Novel PVC decorative material

A decorative material and raw material technology, applied in the field of building material preparation, can solve the problems of wear resistance, poor corrosion resistance, poor toughness, low impact resistance, etc., and achieve the goals of not easy to deform and break, high impact resistance, and prolong service life Effect

Inactive Publication Date: 2015-04-29
FOSHAN CITY GAOMING DISTRICT PLASTICS IND ASSOC
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the existing PVC decorative materials have poor wear resistance and corrosion resistance, and low impact resistance and poor toughness.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The new PVC decoration material of the present invention, its raw material and raw material weight percentage content are as follows: described PVC 80%; Plasticizer 4%; Lubricant 6%; Leveling agent 4%; Calcium zinc stabilizer 2.5%; Antioxidant 2%; Calcium powder 1.5%; Also add PVC weight 2% graphene.

Embodiment 2

[0034] The new PVC decorative material of the present invention, its raw material and raw material weight percent are as follows: PVC 78%; Plasticizer 4.5%; Lubricant 5.5%; Leveling agent 4.5%; Barium zinc stabilizer 2.8%; 2.5% of agent; Calcium powder 2.2%; Also add 2.5% graphene of PVC weight.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a novel PVC decorative material prepared from the following raw materials in percentage by weight: 75-85% of PVC, 3-5% of a plasticizer, 5-7% of a lubricating agent, 3-5% of a flatting agent, 2-3% of a calcium-zinc stabilizer, 1-3% of an antioxidant and 1-3% of calcium powder. Graphene accounting for 1-3% of the weight of PVC is also added. Due to the addition of graphene, the PVC decorative material disclosed by the invention has favorable overall performance, and the service life of artificial quartz stone is prolonged.

Description

technical field [0001] The invention belongs to the technical field of building material preparation, and specifically refers to a PVC decorative material. Background technique [0002] Polyvinyl chloride, referred to as PVC (Polyvinyl chloride), is a thermoplastic resin polymerized by vinyl chloride under the action of an initiator. Vinyl chloride homopolymers and vinyl chloride copolymers are collectively referred to as vinyl chloride resins. [0003] Its transparency is better than that of polyethylene and polypropylene, and worse than that of polystyrene. Depending on the amount of additives, it can be divided into soft and hard PVC. Soft products are soft and tough, and feel sticky. Hard products have higher hardness than low-density polyethylene. , and lower than polypropylene, there will be whitening at the inflection. Common products: plates, pipes, soles, toys, doors and windows, wire sheaths, stationery, etc. [0004] However, the existing PVC decorative materia...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K13/02C08K5/098C08K3/04C08K3/08
CPCC08L27/06C08L2201/08
Inventor 贺炳红
Owner FOSHAN CITY GAOMING DISTRICT PLASTICS IND ASSOC