Plate surface pattern manufacturing technology and manufactured plate and furniture

A technology of surface pattern and production process, which is applied in the process of producing decorative surface effects, decorative art, coating, etc., can solve the problems affecting product quality, poor pattern adhesion, product color difference, etc., and improve the transfer effect , The pattern is firmly attached, and the effect of firm adhesion

Inactive Publication Date: 2015-06-10
SUZHOU METAL PROD
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the field of home decoration, it is often necessary to transfer patterns on the surface of the board to achieve a certain visual effect. However, the existing transfer printing process has insufficient temperature control technology based on the influence of the thickness and size of the board, the indoor and outdoor ambient temperature of the production area, etc., which may easily cause the product to appear. Chromatic aberration, poor pattern adhesion, easy to change color, affect product quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A board surface pattern manufacturing process for making board products with patterns on the surface, comprising the following steps:

[0027] (1) For the steel plate as a plate blank, the surface is deslagged and polished smoothly.

[0028] (2) High-temperature electrostatic spraying on the polished and smooth surface of the board is suitable for the powder material of the wood grain pattern printing material, thereby forming a paint layer on the surface of the board to obtain a semi-finished product.

[0029] The powder material is composed of the following components by weight: 28 parts of polyester resin, 28 parts of epoxy resin, 38 parts of filler, 2.8 parts of auxiliary agent, 2.5 parts of titanium dioxide, and 0.7 part of pigment.

[0030] (3) Slightly polish the surface of the semi-finished paint layer with fine sand, and then wipe it clean with a clean rag.

[0031] (4) Paste the transfer paper on the surface of the polished paint layer of the board, and bake ...

Embodiment 2

[0037] A board surface pattern manufacturing process, the finished board of Example 2 is obtained, and the difference from Example 1 is:

[0038] In the transfer paper, the transfer glue is composed of the following components by weight: 42 parts of vinyl acetate, 4 parts of polyvinyl alcohol, 3 parts of dibutyl phthalate, 0.9 parts of octanol, ammonium persulfate 0.08 parts, and 44.8 parts of water. The printing layer is composed of the following components in proportion by weight: 48 parts of isobutanol, 19 parts of methanol, 19 parts of disperse dye, and 9 parts of polyvinyl butyral.

[0039] The powder material is composed of the following components by weight: 27 parts of polyester resin, 27 parts of epoxy resin, 37 parts of filler, 2.7 parts of auxiliary agent, 2.4 parts of titanium dioxide, and 0.65 parts of pigment.

Embodiment 3

[0041] A board surface pattern manufacturing process, the finished board of Example 3 is obtained, and the difference from Example 1 is:

[0042] In the transfer paper, the transfer glue is composed of the following components in parts by weight: 47 parts of vinyl acetate, 7 parts of polyvinyl alcohol, dibutyl phthalate 5 parts of ester, 1.1 parts of octanol, 0.12 parts of ammonium persulfate, and 45.0 parts of water. The printing layer is composed of the following components in proportion by weight: 52 parts of isobutanol, 21 parts of methanol, 21 parts of disperse dye, and 11 parts of polyvinyl butyral.

[0043] The powder material is composed of the following components by weight: 29 parts of polyester resin, 29 parts of epoxy resin, 39 parts of filler, 2.9 parts of auxiliary agent, 2.6 parts of titanium dioxide, and 0.75 parts of pigment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a plate surface pattern manufacturing technology. The plate surface pattern manufacturing technology comprises the following steps: (1) carrying out primary treatment on the surface of a plate blank; (2) charging powder on the surface of the plate so as to form a paint layer; (3) carrying out surface treatment on the paint layer; (4) pasting transfer paper on the surface of the paint layer of the plate, baking at 160-180 DEG C for 40-50 minutes, then stripping the transfer paper so as to obtain the plate. By adopting the technology, the high-quality plate product is obtained by the working procedures of primary treatment of the blank surface, oil charge on the blank surface, paint surface treatment and transfer, especially the working procedure of controlling the baking temperature and time in transfer, so that the surface pattern of the plate is firm in attachment, has no color difference, and is difficult to discolor; patterns of the surfaces of plates of various furniture can be manufactured by the technology; especially the surface transfer wood grain patterns of steel plates have high-quality and emulational wood effect, the steel plates are relatively environmentally friendly and durable compared with the traditional wood plate, and the manufactured furniture also inherits the corresponding effect.

Description

technical field [0001] The invention relates to a surface treatment process of a home decoration board and related finished boards and furniture. Background technique [0002] In the field of home decoration, it is often necessary to transfer patterns on the surface of the board to achieve a certain visual effect. However, the existing transfer printing process has insufficient temperature control technology based on the influence of the thickness and size of the board, the indoor and outdoor ambient temperature of the production area, etc., which may easily cause the product to appear. Chromatic aberration, poor pattern adhesion, and easy discoloration will affect product quality. Contents of the invention [0003] A kind of sheet material surface pattern making process is characterized in that, comprises the following steps: [0004] (1) Preliminary treatment of the surface of the plate blank; [0005] (2) Powder material on the surface of the board to form a paint lay...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B44C1/17C09J4/00C09J4/06C09J11/06C09D167/00C09D163/00C09D7/12
CPCB44C1/17
Inventor 马留生
Owner SUZHOU METAL PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap