A technology of polyurethane resin and water-based polyurethane, applied in polyurea/polyurethane coatings, anti-corrosion coatings, coatings, etc., can solve problems such as low hardness, acrylic coating adhesion, poor flexibility, and poor fullness, and achieve excellent waterproofing Performance, good anti-corrosion effect, excellent mechanical properties and water resistance

Inactive Publication Date: 2015-04-29
QINGDAO JIASHANG CREATIVE CULTURE
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Waterborne acrylic wood coatings have excellent light resistance, outdoor exposure durability, good acid, alkali and salt corrosion resistance, excellent flexibility and lowest pigment reactivity, and their cost is low, but their paint film is wear-resistant and Defects of poor chemical resistance, low hardness and poor fullness
Most of the coatings in machinery, light industry, chemical industry, metallurgy and other industries use acrylic coatings, but the adhesion and flexibility of acrylic coatings are poor, while the polyurethane coatings in my country are mainly two-component alkyd polyurethane coatings, which have good adhesion and abrasion resistance, but its hardness and high temperature resistance are worse than acrylic coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] The polyurethane resin coating of the present invention comprises the following components: 50 parts of water-based polyurethane emulsion, 15 parts of diisocyanate, 10 parts of polyether polyol, 12 parts of calcium carbonate, 4 parts of dibutyltin dilaurate, 5 parts of triethylamine, kaolin 8 parts, xylene 5 parts, diacetone alcohol 2 parts, aluminum tripolyphosphate 4 parts, polycarbonate diol 5 parts, polyether polyol 2 parts, diisocyanate 2 parts.

Embodiment 2

[0010] The polyurethane resin coating of the present invention comprises the following components: 50 parts of water-based polyurethane emulsion, 15 parts of diisocyanate, 10 parts of polyether polyol, 12 parts of calcium carbonate, 4 parts of dibutyltin dilaurate, 5 parts of triethylamine, kaolin 8 parts, xylene 5 parts, diacetone alcohol 2 parts, aluminum tripolyphosphate 4 parts, polycarbonate diol 5 parts, polyether polyol 2 parts, diisocyanate 2 parts, bentonite 3 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to PU (polyurethane) resin paint which comprises components as follows: 50 parts of a waterborne PU emulsion, 15 parts of diisocyanate, 10 parts of polyether polyol, 12 parts of calcium carbonate, 4 parts of dibutyltin dilaurate, 5 parts of triethylamine, 8 parts of kaolin, 5 parts of xylene, 2 parts of diacetone alcohol, 4 parts of aluminum triphosphate, 5 parts of polycarbonate diol, 2 parts of polyether polyol and 2 parts of diisocyanate. A paint film of the PU resin paint has excellent mechanical performance and water resistance, the paint is free of NCO residues, non-toxic and environment-friendly, construction can be performed on wet foundational planes, and a single-component waterborne polyaniline anticorrosive paint system has the good anticorrosive effect.

Description

technical field [0001] The invention relates to a decorative material, in particular to a polyurethane resin coating. Background technique [0002] Water-based wood coatings mainly include two systems: water-based acrylate and polyurethane. Waterborne acrylic wood coatings have excellent light resistance, outdoor exposure durability, good acid, alkali and salt corrosion resistance, excellent flexibility and lowest pigment reactivity, and their cost is low, but their paint film is wear-resistant and The defects of poor chemical resistance, low hardness and poor fullness. Most of the coatings in machinery, light industry, chemical industry, metallurgy and other industries use acrylic coatings, but the adhesion and flexibility of acrylic coatings are poor, while the polyurethane coatings in my country are mainly two-component alkyd polyurethane coatings, which have good adhesion And wear resistance, but its hardness and high temperature resistance are worse than acrylic co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D175/08C09D7/12C09D5/08
CPCC09D175/04C08L2205/02C09D5/08C09D7/61C09D7/63
Inventor 范开娟李文勇李长敏
Owner QINGDAO JIASHANG CREATIVE CULTURE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products