A kind of lead-free environment-friendly high-density bullet and its preparation method

A high-density, environment-friendly technology, applied to ammunition, warheads, offensive equipment, etc., can solve problems such as low strength of projectiles and damaged barrels, and achieve the effects of avoiding direct friction, pollution, and energy consumption

Active Publication Date: 2016-11-30
XIAMEN HONGLU TUNGSTEN MOLYBDENUM IND CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, high-density composite materials prepared solely with tungsten as a filler can obtain higher elastic body density, but lower elastic body strength.
At the same time, due to the high hardness of tungsten, the tungsten particles exposed on the surface of the bullet will directly rub against the rifling of the barrel during the firing process, damaging the barrel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of lead-free environment-friendly high-density bullet and its preparation method
  • A kind of lead-free environment-friendly high-density bullet and its preparation method
  • A kind of lead-free environment-friendly high-density bullet and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] The formulation of the lead-free environment-friendly high-density bullet base material is:

[0042]

[0043] The preparation method of the lead-free environment-friendly high-density bullet comprises the steps of:

[0044] (1) Blending of ingredients: Weigh the quality of various raw materials according to the formula, and mix them evenly in a high-speed mixer to obtain a mixture.

[0045] (2) Extrusion granulation: Put the mixture into a twin-screw extruder, extrude and pelletize at 180°C to obtain injection feed granules.

[0046] (3) Injection molding: The injection feed particles are injected and molded through an injection machine at 200°C to obtain lead-free, environmentally friendly, high-density blanks.

[0047] (4) Preform shaping: Grinding the obtained lead-free environment-friendly high-density preform to remove the injection gate to obtain a preformed preform.

[0048] (5) Copper plating on the spring blank: the surface of the plastic blank is firstly ...

Embodiment 2

[0052] The formulation of the lead-free environment-friendly high-density bullet base material is:

[0053]

[0054]

[0055] The preparation method of the lead-free environment-friendly high-density bullet comprises the steps of:

[0056] (1) Blending of ingredients: Weigh the quality of various raw materials according to the formula, and mix them evenly in a high-speed mixer to obtain a mixture.

[0057] (2) Extrusion granulation: put the mixture into a twin-screw extruder, extrude and pelletize at 260°C to obtain injection feed granules.

[0058] (3) Injection molding: The injection feed particles are injected and molded through an injection machine at 290°C to obtain lead-free, environmentally friendly, high-density blanks.

[0059] (4) Preform shaping: Grinding the obtained lead-free environment-friendly high-density preform to remove the injection gate to obtain a preformed preform.

[0060] (5) Copper plating on the spring blank: the surface of the shaped blank is...

Embodiment 3

[0065] The formulation of the lead-free environment-friendly high-density bullet base material is:

[0066]

[0067] The preparation method of the lead-free environment-friendly high-density bullet comprises the steps of:

[0068] (1) Blending of ingredients: Weigh the quality of various raw materials according to the formula, and mix them evenly in a high-speed mixer to obtain a mixture.

[0069] (2) Extrusion granulation: Put the mixture into a twin-screw extruder, extrude and pelletize at 180°C to obtain injection feed granules.

[0070] (3) Injection molding: The injection feed particles are injected and molded through an injection machine at 200°C to obtain lead-free, environmentally friendly, high-density blanks.

[0071] (4) Preform shaping: Grinding the obtained lead-free environment-friendly high-density preform to remove the injection gate to obtain a preformed preform.

[0072] (5) Copper plating on the spring blank: firstly carry out chemical copper plating on...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a lead-free environment friendly type high density bullet and a preparation method of the environment friendly type high density bullet. The bullet materials comprise, by weight, 100 parts of high-molecular polymers, 500-2000 parts of tungsten powder, 0.05-100 parts of tungsten fiber, 0.05-200 parts of iron powder, 0.5-5 parts of compatilizer, and 0.05-1 part of antioxidants. The preparation method comprises the steps of (1) ingredient mixing, (2) extruding and granulating, (3) injecting and forming, (4) bullet billet sizing, and (5) bullet billet copper plating, and a final product is obtained. The lead-free environment friendly type high density bullet has no lead element, the pollution to environment and the harm to human, animals and plants of traditional bullets with lead are effectively avoided.

Description

technical field [0001] The invention relates to a lead-free environment-friendly high-density bullet and a preparation method thereof, belonging to the field of design and preparation of advanced functional composite material devices. Background technique [0002] Since the birth of the bullet, its shape, structure and ammunition composition have undergone great changes, but lead metal as its core material has never changed, because lead metal has 11.34g / cm 3 The high density and good ductility can effectively improve the accuracy and lethality of shooting. However, lead is biologically toxic, and lead dispersed in the natural environment has serious toxic effects on animal nervous system, hematopoietic system, urinary system, cardiovascular system, reproductive system, and skeletal system. According to the RoHS directive, WEEE directive and REACH regulations, lead is listed as one of the key restricted use and highly concerned hazardous substances. [0003] In the militar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): F42B30/02C22C27/04B22F3/22C23C28/02
Inventor 赵国璋于洋彭福生赖亚洲庄志刚邓华清叶道兴
Owner XIAMEN HONGLU TUNGSTEN MOLYBDENUM IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com