Thermoplastic polyolefin waterproof sheet material and preparation method thereof

A thermoplastic polyolefin and waterproof sheet technology, which is applied in the field of waterproof material preparation, can solve the problems of aging resistance and adhesion that cannot fully meet the performance requirements of waterproof sheets, and achieve excellent waterproof, high tensile strength, and convenient use Effect

Inactive Publication Date: 2015-06-03
天津市耀新科技发展有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Thermoplastic polyolefin waterproof sheets have been used in my country's waterproofing field for more than ten years, but in recent years, due to aging resistance and adhesion, this material cannot fully meet the performance requirements of new road and bridge waterproof sheets.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermoplastic polyolefin waterproof sheet material and preparation method thereof
  • Thermoplastic polyolefin waterproof sheet material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Recipe and preparation method:

[0031] 1. formula:

[0032] Chlorinated polyethylene 40kg

[0033] Thermoplastic Polyolefin 50kg

[0034] Filler 10kg

[0035] Auxiliary 5kg

[0036] 2. Preparation:

[0037] (1) Measure all the raw materials according to the formula ratio and put them into the high-speed mixer for uniform mixing, then put them into the hopper of the twin-screw extruder, and follow the instructions in the accompanying drawings figure 1 The technical process for the preparation of thermoplastic polyolefin waterproof sheet is extrusion granulation.

[0038] (2) Put the produced thermoplastic polyolefin waterproof sheet pellets into the barrel of the extruder calendering unit for extrusion and calendering to make thermoplastic polyolefin waterproof sheet.

[0039] The main properties of the thermoplastic polyolefin waterproof sheet prepared by the present invention:

[0040]

Embodiment 2

[0042] formula:

[0043] Chlorinated polyethylene 40kg

[0044] Thermoplastic polyolefin 60 kg

[0045] Filler 10kg

[0046] Auxiliary 5kg

[0047] The preparation method is the same as in Example 1.

Embodiment 3

[0049] formula:

[0050] Chlorinated polyethylene 25kg

[0051] Thermoplastic polyolefin 60 kg

[0052] Filler 15kg

[0053] Auxiliary 3kg

[0054] The preparation method is the same as in Example 1.

[0055] The performance table is as follows:

[0056] performance Example 1 Example 2 Example 3 Tensile strengthMpa 19.05 21.43 18.6 elongation at break 1020 980 800

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a thermoplastic polyolefin waterproof sheet material and a preparation method thereof. The thermoplastic polyolefin waterproof sheet material comprises thermoplastic polyolefin as a base material, chlorinated polyethylene, a filler and other assistants and is prepared by an extrusion calendering molding method. The thermoplastic polyolefin waterproof sheet material has excellent comprehensive economic and technical indexes such as excellent water resistance, seepage resistance, weatherability, high tensile strength, high elongation percentage, aging resistance, strong deformation adaptability, wide temperature use range, high bonding strength, long service life, construction easiness and low cost. The thermoplastic polyolefin waterproof sheet material is used for waterproof engineering of passenger transport private line bridge floor concrete, subway, road, port terminal and underground large-scale engineering.

Description

[0001] technical field [0002] The invention belongs to the field of waterproof material preparation, and in particular relates to a thermoplastic polyolefin waterproof sheet and a preparation method thereof. Background technique [0003] Thermoplastic polyolefin (POE) is a high-performance polyolefin product that becomes rubber-elastic at room temperature. It has the characteristics of low density, large bending, high impact resistance at low temperature, and easy processing. [0004] Chlorinated polyethylene is a polymer material obtained by chlorination substitution reaction of high-density polyethylene. According to its chlorine content, residual crystallinity and other technical characteristics, it can be divided into resin-type chlorinated polyethylene and rubber-type chlorinated polyethylene. Ethylene (referred to as CM). Since chlorinated polyethylene is a chlorine-containing high polymer, it is soluble in aromatic hydrocarbons and halogenated hydrocarbons, but ins...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L23/28C08K13/02C08K3/26C08K5/12C08K5/134C08K5/09C08K5/098B29C43/24B29B9/06
CPCC08L23/0815B29B9/06C08K2201/014
Inventor 孙燕峰
Owner 天津市耀新科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More