Plant fiber-reinforced polypropylene composite material and preparation method thereof, and application of plant fiber-reinforced polypropylene composite material in preparation of automobile components

A plant fiber and composite material technology, applied in the field of polypropylene composite materials, can solve the problems of unfavorable low carbon, green environmental protection and sustainable development, low carbon, green environmental protection and insufficient price, poor dimensional stability of polypropylene, etc., and achieve excellent The effect of mechanical properties, light weight and excellent molding performance

Active Publication Date: 2015-06-10
NINGBO HOMELINK ECO ITECH CO LTD
View PDF11 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Chinese patents CN102516665A, CN101781424A and CN102417660A respectively disclose a PP automobile bumper material, but its components are completely derived from petroleum-based materials, and there are deficiencies in low carbon, green environmental protection and price
Chinese patents CN101747560B and CN102827425A respectively report a modified polypropylene for automobiles filled with talcum powder. Although the impact resistance of polypropylene is improved and its cost is reduced, the advantage of low density of polypropylene is weakened.
Although plant fibers are used in this technical solution, the compatibility between the components is poor, and its mechanical properties are not good
[0006] The existing polymer materials for automobiles have the following disadvantages: 1. The components of polymer materials for automobiles are almost all derived from petrochemical resources, which is not conducive to low-carbon, green and sustainable development
3. As a typical non-polar crystalline polymer material, polypropylene has the problems of poor dimensional stability, poor colorability, difficulty in painting and poor color stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Plant fiber-reinforced polypropylene composite material and preparation method thereof, and application of plant fiber-reinforced polypropylene composite material in preparation of automobile components
  • Plant fiber-reinforced polypropylene composite material and preparation method thereof, and application of plant fiber-reinforced polypropylene composite material in preparation of automobile components
  • Plant fiber-reinforced polypropylene composite material and preparation method thereof, and application of plant fiber-reinforced polypropylene composite material in preparation of automobile components

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The formula is as follows:

[0037]

[0038] Weigh the following ingredients by weight:

[0039] Copolymerized polypropylene (Dongguan Xuanhao Plastic Co., Ltd.) 72Kg, kenaf fiber (5mm-10mm in diameter, Gaobeidian Liangjiaying Shengli Hemp Rope Processing Factory) 20Kg, castor oil (Nanjing Qianyue Chemical Co., Ltd.) 3Kg, EVA (VA content is 19%, Kunshan Great Wall Plastic Co., Ltd.) 5Kg, antioxidant 1010 (Shanghai Jinghong Industrial Co., Ltd.) 0.1Kg, antioxidant 168 (Shanghai Jinghong Industrial Co., Ltd.) 0.3Kg.

[0040] The preparation process is as follows:

[0041] First, at an ambient temperature of 25°C, use a high-speed mixer to mix the above-mentioned weighed raw materials uniformly to obtain a uniformly mixed material; then, add the mixed material to a twin-screw extruder for melt blending (mixed The materials are sequentially passed through the melting and blending intervals with temperatures of 170°C, 172°C, 172°C, 175°C, 180°C, 180°C, 175°C, and 175°C)...

Embodiment 2

[0043] The formula is as follows:

[0044]

[0045] Weigh the following ingredients by weight:

[0046] Copolymerized polypropylene (Dongguan Xuanhao Plastic Co., Ltd.) 67Kg, kenaf fiber (5mm-10mm in diameter, Gaobeidian City Liangjiaying Shengli Hemp Rope Processing Factory) 25Kg, castor oil (Nanjing Qianyue Chemical Co., Ltd.) 3Kg, EVA (VA content is 19%, Kunshan Great Wall Plastic Co., Ltd.) 5Kg, antioxidant 1010 (Shanghai Jinghong Industrial Co., Ltd.) 0.1Kg, antioxidant 168 (Shanghai Jinghong Industrial Co., Ltd.) 0.3Kg.

[0047] The preparation process is as described in Example 1.

Embodiment 3

[0049] The formula is as follows:

[0050]

[0051] Weigh the following ingredients by weight:

[0052] Copolymerized polypropylene (Dongguan Xuanhao Plastic Co., Ltd.) 60Kg, kenaf fiber (5mm-10mm in diameter, Gaobeidian City Liangjiaying Shengli Hemp Rope Processing Factory) 30Kg, castor oil (Nanjing Qianyue Chemical Co., Ltd.) 5Kg, EVA (VA content is 19%, Kunshan Great Wall Plastic Co., Ltd.) 5Kg, antioxidant 1010 (Shanghai Jinghong Industrial Co., Ltd.) 0.1Kg, antioxidant 168 (Shanghai Jinghong Industrial Co., Ltd.) 0.3Kg.

[0053] The preparation process is as described in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flexural modulusaaaaaaaaaa
impact strengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a plant fiber-reinforced polypropylene composite material and a preparation method thereof, and an application of the plant fiber-reinforced polypropylene composite material in preparation of automobile components. The composite material is prepared from the following raw materials in percentage by weight: 40%-77% of polypropylene, 20%-40% of a plant fiber, 1%-10% of vegetable oil, 1%-10% of a flexibilizer and 0.1%-5% of an assistant, wherein the plant fibers and the vegetable oil are from renewable biomass, and conform to the requirements of low-carbon, environment-friendly and sustained economic development. In addition, a low-density biomass material is capable of further promoting light weight of automobiles, and is of great significance in energy conservation and emission reduction. The plant fiber-reinforced polypropylene composite material for automobiles can be prepared by extrusion once, so that the method is simple, easy to operate and suitable for industrialized production.

Description

Technical field [0001] The invention relates to the field of polypropylene composite materials, and in particular to a plant fiber reinforced polypropylene composite material, its preparation method and its application in the preparation of automobile parts. Background technique [0002] In order to solve the challenges that "energy shortage" and "environmental pollution" bring to the global economy and people's living environment, and to promote the advancement of automobile products, protect the environment, and promote energy conservation and sustainable development, automobile energy conservation and emission reduction are increasingly popular among people. focus on. In recent years, the development of new material modification technology has promoted the miniaturization and lightweight of automobiles, becoming another important new way to promote automobile energy conservation and emission reduction. Developed countries in the automobile industry have regarded the amou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/14C08L97/02C08L91/00C08L23/16C08L23/08B29B9/06B29C47/92B29C48/92
CPCC08L23/14C08L2205/035C08L2205/08C08L97/02C08L91/00C08L23/0853C08K5/1345C08K5/526
Inventor 陈虎啸汤兆宾王熊李鹏
Owner NINGBO HOMELINK ECO ITECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com