A kind of thermoplastic starch capable of repeated heat processing and preparation method thereof

A thermoplastic starch, repeated thermal processing technology, applied in the field of starch deep processing, can solve the problems of starch no longer having thermoplasticity, poor thermal stability of thermoplastic starch, reduced molecular weight of starch, etc. Effect

Active Publication Date: 2016-08-31
西安康伟岳利软件科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

On the one hand, small molecule plasticizers significantly reduce the hydrogen bond of starch, and the plasticizing effect is excellent; The plasticizer is very easy to precipitate, volatilize, and lose, so the starch no longer has thermoplasticity after repeated thermal processing, which is also the main reason for the poor thermal stability of thermoplastic starch.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of thermoplastic starch capable of repeated heat processing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] (1) 40 parts by weight of tapioca starch, 40 parts by weight of pea starch and 2 parts by weight of hydroxylamine sulfate are refined by a ball mill until the particle size of the powder is ≤ 5 microns to obtain aminated starch;

[0038] (2) The C 18 The dimer acid of hydrogenated fatty acid is added to the high-speed mixer, the temperature of the high-speed mixer is raised to 100°C, the stirring speed is controlled at 200-300rpm, and glacial acetic acid is added while stirring, and the pre-condensation is carried out in the high-speed mixer for 30 minutes. The amount of glacial acetic acid added is controlled 2% of the mass of hydrogenated aliphatic dimer acid;

[0039] (3) Add the precondensed polymer obtained in step (2) into a two-stage twin-screw reaction extruder, set the temperature of the first-stage screw reactor to 80-120°C, and mix through the gap between the screw flight and the barrel to make the amination The crystals of starch relax to form amorphous ge...

Embodiment 2

[0042] (1) Thining 40 parts by weight of sweet potato starch, 45 parts by weight of acorn starch and 3 parts by weight of hexamethylenediamine through a vortex airflow refiner to obtain aminated starch;

[0043] (2) The C 18 The dimer acid of hydrogenated fatty acid is added to the high-speed mixer, the temperature of the high-speed mixer is raised to 100°C, the stirring speed is controlled at 250rpm, and glacial acetic acid is added while stirring, and the pre-condensation is carried out in the high-speed mixer for 45min. 3% of the mass of aliphatic dimer acid;

[0044] (3) Add the precondensed polymer obtained in step (2) into a two-stage twin-screw reaction extruder, set the temperature of the first-stage screw reactor to 80-120°C, and mix through the gap between the screw flight and the barrel to make the amination The crystals of starch relax to form amorphous gel powder, which is polycondensed with hydrogenated aliphatic dimer acid; through the second-stage screw react...

Embodiment 3

[0047] (1) Grinding 80 parts by weight of sago starch and 3 parts by weight of decanediamine through a grinder until the particle size of the powder is ≤5 microns to obtain aminated starch;

[0048] (2) C obtained by derivatizing the aminated starch obtained in step (1) with 10 parts by weight of dimer linolenic acid and dimer oleic acid 18 Add the dimer acid of hydrogenated fatty acid into the high-speed mixer, the temperature of the high-speed mixer is raised to 110°C, the stirring speed is controlled at 300rpm, and glacial acetic acid is added while stirring, and the pre-condensation is carried out in the high-speed mixer for 35min. The amount of glacial acetic acid added is controlled at 2% of hydrogenated aliphatic dimer acid quality;

[0049] (3) Add the precondensed polymer obtained in step (2) into a two-stage twin-screw reaction extruder, set the temperature of the first-stage screw reactor to 80-120°C, and mix through the gap between the screw flight and the barrel ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a thermoplastic starch capable of repeated thermal processing, which comprises the following components in parts by weight: 80-85 parts of starch, 10-15 parts of hydrogenated aliphatic dimer acid, 2-3 parts of aminating agent, thickening agent 0.5-1.5 parts of processing aid; through starch amination, polycondensation with hydrogenated aliphatic dimer acid, overcomes the defects that small molecule plasticizers are easy to separate out and volatilize and lose when directly using small molecule plasticizers to plasticize starch, making Thermoplastic starch has high temperature repeated thermal processing. Further, a preparation method is provided. A double-stage twin-screw reaction extruder is used to make the starch successively amorphized, polycondensed, heat-plasticized, and deeply polycondensed, and finally the starch becomes a kind of starch with high-temperature repeated heat processability. thermoplastic starch.

Description

technical field [0001] The invention relates to the field of deep processing of starch, in particular to thermal plasticization treatment of starch. Thermoplastic starch can be used in biodegradable plastics, environmentally friendly hot melt adhesives and other products. Background technique [0002] Starch is an important renewable and biodegradable natural polymer material, which is widely used in food and textile industries. In order to further expand the use of starch in the industrial field, it is desired to turn starch into a thermoplastic polymer material. However, there are a large number of hydroxyl groups on the starch molecule, and its adjacent molecules form strong crystallization through hydrogen bonds, and a large number of molecular chains gather together to form a tight double helix structure, resulting in a hard outer shell for starch crystalline particles. Due to the hydrogen bond interaction generated by a large number of hydroxyl groups on the surface ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L3/04C08L93/04C08B31/00
CPCC08B31/00C08L3/04C08L93/04
Inventor 陈庆曾军堂
Owner 西安康伟岳利软件科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap