High-temperature wear-resistant coating

A high-temperature wear-resistant and coating technology, which is applied in the field of refractory materials, can solve problems such as shedding, wear-resistant performance, lack of mechanical properties, and easy cracks, and achieve high-temperature resistance, good mechanical properties and impact resistance. Focus on the effect

Inactive Publication Date: 2015-05-13
YIXING GUOQIANG FURNACE IND
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing technology prepares high-temperature wear-resistant coatings, which lack wear resistance and mechanical properties, and are prone to cracks and peeling off in high-temperature environments.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] The high-temperature wear-resistant coating is prepared from the following raw materials: 17 parts by weight of white corundum micropowder with a particle size of 14-20 μm, 6 parts of cement, 10 parts of carbon fluoride, 13 parts of titanium dioxide, and 12 parts of Mohr's salt , 5 parts of barium sulfate, 6 parts of magnesium hexasilicate, 4 parts of aluminum tripolyphosphate, 2.3 parts of sodium persulfate, 1.3 parts of PA-80 cement, 7 parts of alumina, 0.3 parts of silicon micropowder, the mass concentration is 72~80% 4 parts of phosphoric acid.

Embodiment 2

[0013] The high-temperature wear-resistant coating is prepared from the following raw materials: 13 parts by weight of white corundum powder with a particle size of 14-20 μm, 11 parts of cement, 4 parts of carbon fluoride, 8 parts of titanium dioxide, and 9 parts of Mohr's salt , 7 parts of barium sulfate, 3 parts of magnesium hexasilicate, 9 parts of aluminum tripolyphosphate, 3.5 parts of sodium persulfate, 0.7 parts of PA-80 clay, 6 parts of alumina, 0.5 parts of silicon micropowder, the mass concentration is 72~ 3 parts of 80% phosphoric acid.

Embodiment 3

[0015] The high-temperature wear-resistant coating is prepared from the following raw materials: 22 parts by weight of white corundum powder with a particle size of 14-20 μm, 9 parts of cement, 14 parts of carbon fluoride, 10 parts of titanium dioxide, and 14 parts of Mohr's salt , 6 parts of barium sulfate, 9 parts of magnesium hexasilicate, 7 parts of aluminum tripolyphosphate, 4.5 parts of sodium persulfate, 1 part of PA-80 clay, 8 parts of alumina, 1.5 parts of silicon micropowder, the mass concentration is 72~80% 5 parts of phosphoric acid.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a fire-resistant material and particularly relates to a high-temperature wear-resistant coating. The high-temperature wear-resistant coating is prepared from the following raw materials: 13-22 parts of white corundum micro-powder, 6-11 parts of cement, 4-14 parts of carbon fluoride, 8-13 parts of titanium dioxide, 9-14 parts of Mohr's salt, 5-7 parts of barium sulfate, 3-9 parts of magnesium hexasilicate, 4-9 parts of aluminum triphosphate, 2.3-4.5 parts of sodium persulfate, 0.7-1.3 parts of PA-80 cement gum, 6-8 parts of aluminium oxide, 0.3-1.5 parts of silica micro-powder and 3-5 parts of phosphoric acid. The high-temperature wear-resistant coating provided by the invention has the advantages of very good mechanical property and shock resistance, high temperature resistance and excellent adhesive force and can resist wear and hardly fall off when used in a high-temperature furnace.

Description

technical field [0001] The invention relates to a refractory material, in particular to a high-temperature wear-resistant coating. Background technique [0002] High-temperature wear-resistant coatings are mainly used in furnace bodies in the fields of metallurgy, power generation, fluidized beds, building materials, and waste incineration. The high-temperature wear-resistant coating prepared by the existing technology is lacking in wear resistance and mechanical properties, and is prone to cracks and peeling off in high-temperature use environments. Contents of the invention [0003] In view of the above technical problems, the present invention provides a high temperature resistant coating with good wear resistance and mechanical properties. [0004] The specific technical solutions are: [0005] The high-temperature wear-resistant coating is prepared from the following raw materials: 13-22 parts by weight of white corundum powder, 6-11 parts of cement, 4-14 parts of c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D7/12
Inventor 林国强
Owner YIXING GUOQIANG FURNACE IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap