Modified UV paint and preparation method thereof

A paint and modification technology, applied in the direction of coating, etc., can solve the problems of oil accumulation on the edge of the protective film, increase product cost, obvious step feeling, etc., achieve excellent decoration and performance protection, increase flexibility, and the effect of simple method

Inactive Publication Date: 2015-07-01
BYD PRECISION MFG
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, in the above-mentioned several processing methods, there are several problems as follows: the method of using a jig to protect the non-decorative surface may easily cause the boundary between the decorative surface and the non-decorative surface to be unclear, such as sawtooth, multi-spray, steps and other poor appearance, Seriously affect the appearance of integrated seamless technology
The method of protecting the non-decorative surface with a protective film is not suitable for the structure where the non-decorative surface is a curved surface. If the non-decorative surface is a flat surface, when the protective film is used to protect it, because the protective film has a certain thickness, spraying During the process, oil will accumulate on the edge of the protective film, resulting in a problem of obvious step feeling, which will affect the feel of the integrated seamless injection molding product
However, when the non-decorative surface is treated with low surface energy so that the paint cannot be wetted on the surface, the cost of the product will be greatly increased due to the relatively expensive price of low surface energy treatment.
[0005] Due to the existence of the above problems, the plastic surface treatment in the integrated seamless appearance of glass and plastic, metal and plastic has not been effectively solved.
And if a kind of method can be provided to improve the brittleness of UV paint, and make UV paint have no adhesion to glass or metal surface while not reducing UV paint to plastic surface adhesion, that can effectively solve the problem of glass and plastic, metal Plastic surface treatment problems in seamless appearance products integrated with plastic

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The modified UV paint described in this example consists of the following components: 20 g of polyurethane acrylate (trade name: CN9001NS), 10 g of thermoplastic polyurethane resin (trade name: TPU5778), 5 g of isobornyl acrylate (trade name: EM70), 1,6-hexanediol diacrylate (trade name is SR238) 5g, butyl acetate 50g, polysiloxane-polyether copolymer (trade name is Glide 440) 5g, 1-hydroxy-cyclohexyl-phenyl Methanone (trade name is 184) 5g.

Embodiment 2

[0028] The modified UV paint described in this embodiment consists of the following components: polyester acrylate (trade name is CN750) 30g, thermoplastic polyurethane resin (trade name is TPU 5715) 5g, 2(2-ethoxyethoxy ) ethyl acrylate (trade name is SR256) 2g, propoxylated neopentyl glycol diacrylate (trade name is EM2251) 3g, n-butanol 20g, butyl acetate 30g, polysiloxane-polyether copolymer ( The product name is Glide 440) 5 g, 2-hydroxy-2-methyl-1-phenyl-1-propanone (the product name is UV1173) 5 g.

Embodiment 3

[0030]The modified UV paint described in this embodiment consists of the following components: 40g of epoxy acrylate (trade name is CNUVE151NS), 20g of thermoplastic polyurethane resin (trade name is TPU5715), tripropylene glycol diacrylate (trade name is SR306NS) 0.5g, 1,6-hexanediol diacrylate (SR238) 0.5g, xylene 35g, fluorine-containing leveling agent (BYK 340) 3.5g, 2,4,6 (three Toluyl)diphenylphosphine oxide (trade name TPO) 0.5g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a modified UV paint and a preparation method thereof, and belongs to the field of coating. The modified UV paint comprises the following components in percentage by weight: 20-40% of an oligomer, 5-30% of thermoplastic polyurethane resin, 1-10% of a diluent monomer, 30-50% of a diluent, 0.1-5% of an additive and 0.5-5% of a light initiator. The invention further discloses a preparation method of UV paint and an application of the coating. The coating has good performance, is subjected to spray coating on the surface of an integral seamless product of metal and plastic or glass and plastic, is stripped off by an adhesive tape to achieve excellent decoration and performance protection of paint on the plastic position, is not left on glass or plastic and has a clear boundary with the metal and the plastic or with the glass and the plastic without generating a hand feeling.

Description

technical field [0001] The invention relates to a modified UV paint and a preparation method thereof, belonging to the field of paint. Background technique [0002] In the prior art, the integrated seamless appearance product of glass and plastic, metal and plastic has become a bright spot in the electronics industry and other industries, and is more and more widely used. However, in the integrated seamless appearance products of glass and plastic, or metal and plastic, since the surface of the plastic part does not have a dense and smooth appearance like glass or metal, it is often necessary to separately decorate the surface of the plastic deal with. In the prior art, the plastic surface is generally decorated by spraying UV paint. However, during the spraying process of UV paint, it is very easy to be sprayed on the glass or metal surface that does not need to be decorated at the seamless connection with the plastic, and because the UV paint is brittle, and some UV pain...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/02C09D4/06C09D7/12
Inventor 崔静娜韦思伟
Owner BYD PRECISION MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products