Microporous acrylic adhesive layer

An acrylic adhesive and microporous technology, applied in adhesives, ester copolymer adhesives, film/sheet adhesives, etc., can solve poor temperature resistance and reliability, product viscosity and performance attenuation, LED Problems such as broken lamp tubes can be solved to achieve the effect of improving reliability, soft light and reducing the chance of breaking

Active Publication Date: 2016-06-15
太仓斯迪克新材料科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The LED light tube is a row of LED light-emitting units installed inside the light-transmitting light tube. The technical problems of the existing technology are as follows: (1) There are problems and deficiencies such as poor light transmittance, large attenuation of transmitted light, and poor uniformity of the fog surface. ; (2) The LED tube may be broken, which poses a safety hazard; (3) The temperature resistance and reliability are poor, if the temperature rises casually, and the temperature difference changes, the viscosity and performance of the product will decay after a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Microporous acrylic adhesive layer
  • Microporous acrylic adhesive layer
  • Microporous acrylic adhesive layer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The diluent of embodiment 1 is toluene; The diluent of embodiment 2 is ethyl acetate; The diluent of embodiment 3 is acetone; The diluent of embodiment 4 is toluene and ethyl acetate according to the mixed diluent of 1:1; The diluent in Example 5 is a 1:1 mixed diluent of toluene and acetone.

[0037] The polyester film layer 5 of embodiment 1 is a PET film layer; the polyester film layer 5 of embodiment 2 is a PA film layer; the polyester film layer 5 of embodiment 3 is a PP film layer; the polyester film layer of embodiment 4 5 is a PBT film layer; the polyester film layer 5PA film layer of embodiment 5.

[0038] Mix the above components according to the conventional process and stir at high speed, use a high-speed coating machine to coat the above-mentioned matte adhesive on the surface of the polyester film, and pass through the oven (temperature: 60°C, 75°C, 85°C, 110°C, 125°C, 135°C, 90°C) to volatilize the solvent, cure and mature before coating.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface roughnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a microporous acrylic adhesive tape. A pressure-sensitive adhesive layer of the microporous acrylic adhesive tape is adhered to the outer surface of an LED light; the surface of the pressure-sensitive adhesive lay which is opposite to a lamp shade is adhered to a polyester film layer, and the surface of the polyester film layer is coated with a foggy surface coating layer. The surface roughness of the fogging surface coating layer is 0.1-0.8 microns; the pressure-sensitive adhesive layer comprises 100 parts of acrylic ester adhesive, 30-50 parts of diluent, 0.5-2 parts of isocyanate cross-linking agent, 0.5-2 parts of epoxy cross-linking agent, 5-20 parts of rosin resin, 2-15 parts of azo compound, N2-15 parts of N-nitroso-compounds, 0.5-2 parts of coupling agent, and 0.3-1.5 parts of acrylic ester polymer. The microporous acrylic adhesive tape overcomes the deflect of viscosity and adhesive force reduction caused by air holes while realizing uniform light and fogging surface, so that the adhesive strength and adhesive force between polyester film layer and the lamp shade are improved, and then the product reliability is improved.

Description

technical field [0001] The invention relates to a microporous acrylic adhesive layer, belonging to the technical field of acrylic adhesive tapes. Background technique [0002] LED can directly convert electricity into light. At the same time, LED has the characteristics of long life, high luminous efficiency, no radiation, impact resistance and low power consumption. In order to meet the requirements of energy saving and environmental protection, and to meet the needs of different users, more and more manufacturers have developed LED lamps to replace fluorescent lamps in traditional technology. [0003] The LED light tube is a row of LED light-emitting units installed inside the light-transmitting light tube. The technical problems of the existing technology are as follows: (1) There are problems and deficiencies such as poor light transmittance, large attenuation of transmitted light, and poor uniformity of the fog surface. ; (2) The LED lamp tube may be broken, which pose...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): F21V3/04C09J7/02C09J133/04F21Y115/10
CPCC09J7/20C09J133/04F21V3/10
Inventor 金闯周满意
Owner 太仓斯迪克新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com