm for 3 hours to obtain acrylic modified epoxy phosphate resin;

[0043] (4) Cool down the modified resin to 100°C, add 5.2g of N,N-dimethylethanolamine, stir evenly, drop 100g of distilled water at 70°C into the resin under strong stirring, emulsify, and make water dispersion body. Its solid content is 30.8%, VOC 18.3%, and the emulsion does ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of painting, and particularly relates to acrylic acid modified epoxy phosphate resin and an aqueous dispersion thereof. In the formula, the acrylic acid modified epoxy phosphate resin is prepared from 40-45 parts of epoxy resin, 20-30 parts of a solvent, 0.4-0.5 part of phosphoric acid, 8-12 parts of acrylic acid (ester) monomer of which acrylic acid accounts for 1.4-2 parts, 0.5-0.8 part of an initiator, 3.2-5.2 parts of neutralizer and 80-100 parts of water. The resin is prepared by the following steps: modifying epoxy resin with phosphoric acid, and reacting with acrylic acid and ester monomers thereof; adding the neutralizer and deionized water, stirring and emulsifying to obtain the acrylic acid modified epoxy phosphate aqueous dispersion, wherein the acid value of the emulsion is 10-12mgKOH / g, and the solid content is 28-38 percent. The prepared main resin dispersion body is epoxy resin, has a phosphate structure, and has a good adhesive force for metal base materials, thus having good corrosion resistance; acrylic resin is modified, introduced with carboxyl and neutralized by the neutralizer to give aqueous dispersion to resin, so that the resin can be produced into water-borne painting, and the content of VOC is greatly reduced; and multiple hydroxyl radicals are arranged on the main chain of the epoxy resin, and can be crosslinked with amino resin, urea resin and phenolic resin to produce stoving varnish.

Description

technical field [0001] The invention relates to a water-based acrylic modified epoxy phosphate resin and an aqueous dispersion thereof, belonging to the field of water-based coatings. Background technique [0002] Epoxy resin is a kind of resin used in paint making. It has excellent anti-corrosion properties and is widely used in the anti-rust of metal substrates. However, solvent-based epoxy resin paints need to be diluted with a large amount of solvents, resulting in a large amount of VOC emissions, which cannot meet the increasingly stringent environmental protection requirements. In order to solve the above problems, and improve the adhesion of resin substrates, and provide other Anti-rust performance, specially developed the present invention. Contents of the invention [0003] The object of the present invention is to provide a formula of acrylic modified epoxy phosphoric ester and the acrylic modified epoxy phosphoric ester resin and its aqueous dispersion obtained...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F283/10C08G59/14C09D151/08C09D5/08
CPCC08K3/04C08K3/22C08K3/30C08K3/32C08K13/02C08K2003/2241C08K2003/2272C08K2003/3045C08K2003/328C08L2205/03C09D5/08C09D163/10C08L61/20C08L75/04
Inventor 王英秦文
Owner BEIJING JINHWEILI APPLIED CHEM PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com