Racoon dog fur semi-worsted blend functional health yarn as well as preparation and application thereof

A semi-worsted, functional technology, used in textiles, papermaking, yarn, etc., can solve the problem of lack of health care functions, achieve long-lasting antibacterial effect, reduce neps and linters, and have good skin-friendly effects.

Inactive Publication Date: 2015-06-03
ZHONGYUAN ENGINEERING COLLEGE
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Cashmere has the characteristics of lightness, warmth, softness and slipperiness. It has slender fibers, good smoothness, soft and warm hand feeling, high bulkiness, elasticity, good warmth retention, delicate and smoo

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0034] Example 1

[0035] In this embodiment, a 34-inch blended yarn is taken as an example, and the weight percentage of the blended raccoon fiber, gray bamboo charcoal fiber, antibacterial deodorant acrylic fiber, wool fiber and cashmere fiber is 20:16:20:24:20. The preparation method thereof Including raw material and wool refueling, sliver making, drawing, roving and spinning processes in sequence:

[0036] (1) Raw material and wool oiling process: add 1.5% of the total weight of the raw material antistatic agent, the addition amount of water and crude oil are respectively 5.0% and 0.5% of the total weight of the raw material, and the raw material and wool are mixed and opened twice Or three times, fully mix the raw materials evenly, and store the mixed raw materials in the wool warehouse between the wool and wool for 30 hours;

[0037] (2) Carding and sliver making process: The relative speed of the combing and sliver making workshop should be controlled at 60%, the delive...

Example Embodiment

[0045] Example 2

[0046] In this embodiment, a 34-inch blended yarn is taken as an example, and the weight percentage of the blended raccoon fiber, gray bamboo charcoal fiber, antibacterial deodorant acrylic fiber, wool fiber and cashmere fiber is 20:20:23:20:17, and the preparation method thereof Including raw material and wool refueling, sliver making, drawing, roving and spinning processes in sequence:

[0047] (1) Raw material and wool oiling process: add 1.6% of the total weight of the raw material antistatic agent, the addition amount of water and crude oil are respectively 5.0% and 0.5% of the total weight of the raw material, and the raw material and wool are mixed and opened twice Or three times, fully mix the raw materials evenly, and store the mixed raw materials in the wool warehouse between the wool and wool for 32 hours;

[0048] (2) Carding and sliver making process: the relative speed of the combing and sliver making workshop should be controlled at 66%, the d...

Example Embodiment

[0056] Example 3

[0057] In this embodiment, a 34-inch blended yarn is taken as an example, and the weight percentage of the blended raccoon fiber, gray bamboo charcoal fiber, antibacterial deodorant acrylic fiber, wool fiber and cashmere fiber is 20:25:25:15:15. The preparation method thereof Including raw material and wool refueling, sliver making, drawing, roving and spinning processes in sequence:

[0058] (1) Raw material and wool oiling process: add 1.5% of the total weight of the raw material antistatic agent, the addition amount of water and crude oil are respectively 5.0% and 0.5% of the total weight of the raw material, and the raw material and wool are mixed and opened twice Or three times, fully mix the raw materials evenly, and store the mixed raw materials in the wool warehouse between the wool and wool for 24 hours;

[0059] (2) Carding and sliver making process: The relative speed of the combing and sliver making workshop should be controlled at 60%, the deliv...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Single yarn breaking strengthaaaaaaaaaa
Breaking strengthaaaaaaaaaa
Breaking strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a raccoon dog fur semi-worsted blend functional health yarn. The raccoon dog fur semi-worsted blend functional health yarn consists of the following components in percentage by weight: 10-30% of raccoon dog fur fibers, 10-30% of grey bamboo carbon fibers, 10-30% of antibacterial deodorant acrylic fibers, 10-35% of wool fibers, and 10-35% of cashmere fibers, wherein the performance indexes of the blended yarn are as follows: single yarn breaking strength of 11.0-18.5 cN/tex, a single yarn breaking strength variable coefficient Cv value of 7.3-15.2%, and a yarn evenness variable coefficient Cv value of 14.9-21.2%. The raccoon dog fur semi-worsted blend functional health yarn disclosed by the invention is lasting in antibacterial effect and has health care functions of being antibacterial, bacteriostatic, deodorant, skincare and body-building, skin-moistening, good in nature to skin, deodorized, good in comfort and the like.

Description

technical field [0001] The invention relates to the technical field of blended yarns, in particular to a preparation method and application of functional health-care yarns blended with raccoon velvet fibers, gray bamboo charcoal fibers, antibacterial and deodorant acrylic fibers, wool fibers and cashmere fibers. Background technique [0002] Raccoon velvet fiber has similar characteristics to cashmere. Raccoon raccoon velvet contains a medullary layer, and the scales grow in one direction, with a larger inclination angle to the fiber diameter direction and a higher density. Due to the discontinuous medullary cavity It has a large proportion, is lustrous, has good warmth retention property, and has low fiber density. Its length, fineness, curl and warmth retention property are similar to cashmere, but raccoon raccoon cashmere fiber contains medulla layer, and its breaking strength is smaller than that of cashmere. , The coefficient of dispersion of fineness and the coefficien...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D02G3/04
Inventor 赵博
Owner ZHONGYUAN ENGINEERING COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap